Finish paint composite and preparation method and use method thereof

A composition and topcoat technology, applied in the direction of pretreatment surface, device for coating liquid on surface, polyurea/polyurethane coating, etc., can solve the problem of insufficient paint film adhesion, high photoinitiator content, and fast photocuring speed and other problems, to achieve the effect of reducing internal stress residue, short curing time and good mechanical properties

Active Publication Date: 2011-03-02
CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
View PDF4 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of topcoat has the characteristics of high hardness and wear resistance, but because the photoinitiator content of this kind of topcoat is high, so the photocuring speed is fast, and there will be a large stress residue when the topcoat is cured by ultraviolet light, resulting in Insufficient adhesion of the paint film; more photoinitiators remain in the coating after UV curing of this topcoat, and most of the by-products generated by the reaction of photoinitiators contain chromophoric groups, resulting in yellowing of the paint film , especially for light-colored topcoats such as white pearl and silver gray

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Finish paint composite and preparation method and use method thereof
  • Finish paint composite and preparation method and use method thereof
  • Finish paint composite and preparation method and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0049] The present invention also provides a preparation method of the above-mentioned topcoat composition, comprising:

[0050] a), adding pigments and fillers and the water-based hydroxyacrylic resin with the structure shown in (I) to the auxiliary agent in turn, stirring for the first time, grinding after stirring, to obtain the first top coat;

[0051] b), adding water-based polyurethane acrylic resin, cross-linking agent, deionized water and photoinitiator to the first topcoat with the structure shown in (II) or (III) and stirring for the second time, filtering after stirring, get topcoat;

[0052]

[0053] R in formula (Ⅰ) 0 is a tertiary amino group, R in formula (II) and formula (III) 1 is a tertiary amino group, R 2 is a hydroxyacrylate group, R 3 is a diisocyanate group, R 4 is a polymer diol group, 20≤n≤60. The process of stirring the additives, pigments and water-based hydroxyacrylic resin can be a method well known to those skilled in the art, such as sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention provides a finish paint composite and a preparation method and use method thereof. The finish paint composite provided by the invention comprises: 9-44 wt% of water-borne hydroxylated acrylic resin of which the structure is disclosed in (I), 6-35 wt% of water-borne urethane acrylate resin of which the structure is disclosed in (II) or (III), 5.4-29.4 wt% of cross linking agent, 0.18-1.7 wt% of photoinitiator, 2.64-12.7 wt% of pigment filler, 2.37-8.9 wt% of accessory ingredient and 18-95.8 wt% of deionized water, wherein R0 in formula (I) is tertiary amine group, R1 in formulas (II) and (III) is tertiary amine group, R2 is hydroxyethyl acrylate group, R3 is diisocyanate group, R4 is polymer divalent alcohol group, and n is more than or equal to 20 and less than or equal to 60. The finish paint provided by the invention has high adhesive force, good yellowing resistance and low energy consumption of paint film solidification.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a topcoat composition and a preparation method and application method thereof. Background technique [0002] Automotive body coatings are multilayer systems that typically include electrophoretic deposition of a primer, midcoat, and topcoat. Among them, the topcoat layer is the outermost coating layer of the car, which is the most direct reflection of the decorative effect of the car appearance, and has a protective effect on the middle coat layer and the primer layer. [0003] Since the topcoat plays an important decorative and protective role in the entire coating of the car, the topcoat needs to have more perfect properties than the primer and the middle coat. Hardness and excellent weather resistance, corrosion resistance and water resistance, etc.; in order to make the paint film have better gloss and improve the decorative effect, the top coat also needs to have better leveling pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/16C09D133/14B05D3/02
Inventor 张红明吕金龙李季王献红王佛松
Owner CHANGCHUN INST OF APPLIED CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap