Water-in-water colorful stone simulated paint

A technology of water-in-water, imitation stone paint, applied in the field of architectural paint or interior and exterior wall coatings, can solve the problems of insufficient cohesion of pattern particles, poor cohesion of pattern particles, and easy breakage of pattern particles, and achieves strong stereoscopic effect and extended use Longevity, elegant effect of pattern

Inactive Publication Date: 2011-09-14
张兴艺
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, there are a small amount of water-in-water type Xuancai paint products for sale in the market, but the storage stability is generally poor. After a period of storage, the patterned particles will sink, and there will be a layer of protective glue on it. The solution is in a turbid state, obviously showing the same color as the patterned color grains
And the cohesive force of the patterned particles is not enough, after a period of storage, the patterned particles are easy to become broken, so that the sprayed Xuancai paint has a great change
Therefore, it is urgent to study a new type of water-in-water type Xuancai coating to solve the common problems of poor storage stability and poor cohesion of patterned particles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The preparation process includes 1) preparation of water dispersion phase; 2) preparation of protective glue; 3) preparation of water dispersion medium and 4) preparation of water-in-water type Xuancai imitation stone paint: wherein:

[0034] 1) The aqueous dispersed phase is made of the following raw materials in weight ratio:

[0035] Synthetic resin emulsion: 40 parts, film-forming aid: 1 part, titanium dioxide: 4 parts, calcium carbonate: 4 parts, dispersant: 0.4 part, defoamer: 0.25 part, thickener: 0.1 part, ammonia water: 0.022 , preservatives: 0.2 parts, water: 35 parts;

[0036] Preparation process: Add film-forming aids, titanium dioxide, calcium carbonate, dispersants, thickeners, ammonia, preservatives and water to the dispersion tank in sequence according to the formula amount, stir and mix evenly, and grind to a suitable Fineness, finally add synthetic resin emulsion and defoamer, adjust viscosity with thickener, and control the viscosity at 50-500CPS to ...

Embodiment 2

[0048] The preparation process includes 1) preparation of water dispersion phase; 2) preparation of protective glue; 3) preparation of water dispersion medium and 4) preparation of water-in-water type Xuancai imitation stone paint: wherein:

[0049] 1) The aqueous dispersed phase is made of the following raw materials in weight ratio:

[0050] Synthetic resin emulsion: 45 parts, film-forming aid: 2 parts, titanium dioxide: 6 parts, calcium carbonate: 6 parts, dispersant: 0.6 parts, defoamer: 0.35 parts, thickener: 0.2 parts, ammonia water: 0.02 parts parts, preservatives: 0.3 parts, water: 45 parts;

[0051] The preparation process is the same as in Example 1.

[0052] 2) The protective glue is made of raw materials with the following weight ratio:

[0053] Synthetic resin emulsion: 75 parts; dispersant: 1.5 parts; defoamer: 1 part; cellulose: 1 part; preservative: 0.2 parts; water: 35 parts;

[0054] The preparation process is the same as in Example 1.

[0055] 3) The water...

Embodiment 3

[0061] The process includes: 1) preparation of water dispersion phase; 2) preparation of protective glue; 3) preparation of water dispersion medium and 4) preparation of water-in-water type Xuancai imitation stone paint: wherein:

[0062] 1) The aqueous dispersed phase is made of the following raw materials in weight ratio:

[0063] Synthetic resin emulsion: 44 parts, film-forming aid: 1.8 parts, titanium dioxide: 5.5 parts, calcium carbonate: 5.5 parts, dispersant: 0.55 parts, defoamer: 0.32 parts, thickener: 0.18 parts, ammonia water: 0.03 parts parts, preservatives: 0.28 parts, water: 43 parts;

[0064] The preparation process is the same as in Example 1.

[0065] 2) The protective glue is made of raw materials with the following weight ratio:

[0066] Synthetic resin emulsion: 72 parts; dispersant: 1.3 parts; defoamer: 0.9 parts; cellulose: 0.8 parts; preservative: 0.19 parts; water: 32 parts

[0067] The preparation process is the same as in Example 1.

[0068] 3) The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a novel water-in-water colorful stone simulated paint, and belongs to the technical field of coating preparation. In the process of preparing a dispersion phase, a surface treated calcium carbonate is added, and the dispersion phase prepared from the calcium carbonate can be obviously separated from the aqueous phase; the protective glue component mainly consists of cellulose, water, water-soluble resin, defoaming agent, dispersant and preservative; by adding the protective glue component, the dispersion phase is coated by the protective glue, so that the prepared colorful paint has good stability and the dispersion phase is obviously separated from the dispersion medium; and the aqueous dispersion medium mainly consists of water, organic bentonite, aluminum sulfate and magnesium chloride. On the process design, secondary reaction of base paints is adopted to improve the viscosity of the base paints and the strength of cohesion; and on the formula design, protective solution with polarity is added among the base paints of different colors, and granules are uniformly distributed in the protective solution under mechanical action.

Description

technical field [0001] The invention relates to a building paint or a paint for interior and exterior walls, in particular to a water-in-water type black color imitation stone paint. Background technique [0002] With the improvement of living standards, people's pursuit of life is not only to solve the problem of food and clothing, but to the pursuit of spirit and materials. At the same time, people gradually begin to reflect simple and individual styles in the decoration of interior and exterior walls. The construction of Xuancai paint is relatively simple, and it can meet the needs of consumers in terms of product individuation and diversification, so it has gradually attracted people's attention. [0003] In the 1980s, Xuancai paint was popular in my country, but because it contained organic solvents such as toluene and xylene, a large amount of toxic organic solvents would be released during production and construction, which constituted a threat to the environment and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/29C09D7/12
Inventor 张兴艺钱皓窦俊英岳森李峰
Owner 张兴艺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap