Hot dipping covering agent

A covering agent and hot-dip coating technology, applied in hot-dip coating process, coating, metal material coating process, etc., can solve the problem of affecting the quality of alloy coating and the life of alloy liquid, high hot-dip coating temperature, and degradation of coating quality, etc. problems, to achieve the effect of simple preparation and application method, wide application range and improved surface quality

Inactive Publication Date: 2011-07-06
NORTHEASTERN UNIV
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the content of Al increases, a large amount of slag will be produced when the Zn-Al alloy is hot-dip, which will cause the alloy to be oxidized and then lost. large amount of energy
[0003] Existing covering agents, such as the NaCl-KCl system for pure aluminum and aluminum alloy plating, have a mass ratio of 1:1 and a melting point of 650°C, which is close to the melting point of zinc-aluminum alloys and zinc alloys, so it is not suitable for hot-dip galvanizing Aluminum alloy and zinc alloy, narrow scope of application; other covering salts, such as LiCl-NaCl or ZnCl 2 -NaCl system, although the melting points are 352°C and 365°C respectively, it is suitable for hot-dip galvanized aluminum alloy and zinc alloy, but there is a problem that the covering agent reacts with the alloy liquid and causes the loss of the alloy liquid
[0004] In addition, the traditional covering agent forms a large amount of slag in hot-dip galvanized aluminum alloy, zinc alloy and aluminum alloy, which is mainly composed of Al 2 o 3 , ZnO, Fe 2 al 5 、FeAl 3 , FeZn 7 This kind of slag affects the quality of the alloy coating and the life of the alloy liquid. Therefore, it is a challenge in the field of hot dip coating technology to find a covering salt that does not lose the alloy composition and has a wide range of applications, and does not react with the alloy liquid to form slag.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot dipping covering agent
  • Hot dipping covering agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: will be 5% KF by mass percentage, 15% LiCl, 30% KCl, 10% ZnCl 2 , 40% NaAlF 6 Mix and grind with a mortar until the particle size is not greater than 2mm, then dry in an oven at 120°C for 30 minutes to complete the preparation of the covering agent; the prepared covering agent has a melting point of 440°C and a density of 1.5765 g / cm 3 ;

[0026] After the alloy is melted, put in the covering agent; apply the above covering agent to hot-dip Zn-5%Al, Zn-55%Al, and pure Al respectively. The effect of covering agent is shown in Table 1:

[0027] Table 1 Covering salt effect of hot-dip galvanized aluminum alloy and aluminum alloy

[0028] alloy composition

[0029] figure 1 It is the appearance picture of the coating after hot-dip galvanized aluminum alloy and pure Al in Example 1. From left to right, it is respectively hot-dip Zn-5%Al, Zn-55%Al and pure Al. It can be seen from the figure that the present invention is used to cover The surface ...

Embodiment 2

[0030] Embodiment 2: will be 15% KF by mass percentage, 25% LiCl, 20% KCl, 5% ZnCl 2 , 35% NaAlF 6 Mix and grind with a mortar until the particle size is not greater than 2mm, and then dry in an oven at 120°C for 30 minutes to complete the preparation of the covering agent. The prepared covering agent has a melting point of 460°C and a density of 2.1207 g / cm 3 ;

[0031] Apply the above covering agents to hot-dip Zn-5%Al, Zn-55%Al, and pure Al respectively. The effects of the covering agents are shown in Table 2:

[0032] Table 2 Covering salt effect of hot-dip galvanized aluminum alloy and aluminum alloy

[0033] alloy composition

[0034] figure 2 It is the appearance picture of the coating after hot-dip galvanized aluminum alloy and pure Al in embodiment 2. From left to right, it is respectively hot-dip Zn-5%Al, Zn-55%Al and pure Al. It can be seen from the figure that the present invention is used to cover The surface of the coating after hot-dip coating is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Densityaaaaaaaaaa
Melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of hot dipping, in particular to a hot dipping covering agent. The hot dipping covering agent comprises the following components in percentage by weight: 5-15 percent of KF, 15-25 percent of LiCl, 20-30 percent of KCl, 5-10 percent of ZnCl2 and 35-40 percent of NaAlF6. The covering agent is prepared by the following steps of: mixing the components according to percentage by mass and grinding the mixture with a mortar until the particle size of the covering agent is less than or equal to 2.0 millimeters; putting the mixture into a baking box; and drying the mixture at the temperature of 120 DEG C for 30 minutes. The particle size of the hot dipping covering agent is less than or equal to 2.0 millimeters, the melting point is between 440 DEG C and 460 DEG C, and the density is between 1.5765 g / cm<3> and 2.1207 g / cm<3>. The hot dipping covering agent is suitable for hot dipping of a zinc high-aluminum alloy, a zinc alloy or an aluminum alloy.

Description

technical field [0001] The invention relates to the technical field of hot-dip plating, in particular to a covering agent for hot-dip plating. Background technique [0002] Hot-dip galvanizing technology is a very effective method for anti-corrosion of steel. Traditional hot-dip anti-corrosion coatings are mainly hot-dip pure Zn and hot-dip pure Al layers. Hot-dip Zn-Al alloy coating is a new technology developed in recent decades. Hot-dip Zn-5Al-RE (Galfan) and Zn-55Al-1.6Si (Galvalume) coatings are typical representatives of hot-dip Zn-Al alloy coatings. They all have good corrosion resistance. As the content of Al increases, a large amount of slag will be produced when the Zn-Al alloy is hot-dip, which will cause the alloy to be oxidized and then lost. Lots of energy. [0003] Existing covering agents, such as the NaCl-KCl system for pure aluminum and aluminum alloy plating, have a mass ratio of 1:1 and a melting point of 650°C, which is close to the melting point of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C2/30C23C2/06C23C2/12
Inventor 高波胡亮涂赣峰李世伟石为喜郝仪
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com