Method for forming hot melt super coating on coated abrasive tool

A kind of coated abrasive, hot-melt technology, applied in the direction of coating, device for coating liquid on the surface, abrasives, etc., can solve the problems of unhealthy operators, long production process, increased process, etc., to prevent burns Good effect, dense surface structure, cost reduction effect

Inactive Publication Date: 2011-04-13
ZIBO RIKEN MT COATED ABRASIVES
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantages of solvent-based coatings are: 1. Organic solvents are highly toxic, cause serious pollution, have a great impact on the environment, and are harmful to the health of operators
2. The price of organic solvents is relatively expensive, and most of them will be volatilized during use, resulting in high cost
3. The manufacturing process is relatively long and requires heating and drying, which consumes a lot of energy
[0006] The disadvantages of water-soluble coating products are: 1. The water-soluble emulsion system is unstable, which may easily lead to low product yield
2. The production process of water-soluble coating is long and requires heating and drying, which consumes a lot of energy
In actual production, it is necessary to purchase and prepare one or more of hot melt adhesives, hot melt lubricants or hot melt coatings, which objectively increases the product cost and increases the process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for forming hot melt super coating on coated abrasive tool
  • Method for forming hot melt super coating on coated abrasive tool
  • Method for forming hot melt super coating on coated abrasive tool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Zinc stearate is heated and melted at 120°C, and zinc stearate is coated on sandpaper by hot-melt coating equipment in a molten state, and cooled naturally to room temperature to make a hot-melt coating product.

[0032] Table 1 Comparative grinding data of hot-melt coating and solvent-based or water-soluble coated sandpaper (grinding aluminum rod)

[0033]

[0034] Table 1 and Figure 5 The data shows that the sanding performance of the resulting hot-melt coating product is better than that of ordinary solvent-based or water-soluble coatings.

Embodiment 2~5

[0036] Combination of zinc stearate (A) and paraffin (B) or zinc stearate (A), paraffin (B) and antioxidant (C)

[0037]

Embodiment 6~9

[0039] Combination of zinc stearate (A), paraffin (B), antioxidant (C) and EVA resin (D) or PP resin (E)

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for forming a hot melt super coating on a coated abrasive tool, which is to heat and melt a material and coat the molten material by a roller coating equipment onto the surface of the coated abrasive tool, and is characterized in that: the material is stearate, or a mixture of stearate and paraffin wax or a mixture of stearate, paraffin wax and antioxidant or mixture of stearate, paraffin wax, antioxidant and EVA resin or PP resin and is heated and melted at the temperature of 110 to 160 DEG C; the molten stearate or mixtures of the stearate is coated on the surface of abrasive paper or abrasive cloth by hot melt coating equipment; and naturally cooling, drying and obtaining hot melt coating products. The hot melt coating has the advantages of no toxicity, no solvent, low cost, short production route and the like compared with water soluble or solvent coating, and the obtained abrasive tool has a more compact surface structure and has the advantages of blockage prevention, burn prevention and the like in use.

Description

technical field [0001] The invention discloses a hot-melt supercoat coating method for coating abrasive tools, which belongs to the field of abrasive tool manufacturing. In particular, it relates to a coating method of a hot-melt supercoat coating on the surface of abrasive tools. Background technique [0002] Abrasives are tools used for grinding, grinding and polishing. Most of the grinding tools are artificial grinding tools made of abrasives and bonding agents, and natural grinding tools are also directly processed into natural ore rocks. In addition to being widely used in machinery manufacturing and other metal processing industries, abrasive tools are also used in the processing of non-metallic materials such as grain processing, paper industry, ceramics, glass, stone, plastic, rubber, and wood. Coated abrasives are an important part of abrasives, which refer to abrasives made by adhering abrasives to a flexible substrate (cloth or paper, etc.) with a binder. The c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/24B05C1/08B24D11/00
Inventor 翟建昌吴三国孟强郭巍
Owner ZIBO RIKEN MT COATED ABRASIVES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products