Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Integral fuel gas buring catalyst and process for preparing the same

A gas combustion and catalyst technology, which is used in catalyst activation/preparation, chemical instruments and methods, physical/chemical process catalysts, etc. It can solve the problems of inability to process burners of gas appliances, inability to achieve effective heat flow, and high catalyst costs. , to achieve the effect of low pressure drop, good low temperature performance and anti-aging performance, high activity

Inactive Publication Date: 2004-06-16
SICHUAN TIANJIAN CATALYTIC COMBUSTION
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to CH 4 The volume concentration is low, and the range of effective heat flow cannot be reached, and the cost of the catalyst is high due to the noble metal component
The catalysts disclosed in the above two Chinese patent applications are all granular catalysts, and obviously cannot be directly used to process burners of gas appliances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The matrix uses a pore density of 46 pores / cm 2 The monolithic cordierite honeycomb ceramics, the composite catalytic functional components and coating additives in the catalyst coating account for 70% and 30% of the weight of the entire catalyst coating respectively. The composite catalytic functional component includes three catalytic functional components; the first catalytic functional component accounts for 30% of the weight of the entire catalyst functional component, and its carrier is γ-Al 2 o 3 , the active component is ferric oxide, and the auxiliary agent is lanthanum oxide, which respectively account for 85%, 10% and 5% of the weight of the catalytic functional component, and the precursors are all nitrates; the second catalytic functional component Accounting for 30% of the weight of the entire catalytic functional component, the carrier is θ-Al 2 o 3 , the active component is manganese oxide, and the auxiliary agent is zirconia, which account for 90%, 7...

Embodiment 2

[0045] The matrix uses a pore density of 31 pores / cm 2 The monolithic metal honeycomb body, the composite catalytic functional component and the coating aid group in the catalyst coating accounted for 78% and 22% of the weight of the entire catalyst coating, in which the composite catalytic functional component included four different catalytic functions Components: The first catalytic functional component accounts for 20% of the weight of the entire catalytic functional component, and the carrier is γ-Al 2 o 3 , the active component is manganese oxide, and the auxiliary agent is zirconia, which account for 90%, 8.0% and 2.0% of the catalytic functional components respectively, and the precursors are all nitrates; the second catalytic functional component accounts for the entire catalytic functional component Component 20%, carrier is CeO 2 -ZrO 2 (where CeO 2 30%, ZrO 2 accounted for 70%), the active component is iron oxide, and the auxiliary agent is cerium oxide, which...

Embodiment 3

[0048] The matrix uses a pore density of 54 pores / cm 2 The ceramic honeycomb body, the composite catalytic functional components and coating additives in the catalytic coating accounted for 83% and 17% of the weight of the entire catalytic coating, and the composite catalytic functional components included five different catalytic functional components: A catalytic functional component accounts for 22% of the entire catalytic component, and the carrier is γ-Al 2 o 3 , the active component is Fe 2 o 3 , the auxiliary agent is lanthanum oxide, accounting for 80%, 14% and 6.0% of the catalytic functional components respectively, and the precursors are all nitrates; the second catalytic functional component accounts for 18% of the entire catalytic functional component, and the carrier for CeO 2 -ZrO 2 (where CeO 2 30%, ZrO 2 accounted for 70%), the active component is cobalt oxide, and the auxiliary agent is strontium oxide, accounting for 73%, 20% and 7.0% of the catalytic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an integral style gas, combustion catalyst and method for the making same, wherein the base material of the catalyst is integral ceramic honeycomb body or metallic honeycomb body, the catalyst coating layer coated on the base material surface comprises catalytic functional components and coating layer aiding agents, the catalytic functional components are classified into compound catalytic functional components having at least three different catalytic functions, each of which is prepared through corresponding predecessor physical process. The catalyst by the invention has high activity, high stability, high heat efficiency and low contaminant discharge.

Description

1. Technical field [0001] The invention relates to an integral catalyst capable of improving the combustion efficiency of combustible gases such as natural gas, liquefied petroleum gas and coal gas, and reducing pollutant emissions and a preparation method thereof. 2. Background technology [0002] So far, most of the energy used by humans still comes from the spontaneous combustion of combustible substances, which is also called flame combustion. In flame combustion, due to the initiation of free radicals in the gas phase, the products in the excited state of the electron are generated, and energy is released in the form of visible light during the transition back to the ground state. This part of energy cannot be used and lost. At the same time, due to the initiation of free radicals in the gas phase, the N in the air 2 Will participate in the reaction to generate NO x , In addition, there are HC and CO produced by incomplete combustion. Therefore, flame combustion has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/32B01J23/74B01J23/76B01J37/025
Inventor 陈耀强龚茂初郑林周世蓉李云胡安明
Owner SICHUAN TIANJIAN CATALYTIC COMBUSTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com