Two-component structural silicone sealant for building

A two-component, sealant technology, applied in adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of not being able to bear large loads for a long time, short service life, etc., to achieve extended service life, Excellent anti-attenuation, excellent anti-aging and excellent effect

Inactive Publication Date: 2010-10-20
ZHENGZHOU ZHONGYUAN SILANDE HIGH TECH CO LTD
View PDF4 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is that it cannot bear a large load for a long time and has a short service life. It provides a silicone structural sealant for construction that has a long service life and can meet the structural assembly requirements of specific curtain walls.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Two-component structural silicone sealant for building
  • Two-component structural silicone sealant for building

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A two-component silicone structural sealant for construction, its components are as follows:

[0031] A component

[0032] 10000cp hydroxyl terminated polydimethylsiloxane 60kg

[0033] 200000cp hydroxyl terminated polydimethylsiloxane 60kg

[0034] 100cp alkyl-terminated polydimethylsiloxane 40kg

[0035] 2000cp alkyl-terminated polydimethylsiloxane 40kg

[0036] Active Calcium Carbonate 100kg

[0037] B component

[0038] Methyltrimethoxysilane 5kg

[0039] Bis(3-triethoxysilylpropyl)amine 3kg

[0040] Dibutyldioctin 0.05kg

[0041] Tris(1,2,2,6,6-pentamethylpiperidinyl) phosphite 0.01kg

Embodiment 2

[0043] A two-component silicone structural sealant for construction, its components are as follows:

[0044] A component

[0045] 500000cp hydroxyl terminated polydimethylsiloxane 110kg

[0046] 5000cp alkyl-terminated polydimethylsiloxane 50kg

[0047] Calcium carbonate treated with silane coupling agent 150kg

[0048] Inactive calcium carbonate 50kg

[0049] B component

[0050] Methyltrimethoxysilane 15kg

[0051] γ-(2.3 Glycidoxy)propyltrimethoxysilane 0.3kg

[0052] Dibutyltin diacetate 0.2kg

[0053] 4-Benzoyloxy-2,2,6,6-tetramethylpiperidine 0.1kg

Embodiment 3

[0055] A two-component silicone structural sealant for construction, its components are as follows:

[0056] A component

[0057] 200000cp hydroxyl terminated polydimethylsiloxane 80kg

[0058] 3000cp alkyl-terminated polydimethylsiloxane 10kg

[0059] Fumed silica 100kg

[0060] Precipitated silica 100kg

[0061] B component

[0062] Polymethyltriethoxysilane 3kg

[0063] Methyltrimethoxysilane 2kg

[0064] Bis(3-triethoxysilylpropyl)amine 0.3kg

[0065] Dibutyltin diacetate 0.01kg

[0066] Hexamethylphosphoric triamide 0.01kg

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a two-component structural silicone sealant for building, which comprises the following components by weight part: a component A: 80 to 120 parts of hydroxy-terminated polydimethylsiloxane, 10 to 80 parts of alkyl-terminated poly dimethylsiloxane, 100-300 parts of active filler; and a component B: 5 to 15 parts of alkoxy silane, 0.3-5 parts of coupling agent, 0.01-0.2 part of catalyst, and 0.01-5 parts of light stabilizer. The invention takes hydroxyl-terminated poly dimethyl siloxane as a base adhesive, and adjusts the ratio of ingredients by adding the crosslinking agent alkoxy silane and the coupling agent to obtain the structural silicone sealant with excellent anti-aging and anti-decay performances, and the ratio of the tensile bond strength of water-ultraviolet 1008h and the like and the standard-condition tensile bond strength is equal to or greater than 0.75; the standard-condition tensile bond strength reaches 0.8-3.0MPa, and the elongation rate exceeds 100%; and the service life is prolonged to 25 years, and the requirements of the structural assembly of specific curtain walls can be met.

Description

technical field [0001] The invention relates to a silicone structural sealant, in particular to a two-component silicone structural sealant for construction. Background technique [0002] As my country's building curtain walls are built higher and higher, the structure is more and more complex, the load they bear is also increasing, and the forms are more diverse, so the requirements for structural sealants are also getting higher and higher. Because the silicone structural sealant is bonded to the building reinforcement, it can not only make the components reach or exceed the original design level, improve the strength, stability and integrity, but also prolong the service life, safe and reliable, and the construction is simple and time-saving, without damage The original structure, after strengthening, has a beautiful appearance, is leak-proof and anti-corrosion, so it has attracted attention from all sides. In 1997, the country formulated the standard GB 16776 "Silicon S...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/06C08L83/04C08K13/06C08K3/26C08K3/36C08K5/5419C08K5/5415C09J183/06C09J11/06C09K3/10
Inventor 张德恒张燕红杨晓菲张燕青姚英艳张燕玲王晓红杨潇珂安静冯培杨玉宁高新典
Owner ZHENGZHOU ZHONGYUAN SILANDE HIGH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com