White acrylic resin plastic cement primer and its preparation method

A technology of acrylic resin and methyl methacrylate, which is applied in the field of paint making, can solve the problem that the coating is not resistant to boiling salt water, etc., and achieve the effect of excellent boiling resistance

Inactive Publication Date: 2012-02-29
深圳市美丽华科技股份有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a white acrylic resin plastic primer and its preparation method, aiming to solve the problem in the prior art that the coating of the white primer for the plastic case of the mobile phone and the button is not resistant to boiled salt water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0066] Ethylene glycol butyl ether 2.0%;

[0067] Butyl acetate 2.5%;

[0068] Methyl isobutyl ketone 2.5%;

[0069] Cyclohexanone 1.0%;

[0070] Toluene 2.5%;

[0071] Polymethylmethacrylate 2.0%;

[0072] Dispersant Disperbyk-111 0.05%;

[0073] Titanium dioxide Ti-pure R902 18.0%;

[0074] Polystyrene modified methyl methacrylate 40.5%;

[0075] 80-200 seconds nitrocellulose solution 18.5%;

[0076] Butanone 1.5%;

[0077] Ethyl acetate 4.95%;

[0078] Isobutanol 2.5%;

[0079] Plasticizer Plasticizer 168 1.0%;

[0080] Polyacrylic acid leveling agent (BYK-358) 0.5%.

[0081] The white acrylic resin plastic primer produced by the above formula is diluted and sprayed on the surface of the polycarbonate plastic shell with a diluent, baked at 70-80°C for 10-15 minutes, and then sprayed with an ultraviolet radiation curing topcoat.

Embodiment 2

[0083] Ethylene glycol butyl ether 1.0%;

[0084] Butyl acetate 4.9%;

[0085] Methyl isobutyl ketone 5.0%;

[0086] Cyclohexanone 1.0%;

[0087] Toluene 5.0%;

[0088] Polymethylmethacrylate 1.0%;

[0089] Dispersant Disperbyk-111 0.1%;

[0090] Titanium dioxide Ti-pure R902 15.0%;

[0091] Polystyrene modified methyl methacrylate 38.0%;

[0092] 80-200 seconds nitrocellulose solution 20.0%;

[0093] Butanone 1.0%;

[0094] Ethyl acetate 1.0%;

[0095] Isobutanol 1.0%;

[0096] Plasticizer Plasticizer 168 5.0%;

[0097] Polyacrylic acid leveling agent (BYK-358) 1.0%.

[0098] The white acrylic resin plastic primer produced by the above formula is diluted and sprayed on the surface of the polycarbonate plastic shell with a diluent, baked at 70-80°C for 10-15 minutes, and then sprayed with an ultraviolet radiation curing topcoat.

Embodiment 3

[0100] Ethylene glycol butyl ether 4.45%;

[0101] Butyl acetate 1.0%;

[0102] Methyl isobutyl ketone 1.0%;

[0103] Cyclohexanone 5.0%;

[0104] Toluene 1.0%;

[0105] Polymethylmethacrylate 5.0%;

[0106] Dispersant Disperbyk-111 0.05%;

[0107] Titanium dioxide Ti-pure R902 20.0%;

[0108] Polystyrene modified methyl methacrylate 43.0%;

[0109] 80-200 seconds nitrocellulose solution 15.0%;

[0110] Butanone 1.0%;

[0111] Ethyl acetate 1.0%;

[0112] Isobutanol 1.0%;

[0113] Plasticizer Plasticizer 168 1.0%;

[0114] Polyacrylic acid leveling agent (BYK-358) 0.5%.

[0115] The white acrylic resin plastic primer produced by the above formula is diluted and sprayed on the surface of the polycarbonate plastic shell with a diluent, baked at 70-80°C for 10-15 minutes, and then sprayed with an ultraviolet radiation curing topcoat.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a white acrylic resin plastic cement primer and its preparation method. The white acrylic resin plastic cement primer provided by the invention contains main components of polystyrene modified methyl methacrylate, polymethyl methacrylate, a cellulose nitrate liquid of 80-200 second and titanium dioxide, and simultaneously contains a solvent and an auxiliary agent. The white primer prepared by the formula accords with the requirement on halogen-free paints in the mobile-phone industry. A diluent and an ultraviolet curing top finish are sprayed on polycarbonate plastic housing and buttons of a handset. The dried and cured coating has excellent boiling resistance. After boiled in water of 100 DEG C for 30 minutes, the coating will not foam, crack and change color.

Description

technical field [0001] The invention relates to the field of paint making, in particular to a white acrylic resin plastic primer used for surface coating of polycarbonate plastic shells and keys of mobile phones and a preparation method thereof. Background technique [0002] At present, the plastic casings and buttons of mobile phones are painted with halogen-containing white primers and UV radiation-curable topcoats, and also with halogen-free white primers with UV radiation-curable topcoats. The limitation of environmental management substances has clearly stipulated the halogen content in the mobile phone coating formula. It is required that the bromine content in the mobile phone coating formula is less than 900ppm, the chlorine content is less than 900 ppm, and the total content of bromine and chlorine is less than 1500 ppm. The primer is not suitable for some mobile phone manufacturers; at present, some mobile phone paint users require the white primer cover to be spra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D125/14C09D133/12C09D101/18C09D7/12C08J7/04
Inventor 鲁春风
Owner 深圳市美丽华科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More