Aqueous binding agent and preparation method thereof

A technology of water-based adhesives and water-retaining agents, which is applied in the direction of adhesive types, ester copolymer adhesives, hydrocarbon copolymer adhesives, etc., can solve the problems of poor washing resistance and environmental protection, and achieve good Effects of elasticity and hand feeling, good hand feel and elasticity, and good printing adaptability

Active Publication Date: 2010-11-10
浙江德尚化工科技有限公司
View PDF10 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] The above-mentioned adhesives contain more plasticizers and solvents, which are not environmentally friendly and have poor washing resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] a. Preparation of emulsion

[0045] 4.63 parts of octylphenol polyoxyethylene ether (OP-10), 1.67 parts of sodium lauryl sulfate, and 0.6 parts of sodium bicarbonate were dissolved in 70 parts of deionized water, then added to the reaction kettle, and the temperature was raised to about 70°C; Take 1.3 parts of methyl methacrylate, 2.14 parts of styrene, 50.9 parts of butyl acrylate, 29.08 parts of isooctyl acrylate, 2.45 parts of butyl methacrylate, 1.8 parts of acrylonitrile, 0.8 parts of acrylic acid and 1.44 parts of methacrylic acid into a mixed monomer; add 1 / 3 part of the mixed monomer into the reactor, and pre-emulsify at 85°C for 30 minutes; then add 0.45 parts of the initiator ammonium persulfate (APS) to 50 parts of deionized water to make a solution and gradually add it dropwise To the reaction kettle, add the remaining monomer dropwise at the same time, and the dropwise addition is completed in about 3 hours. Control the mixed monomer before the initiator s...

Embodiment 2

[0052] a. Preparation of emulsion

[0053] 5.28 parts of sulfonated castor oil, 1.84 parts of sodium lauryl sulfate, and 0.66 parts of sodium bicarbonate were dissolved in 70 parts of deionized water, then added to the reaction kettle, and the temperature was raised to about 70°C; 6.12 parts of methyl methacrylate were weighed ester, 62.78 parts of butyl acrylate, 11.58 parts of styrene, 7.35 parts of butyl methacrylate, 0.88 parts of acrylic acid, 1.58 parts of methacrylic acid, and 8.7 parts of isooctyl acrylate to make mixed monomers; Add the monomer into the reaction kettle, and pre-emulsify at 85°C for 30 minutes; then add 0.5 parts of initiator APS to 50 parts of deionized water to make a solution, and gradually add it dropwise to the reaction kettle, while adding the remaining monomer dropwise, and the addition is completed in about 3 hours , control the mixed monomer before the initiator solution is added dropwise; after the dropwise addition is completed, it can be m...

Embodiment 3

[0060] a. Preparation of emulsion

[0061] 4.63 parts of OP-10, 1.5 parts of sodium dodecylbenzenesulfonate and 0.6 parts of sodium bicarbonate were dissolved in 70 parts of deionized water, then added to the reaction kettle, and the temperature was raised to about 70°C; weighed 3.52 parts of methacrylic acid Methyl ester, 61.24 parts of butyl acrylate, 6.59 parts of styrene, 4.23 parts of butyl methacrylate, 0.8 parts of acrylic acid, 1.44 parts of methacrylic acid, 12.18 parts of isooctyl acrylate to make mixed monomers; mix 1 / 3 parts Add the monomer into the reactor and pre-emulsify at 85°C for 30 minutes; then add 0.45 parts of the initiator APS to 50 parts of deionized water to make a solution and gradually add it to the reactor, while adding the remaining monomer dropwise for about 3 hours Complete, control the mixed monomer before the initiator solution to drop; after the drop is completed, after 1 hour of heat preservation, the ready-to-use emulsion can be made;

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an aqueous binding agent which has washing resistance and is used for electrochemical aluminium hot stamping, and a preparation method thereof, belonging to a binding agent composition. The aqueous binding agent comprises 40-80 parts by weight of acrylic resin emulsion (with the solid content of 40-55%), 20-40 parts by weight of acrylic resin powder and 5-20 parts by weight of ethylene-vinyl acetate copolymer (EVA) emulsion (with the solid content of 40-60%). The binding agent does not contain organic volatile component, is harmless for the human body, is an environment-friendly electrochemical aluminium hot stamping binding agent, and is especially suitable for fabric which is needed to be printed and frequently washed.

Description

technical field [0001] The invention relates to a binder composition and a preparation method thereof, in particular to a washable water-based binder for anodized aluminum hot stamping and a preparation method thereof. Background technique [0002] Anodized aluminum hot stamping refers to the use of a certain pressure and temperature, using the template installed on the hot stamping machine, so that the printed matter and the hot stamping foil are pressed together in a short time, and the metal foil is transferred to the substrate according to the image and text of the hot stamping template. The craft of the print surface. The main material required for hot stamping is anodized aluminum foil, which has a metallic luster and is used for inscription patterns. The effect is better than that of ink-printed products, so it is widely used in hot stamping book covers, packaging decoration, product advertisements, product samples and calendars Postcards and other fine print. Anodi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/00C09J133/08C09J125/14C09J123/08C09J131/04
Inventor 辜朝辉
Owner 浙江德尚化工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com