Solid phase synthesis method of silver and chitosan and/or chitosan derivative nanometer compound

A technology of chitosan derivatives and nanocomposites, which is applied in the field of solid-phase synthesis of silver, chitosan and/or its derivative nanocomposites, can solve problems such as preparation methods and applications that have not been reported, and achieves Uniform particle size effect

Inactive Publication Date: 2012-02-22
LIAOCHENG UNIV
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation method and application of silver-chitosan and its derivatives nanocomposite powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid phase synthesis method of silver and chitosan and/or chitosan derivative nanometer compound
  • Solid phase synthesis method of silver and chitosan and/or chitosan derivative nanometer compound

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0053] Example 1

[0054] A silver and chitosan nanocomposite, the preparation method steps are as follows:

[0055] (1) Grind 10g of chitosan into fine powder;

[0056] (2) Grind 0.005g silver nitrate into fine powder;

[0057] (3) Mix fine chitosan powder with fine silver nitrate powder and grind thoroughly for 1 hour;

[0058] (4) Add 0.005 g of ascorbic acid and continue to fully grind for 2 hours to obtain a silver and chitosan nanocomposite with a silver particle size of 1-100 nm (sample 1).

Example Embodiment

[0059] Example 2

[0060] A silver and chitosan derivative nanocomposite, the preparation method steps are as follows:

[0061] (1) Grind 10g of carboxymethyl chitosan into fine powder;

[0062] (2) Grind 0.005g silver nitrate into fine powder;

[0063] (3) Mix fine carboxymethyl chitosan powder with fine silver nitrate powder and grind thoroughly for 2 hours;

[0064] (4) Add 0.005 g of glucose and continue to grind thoroughly for 2.5 hours to obtain a nanocomposite of silver and chitosan derivatives with a silver particle size of 1-100 nm (sample 2).

Example Embodiment

[0065] Example 3

[0066] A nanocomposite of silver, chitosan and chitosan derivatives, the preparation method is as follows:

[0067] (1) Grind 7g chitosan and 3g hydroxypropyl chitosan into fine powder;

[0068] (2) Grind 0.005g silver nitrate into fine powder;

[0069] (3) Mix chitosan and hydroxypropyl chitosan fine powder with silver nitrate fine powder, and grind thoroughly for 2 hours;

[0070] (4) Add 0.005 g of N-acetylglucosamine and continue to fully grind for 6 hours to obtain a nanocomposite of silver, chitosan and chitosan derivative with a silver particle size of 1-100 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a solid phase synthesis method of a silver and chitosan and/or chitosan derivative nanometer compound. The silver and chitosan and/or chitosan derivative nanometer compound has the effects of promoting wound healing, stopping bleeding, relieving pain, diminishing inflammation and killing bacteria. The silver and chitosan and/or chitosan derivative nanometer compound can beutilized for treating female colpitis, cervicitis, cervical erosion, bedsore, skin ulcers, burns, scalds, wounds, other skin inflammation, tinea manus and tinea pedis. The silver and chitosan and/or chitosan derivative nanometer compound also can be utilized for preparation of various wound dressings such as films, sponges, suppositories for gynaecology, and adhesive films.

Description

[0001] This application is a divisional application: original application number: 200910017600.8, filing date: 2009.8.11, invention name: preparation method and application of nanocomposite of silver, chitosan and / or its derivatives. technical field [0002] The invention relates to the technical fields of chemical industry and medicine, in particular to a preparation method of silver, chitosan and / or chitosan derivative nanocomposite powder and its application in the treatment of female vaginitis, cervicitis, cervical erosion, bedsore, skin Ulcers, burns, scalds, wounds, and other skin inflammations, tinea pedis and other pharmaceutical applications, and can also be used to prepare various trauma dressings such as films, sponges, gynecological suppositories, films, etc. Background technique [0003] Chitosan is the deacetylation product of chitin, and it is a basic amino polysaccharide existing in nature. In recent years, studies by scholars at home and abroad have shown th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L5/08C08K3/08B22F9/20
Inventor 桑青秦东风
Owner LIAOCHENG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products