A bioactive calcium and abalone shell technology, applied in the field of food processing, can solve the problems of low reaction efficiency of chelated calcium, high requirements for crushing equipment, incomplete reaction, etc., and achieve good practical value and application prospect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0030] 1. Wash the abalone shell with water to remove impurities such as silt, drain and dry in a constant temperature blast drying oven at 90°C for 30 minutes;
[0031] 2. Put the dried abalone shell into the muffle furnace for calcination, the calcination temperature is 800°C, and the calcination time is 100min to obtain the abalone shell ash;
[0032] 3. Put the calcined abalone shell ash into the crushing equipment for coarse crushing to obtain abalone shell ash powder with a particle size of 30 mesh;
[0033] 4. Mix abalone shell ash powder with water to make milk of lime, and the mass ratio of the abalone shell ash powder to water is 1:14;
[0034] 5. Add abalone shell lime milk to the ultrasonic equipment, slowly add lactic acid solution with a mass percentage concentration of 50% according to the mass ratio of lactic acid solution and lime milk at a mass ratio of 8:15, ultrasonic treatment accelerates the reaction, ultrasonic power is 200W, ultrasonic The frequency is...
Embodiment 2
[0041] 1. Wash the abalone shells with water to remove impurities such as silt, drain and dry in a constant temperature blast drying oven at 95°C for 40 minutes;
[0042] 2. Put the dried abalone shell into a muffle furnace for calcination, the calcination temperature is 900°C, and the calcination time is 110min to obtain abalone shell ash;
[0043] 3. Put the calcined abalone shell ash into the crushing equipment for coarse crushing to obtain abalone shell ash powder with a particle size of 35 mesh;
[0044] 4. Mix abalone shell ash powder with water to make milk of lime, and the mass ratio of the abalone shell ash powder to water is 1:14;
[0045] 5. Add the abalone shell lime milk to the ultrasonic equipment, slowly add the lactic acid solution with a mass percentage concentration of 52% according to the mass ratio of the lactic acid solution and the lime milk at a mass ratio of 8:15, ultrasonic treatment accelerates the reaction, the ultrasonic power is 300W, and the ultraso...
Embodiment 3
[0052] 1. Wash the abalone shells with water to remove impurities such as silt, drain and dry in a constant temperature blast drying oven at 100°C for 50 minutes;
[0053] 2. Put the dried abalone shell into a muffle furnace for calcination, the calcination temperature is 1000°C, and the calcination time is 120min to obtain abalone shell ash;
[0054] 3. Put the calcined abalone shell ash into the crushing equipment for coarse crushing to obtain abalone shell ash powder with a particle size of 40 mesh;
[0055] 4. Mix the abalone shell ash powder with water to make milk of lime, and the mass ratio of the abalone shell ash powder to water is 1:15;
[0056] 5. Add abalone shell lime milk to the ultrasonic equipment, slowly add the lactic acid solution with a mass percentage concentration of 55% according to the mass ratio of lactic acid solution and lime milk at a mass ratio of 8:16, ultrasonic treatment accelerates the reaction, ultrasonic power is 600W, ultrasonic The frequen...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Granularity | aaaaa | aaaaa |