Enhancement paster matrix, enhancement paster and steel plate composite material

A patch and matrix technology, applied in the field of reinforced patch matrix, reinforced patch and steel plate composite materials, can solve the problems of low adhesion of reinforced patch and high adhesion of reinforced patch

Active Publication Date: 2011-10-05
BYD CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the problem of low adhesion of the reinforced patch on the steel plate in the prior art, a reinforced patch matrix is ​​provided, and the reinforced patch prepared by the reinforced patch matrix has high adhesion on the surface of the oil-containing steel plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The preparation method of the steel plate composite material can adopt various existing methods, such as adhering the surface of the side of the reinforcing film without the reinforcement layer mentioned above on the steel plate, heating at 170-250 ° C for 20-50 min, That is, the steel plate composite material is obtained.

[0046] Preferably, the thickness ratio of the steel plate, the reinforcement patch matrix and the reinforcement layer is 0.6-1.2:0.5-5:0.05-2.

[0047] On the steel plate composite material prepared by the technical scheme disclosed in the invention, the adhesion of the reinforcement patch on the steel plate is strong.

Embodiment 1

[0050] This embodiment is used to illustrate the reinforced film matrix, reinforced film and steel plate composite material disclosed in the present invention.

[0051] With 100 parts by weight of epoxy resin (the bisphenol A epoxy resin of Nanya Epoxy Resin Co., Ltd., the number average molecular weight is 650, and the epoxy equivalent is 212 grams / equivalent), 80 parts by weight of non-reactive nitrile rubber (Jilin Petrochemical Butyronitrile-40 produced by the company has a number average molecular weight of 1600 and acrylonitrile content of 30), 13 parts by weight of diaminodiphenyl sulfone, 60 parts by weight of nano-calcium carbonate (average particle size is 90nm) and 20 parts by weight of styrene- Ethylene / butylene-styrene copolymer (the number-average molecular weight is 50,000, and the styrene content is 10wt%) is stirred and mixed for 50min under the condition of 100 rev / min at 110°C, then the mixture is cooled to 40°C, and Press into a sheet on a molding equipment...

Embodiment 2

[0055] This embodiment is used to illustrate the reinforced film matrix, reinforced film and steel plate composite material disclosed in the present invention.

[0056] 100 parts by weight of epoxy resin (the bisphenol F epoxy resin of South Asia Epoxy Resin Co., Ltd., the number average molecular weight is 5000, and the epoxy equivalent is 537 grams / equivalent), 15 parts by weight of non-reactive nitrile rubber (Jilin Petrochemical Produced by the company, the number average molecular weight is 4300, and the acrylonitrile content is 50), 7 parts by weight of diaminodiphenyl ether, 8 parts by weight of p-benzoquinone, 80 parts by weight of nano-calcium carbonate (average particle size is 40nm), 10 parts by weight of oxidation Zinc (average particle size is 30um) and 90 parts by weight styrene-butadiene-styrene copolymer (number average molecular weight is 200,000, styrene content is 35wt%), 10 parts by weight hydrogenated rosin at 120 ℃ and rotating speed is Stir and mix at 14...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides an enhancement paster matrix, an enhance paster and a steel plate composite material. The enhancement paster matrix, which contains epoxy resin, nitrile rubber, a filling material and a curing agent, is characterized in that the enhance paster matrix also contains adhesion promoting resin and the adhesion promoting resin contains styrene-ethene/butylene-styrol copolymer or styrene-butadiene-styrene copolymer. The enhancement paster prepared by the enhancement paster matrix has a high adhesion on the surface of steel plates, and especially antirust oil on the surface of steel plates has no impact on the adhesion.

Description

technical field [0001] The invention belongs to the field of automobile steel plate reinforcement, and in particular relates to a reinforcement patch matrix, a reinforcement patch and a steel plate composite material. Background technique [0002] At present, the world's climate continues to deteriorate, and the greenhouse effect is becoming more and more serious. As a major source of greenhouse gases, the emission of automobile exhaust has attracted more and more attention. [0003] In order to reduce the emission of automobile exhaust, reduce the weight of the vehicle body and reduce the average load of the automobile, it has become an effective method for energy saving and emission reduction. In actual automobile manufacturing, the weight of the body is generally reduced by reducing the thickness of the steel plate of the body to achieve the purpose of energy saving and consumption reduction. However, while reducing the thickness of the steel plate of the vehicle body, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/02C08L9/02C08L23/08C08L23/20C08L53/02C08L93/04C08K3/26C08K3/22C08K5/41C08K5/18B32B25/10B32B15/06B32B27/28B32B27/12B32B15/092B62D29/04
Inventor 常德才王辉刘勇
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka