Ultraviolet curing white base paint and construction process on medium density fiber by using same

A technology of ultraviolet light and white primer, which is applied to the device for coating liquid on the surface, coating, pretreatment surface, etc., can solve the problem of great pollution to construction personnel and the environment, low overall benefit and efficiency, and volatilization of organic solvents Serious problems, to achieve the effect of good fullness, good filling and hiding power, and excellent adhesion

Active Publication Date: 2011-05-25
HUIZHOU CHANGRUNFA PAINT
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process involves a long time (at least 58 hours in rough calculation), high energy consumption, serious volatilization of organic solvents, great pollution to construction personnel and the environment, and the overall benefit and efficiency are not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The ultraviolet curing white primer (UV white primer) of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0036] 24 parts of polyurethane acrylate;

[0037] 28 parts of modified polyester acrylate;

[0038] 20 parts of monomer;

[0039] Filling agent 20 parts;

[0040] 5 parts of photoinitiator;

[0041] 0.7 parts of anti-settling agent;

[0042] 0.3 part of defoamer.

[0043] In the raw material formula of the above UV white primer, the polyurethane acrylate adopts Changxing 6170;

[0044] In the raw material formula of the above-mentioned ultraviolet curing white primer, the modified polyester acrylate adopts Changxing 6316;

[0045] In the raw material formula of the above UV white primer, the monomer uses tripropylene glycol diacrylate (TPGDA);

[0046] In the raw material formula of above-mentioned UV white primer, filler adopts 3000# talcum powder;

[0047] In the raw material formula of above-me...

Embodiment 2

[0055] The UV white primer of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0056] 26 parts of polyurethane acrylate;

[0057] 28 parts of modified polyester acrylate;

[0058] 20 parts of monomer;

[0059] Filling agent 20 parts;

[0060] 5 parts of photoinitiator;

[0061] 0.7 parts of anti-settling agent;

[0062] 0.3 part of defoamer.

[0063] In the raw material formula of the above UV white primer, the polyurethane acrylate adopts Changxing 6170;

[0064] In the raw material formula of the above UV white primer, the modified polyester acrylate adopts Changxing 6316;

[0065] In the raw material formula of the above UV white primer, the monomer uses tripropylene glycol diacrylate (TPGDA);

[0066] In the raw material formula of above-mentioned UV white primer, filler adopts 3000# talcum powder;

[0067] In the raw material formula of above-mentioned UV white primer, photoinitiator adopts photoinitiato...

Embodiment 3

[0076] The UV white primer of the present embodiment, its raw material formula is made up of each component of following parts by weight:

[0077] 28 parts of polyurethane acrylate;

[0078] 26 parts of modified polyester acrylate;

[0079] 20 parts of monomer;

[0080] Filling agent 20 parts;

[0081] 5 parts of photoinitiator;

[0082] 0.7 parts of anti-settling agent;

[0083] 0.3 part of defoamer.

[0084] In the raw material formula of the above UV white primer, the polyurethane acrylate adopts Changxing 6170;

[0085] In the raw material formula of the above UV white primer, the modified polyester acrylate adopts Changxing 6316;

[0086] In the raw material formula of the above UV white primer, the monomer uses tripropylene glycol diacrylate (TPGDA);

[0087] In the raw material formula of above-mentioned UV white primer, filler adopts 3000# talcum powder;

[0088] In the raw material formula of above-mentioned UV white primer, photoinitiator adopts photoinitiato...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses ultraviolet curing white base paint and a construction process on the medium density fiber by using same. The ultraviolet curing white base paint comprises the following components in parts by weight: 20-35 parts of urethane acrylate, 20-30 parts of modified polyester acrylate, 15-20 parts of monomer, 10-20 parts of filler, 3-5 parts of photoinitiator, 0.5-1 part of anti-settling agent and 0.2-0.3 parts of defoaming agent. The construction process of the invention comprises the following steps: firstly spraying quick-drying water-based white base paint on a bottom plate, polishing, coating the ultraviolet curing white base paint on the bottom plate once, performing ultreviolet curing, polishing, and then coating polyurethane (PU) colored paint. Compared with the traditional process, the adhesive force of the base paint used in the construction process of the invention is not lower than that of the base paint used in the traditional process, or even higher; and the operation is simple, the construction time is short, the efficiency can be greatly increased, the energy can be saved and the emissions of the volatile organic compound (VOC) can be greatly reduced.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to the coating of paint on a medium-fiber board, in particular to an ultraviolet-curable white primer and a construction process using the white primer on a medium-fiber board. Background technique [0002] In recent years, cabinet furniture mostly uses MDF as the base material, on which different colors and colorful effects can be made. [0003] Coating paint on the MDF, the traditional process is to first make a PU sealing primer on the MDF, after polishing, do 2~3 PE white primers, after it is completely dry, polish and then apply PU color paint . This process involves a long time (at least 58 hours in rough calculation), high energy consumption, serious volatilization of organic solvents, great pollution to construction personnel and the environment, and low overall benefits and efficiency. [0004] UV curing coatings, referred to as UV coatings, also known as photoinitiated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D167/06B05D1/38B05D3/06B05D7/08
Inventor 张运斌
Owner HUIZHOU CHANGRUNFA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More