Conductive fiber for clothing

A technology for conductive fibers and clothing, applied in the field of fibers, can solve problems such as poor conductivity, and achieve the effects of increasing conductivity, enhancing mechanical strength, and high mechanical strength

Inactive Publication Date: 2011-08-17
JIHUA 3506 TEXTILE & APPL
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defects and problems of poor conductive effect existing in the prior art, and to provide a conductive fiber with better conductive effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A conductive fiber for clothing, its composition and weight ratio are: conductive carbon black 21, polyester 70, light shielding agent 2.2, coupling agent 1.5, dispersant 10.

[0025] The composition and weight ratio of the polyester are: 60% polyethylene terephthalate and 40% polyethylene resin.

[0026] The light shielding agent is silicon dioxide.

[0027] The coupling agent is zeolite powder.

[0028] The dispersant is a mixture of phosphoric acid ester and polyurethane.

Embodiment 2

[0030] A conductive fiber for clothing, including conductive carbon black and polyester, its composition and weight ratio are: conductive carbon black 28, polyester 65, light shielding agent 3, coupling agent 1.8, dispersant 9.

[0031] The composition and weight ratio of the polyester are: polyethylene terephthalate 60-80, polyethylene resin 20-40.

[0032] The light shielding agent is a mixture of silicon dioxide and calcium carbonate.

[0033] The coupling agent is a mixture of aluminate and oligomeric aluminate.

[0034] The dispersant is phosphoric acid ester.

Embodiment 3

[0036] A conductive fiber for clothing, including conductive carbon black and polyester, its composition and weight ratio are: conductive carbon black 25, polyester 60, light shielding agent 3, coupling agent 2, dispersant 10.

[0037] The composition and weight ratio of the polyester are: 70% polyethylene terephthalate and 30% polyethylene resin.

[0038] The light shielding agent is calcium carbonate.

[0039] The coupling agent is a mixture of aluminate, oligomeric aluminate and zeolite powder.

[0040] The dispersant is a mixture of phosphoric acid ester and polyurethane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a conductive fiber, which comprises the following components in parts by weight: 20-30 parts of conductive carbon black, 50-70 parts of polyester, 2-4 parts of light screener, 1-3 parts of coupling agent and 8-12 parts of dispersing agent, wherein the polyester comprises the following components in parts by weight: 60-80 parts of polyethylene terephthalate and 20-40 parts of polyethylene resin; the light screener is one or the mixture of silicon dioxide and calcium carbonate; the coupling agent is one or the mixture of aluminic acid ester, oligomeric aluminic acid and zeolite powder; and the dispersing agent is one or the mixture of phosphate ester and polyurethane. The conductive fiber has a good conducting effect and high mechanical strength.

Description

technical field [0001] The invention relates to a fiber, in particular to a conductive fiber for clothing, and is particularly suitable for the manufacture of a fiber with good conductive effect and strong spinnability. Background technique [0002] With the wide application of polymer materials such as synthetic fibers that are prone to static electricity and the popularization of static-sensitive microelectronic devices, static electricity in textiles has become the main cause of oil and pyrotechnic explosions and damage to microelectronic devices. The static electricity of textiles also causes clothing to entangle the human body, absorb dust, affect work efficiency, and affect health. For this reason, conductive fibers are often used to reduce the generation and accumulation of electrostatic charges, dissipate electrostatic charges, and overcome electrostatic interference. At the same time, some conductive fibers can also be used to block or absorb electromagnetic waves ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/14D01F8/06D01F1/09D01F1/10
Inventor 郭业丽鱼春荣熊文洲介继峰
Owner JIHUA 3506 TEXTILE & APPL