A kind of anti-adhesive paper preparation method with well-tac-toe groove structure

A technology of anti-sticking paper and tic-tac-toe, which is applied in the field of light industry papermaking, can solve the problems of high manufacturing cost and large amount of silicone oil used for anti-sticking paper, and achieve the effects of reducing production costs, good anti-sticking performance, and reducing consumption

Inactive Publication Date: 2011-12-14
FUJIAN NORMAL UNIV
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is mainly to provide a new production process to prepare anti-adhesive paper in order to solve the problems of large amount of silicone oil and high manufacturing cost of the existing anti-adhesive paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-adhesive paper preparation method with well-tac-toe groove structure
  • A kind of anti-adhesive paper preparation method with well-tac-toe groove structure
  • A kind of anti-adhesive paper preparation method with well-tac-toe groove structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Use a corona treatment machine to treat the surface of the backing paper of the release paper with a power of 600W for 100s.

[0029] (2) Mix polyethylene and isocyanate-modified polyethylene uniformly in a mass ratio of 1:0.1, first heat the bridge at a temperature of 180°C, then increase the temperature to 280°C, and apply a pressure of 10Mpa after melting It is extruded and kept at a temperature of about 320°C when laminating. After coating, the coated paper is obtained, and the coating amount is 10g / m 2 .

[0030] (3) The conveyor belt sends the coated paper to the roller with a convex module at a conveying speed of 60m / min for rolling.

[0031] After rolling, grooves appear on the surface of the coated paper. The size of the groove is 15mm×15mm, the depth of the groove is 1.8mm, and the width of the well-shaped side on the side is 12mm. Cool the fluted coated paper.

[0032] (4) Add methyl silicone oil to 1.0g / m 2 The amount of dry silicon coated evenly o...

Embodiment 2

[0035] (1) Use a corona treatment machine to treat the surface of the backing paper of the release paper with a power of 800W for 100s.

[0036] (2) Mix polyethylene and isocyanate-modified polypropylene evenly in a mass ratio of 1:0.2, first heat and bridge at a temperature of 250°C, then increase the temperature to 300°C, and apply a pressure of 20Mpa after melting It is extruded and kept at a temperature of about 380°C when laminating. After coating, the coated paper is obtained, and the coating amount is 6g / m 2 .

[0037] (3) The conveyor belt sends the coated paper to the rollers with convex modules at a conveying speed of 100m / min for rolling.

[0038] After rolling, grooves appear on the surface of the coated paper. The size of the groove is 15mm×15mm, the depth of the groove is 0.6mm, and the width of the well-shaped side of the side is 10mm. Cool the fluted coated paper.

[0039] (4) Add methyl hydrogen silicone oil at 1.5g / m 2 The amount of dry silicon coated e...

Embodiment 3

[0042] (1) Use a corona treatment machine to treat the surface of the backing paper of the release paper with a power of 800W for 100s.

[0043] (2) Mix polyethylene and isocyanate-modified polyethylene evenly in a mass ratio of 1:0.15, first heat the bridge at a temperature of 200°C, then increase the temperature to 350°C, and apply a pressure of 16Mpa after melting It is extruded and kept at a temperature of about 330°C during coating. After coating, the coated paper is obtained. The amount of coating is 20g / m 2 .

[0044] (3) The conveyor belt sends the coated paper to the rollers with convex modules at a conveying speed of 80m / min for rolling.

[0045] After rolling, grooves appear on the surface of the coated paper. The size of the groove is 15mm×15mm, the depth of the concave-convex groove is 1.5mm, and the width of the well-shaped side on the side is 11mm. Cool the fluted coated paper.

[0046] (4) Add methyl vinyl silicone oil at 2g / m 2 The amount of dry silicon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of light industry papermaking, and relates to a method for preparing anti-adhesive paper with a well-shaped groove structure. In this method, polyethylene and modified polyolefin are evenly mixed in a mass ratio of 1:0.1 to 0.2, heated and melted, and coated onto the corona pretreated backing paper with a coating amount of 10- 20g/m2, after cooling, the coated paper is obtained; after the coated paper is rolled by a roller with a convex module, grooves appear on the surface; the silicone oil is coated with 1.0-2.0g/m2 of dry silicon by a coating machine The amount of coating is evenly coated on the surface of the coated paper; then it is dried at 100°C to 200°C in three temperature sections, and the release paper is obtained after cooling. With the method of the present invention, after the anti-adhesive paper is rolled into grooves, the concave part of the anti-adhesive paper is not coated with anti-adhesive agent, thereby reducing the amount of silicone oil used, the amount of organic solvent used, the production cost, and environmental protection. Energy saving requirements.

Description

technical field [0001] The invention belongs to the field of light industry papermaking, and relates to a method for preparing release paper, in particular to a method for preparing release paper with a well-shaped groove structure. Background technique [0002] The release paper is mainly pasted on the glued surface of the tape to protect the adhesive layer on the surface of the tape. The anti-adhesive paper is composed of a base paper, an isolation layer and an anti-adhesive layer. The preparation process is to coat a layer of release agent on the entire surface of the base paper (the release agent used mainly includes polyethylene), and then coat the surface of the coating layer with a layer of release agent. A layer of release agent (adopted release agent is mainly silicone oil) is coated to obtain release paper. [0003] Silicone oil is generally a colorless or light yellow, odorless, non-toxic, non-volatile liquid. Silicone oil is insoluble in water, methanol, glycol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/02D21H17/35D21H19/00
Inventor 陈登龙吴钦缘
Owner FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap