Two-in-one water-soluble nail painting and protecting membrane solution

A water-soluble, two-in-one technology, used in manicure, cosmetics, cosmetic preparations, etc., can solve problems such as non-peeling, and achieve the effects of fast drying, outstanding water resistance, good fastness and adhesion

Active Publication Date: 2011-11-02
广州绿徽新材料研究院有限公司
View PDF0 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a two-in-one water-soluble manicure protection film solution for the shortcomings of the existing water-based nail polish and its preparation technology. The two-in-one water-soluble manicure protection film solution is remarkable in that The absorption of its "water-based" ingredients is faster than in the air, which can simultaneously solve the problem of rapid drying of water-based nail polish, long-lasting and firmness, non-toxic and tasteless, environmental protection and safety, heat and cold resistance during transportation and storage (temperature resistance from - 25°C to +90°C, continuous 96 hours, normal use after returning to normal temperature), high-difficulty technical problems such as super-bright mirror surface with good gloss and color retention effects, and also has the characteristics of not afraid of hot water immersion and friction, high hardness, attachment Strong, non-peelable, solvent-resistant, scratch-resistant and scratch-resistant, high-transparency, high-fullness, high-adhesion, gloss-retaining, color-retaining super-bright mirror surface (60-degree injection method, high-gloss ≥90) Features

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] 1. Use the following components and raw materials to prepare a two-in-one water-soluble nail armor film solution:

[0061] (1) Basic unit: modified waterborne polyurethane resin, its performance characteristics are: solid content 25%, hardness H, particle size 10nm;

[0062] (2) Water-soluble compound components: deionized water, film-forming aids, water-based organic silicon crosslinking agent, water-based thickening and leveling agent, water-based drier, water-based brightener, water-based polyurea hardener, emulsifier , Anti-cooling agent, bactericidal preservative, water-based high-efficiency dispersant, color-developing substance;

[0063] (3) The basic unit and the following water-soluble compound constituent units are made into base material according to the following raw material ratio:

[0064] Modified waterborne polyurethane resin 45%

[0065] Deionized water 20%

[0066] Film forming aid 8%

[0067] Waterborne silicone crosslinking agent 5%

[0068] Water-based thickeni...

Embodiment 2

[0087] 1. Use the following components and raw material ratios to prepare a two-in-one water-soluble nail armor film solution:

[0088] (1) Basic unit: modified waterborne polyurethane resin, its performance characteristics are: solid content 35%, hardness 2H, particle size 60nm;

[0089] (2) Water-soluble compound components: deionized water, film-forming aids, water-based organic silicon crosslinking agent, water-based thickening and leveling agent, water-based drier, water-based brightener, water-based polyurea hardener, emulsifier , Anti-cooling agent, bactericidal and preservative, water-based high-efficiency dispersant, coloring substance;

[0090] (3) The basic unit and the following water-soluble compound constituent units are made into base material according to the following raw material ratio:

[0091] Modified waterborne polyurethane resin 77.7%

[0092] Deionized water 8%

[0093] Film forming aid 3%

[0094] Water-based silicone crosslinking agent 3%

[0095] Water-based thi...

Embodiment 3

[0114] 1. Use the following components and raw materials to prepare a two-in-one water-soluble nail armor film solution:

[0115] (1) Basic unit: modified waterborne polyurethane resin, its performance characteristics are: solid content 55%, hardness 3H, particle size 80nm;

[0116] (2) Water-soluble compound components: deionized water, film-forming aids, water-based organic silicon crosslinking agent, water-based thickening and leveling agent, water-based drier, water-based brightener, water-based polyurea hardener, emulsifier , Anti-cooling agent, bactericidal preservative, water-based high-efficiency dispersant, coloring substance;

[0117] (3) The basic unit and the following water-soluble compound constituent units are made into base material according to the following raw material ratio:

[0118] Modified waterborne polyurethane resin 61.35%

[0119] Deionized water 14%

[0120] Film forming aid 5.5%

[0121] Waterborne silicone crosslinking agent 4%

[0122] Water-based thickening...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
particle diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a two-in-one water-soluble nail painting and protecting membrane solution. The solution is prepared by taking modified water-borne resin and a water-soluble compound as a base stock and mixing the base stock with a water-borne dispersant and a colour development substance. The two-in-one water-soluble nail painting and protecting membrane solution is non-toxic, tasteless,environmentally-friendly and safe. The water-soluble components in the solution are absorbed rapidly compared with that in air, therefore, highly difficult technical problems, such as quick drying, no fear of hot water soak and friction, high hardness, strong adhesive force, excellent solvent resistance, scratch resistance and scrape resistance, high fullness, good effects on protecting light andcolour (a 60-degree incoming method and a mirror surface with a special bright surface on which highlight is more than or equal to 90), heat resistance and cold resistance (temperature resistance is from -25 DEG C to +90 DEG C for 96 h continuously, and the solution can be normally used at room temperature) during transporting and storing, are completely solved in the same time,. In addition, thetwo-in-one water-soluble nail painting and protecting membrane solution has the characteristics of capability of regulating colours, alternating colours, mixing colours, or colour-painting nails, mobile phones, teacups or the surfaces of other living objects according to the favour, and the like. The two-in-one water-soluble nail painting and protecting membrane solution can be washed away by an ester or alcohol solution after being painted on nails.

Description

technical field [0001] The invention relates to a manicure protection film solution, in particular to a two-in-one water-soluble manicure protection film solution. Background technique [0002] At present, there are many types and quantities of water-based nail polish and oil-based nail polish on the market, but there are problems of one kind or another. If they are not taken seriously and a good solution is taken, it will not only affect human health, but also affect the development of the entire industry. cause a certain impact. [0003] At present, most of the traditional oil-based nail polishes on the market contain a large amount of irritating chemicals (usually accounting for 70%). They have a severe nasal odor and can enter the human body through the skin and inhalation. Regular use will affect human health. For example, phthalates in traditional oily nail polish can interfere with normal hormonal balance and cause serious reproductive damage and other health problem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/87A61K8/86A61K8/85A61K8/84A61K8/81A61Q3/02
CPCA61K8/85A61K8/87A61K8/81A61K8/84A61Q3/02A61K8/86A61Q3/00
Inventor 谭卓华孙东成郭亨堆
Owner 广州绿徽新材料研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products