Recycled aggregate medium-dry hard concrete prepared by using building waste and preparation method of recycled aggregate medium-dry hard concrete

A dry hard concrete and construction waste technology, applied in the field of semi-dry hard concrete and its preparation, can solve the problems that the construction quality and service life cannot be guaranteed

Inactive Publication Date: 2013-01-02
云南华威废弃物资源化有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because the physical properties of waste concrete and natural building materials are quite different, such as the water absorption rate of waste concrete is relatively large, usually 3.6-8%, while the water absorption rate of natural aggregate is less than 3%, the construction quality cannot be guaranteed if the usual method is used. and service life
[0004] "Construction Method of Dry Hard Concrete" Patent No. 201010501877.0 of Chinese patent literature report, "A kind of preparation method of Dry Hard Concrete Test Block" Patent No. 201010501859, all are dry hard concrete construction methods, there is no semi-dry hard concrete, especially It is a patent report on the construction method of recycled aggregate semi-dry hard concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recycled aggregate medium-dry hard concrete prepared by using building waste and preparation method of recycled aggregate medium-dry hard concrete
  • Recycled aggregate medium-dry hard concrete prepared by using building waste and preparation method of recycled aggregate medium-dry hard concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Below in conjunction with embodiment, the present invention is described in further detail and completeness:

[0015] Recycled aggregate semi-dry hard concrete prepared from construction waste. According to the "Common Concrete Mix Proportion Design Regulations" (JGJ55-2000), with the C30 concrete mix ratio as the benchmark, refer to the "Technical Specifications for Highway Cement Concrete Pavement Construction" (JTG F30-2003), "General Portland Cement" (GB 175 -2007) and "Technical Specifications for the Application of Fly Ash Concrete" (GBJ 146-90).

[0016] 1. Raw materials

[0017] It is composed of the following raw materials by weight, coarse aggregate 1200-1320, fine aggregate 580-620, gelling agent 320-420, water reducer and water, the gelling agent is cement and fly ash, cement accounts for 60-90% of the gelling agent, fly ash accounts for 10-40% of the gelling agent, the water reducing agent is 0.3-0.5% of the cement content, and the water is 150±10. The s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a recycled aggregate medium-dry hard concrete prepared by using building waste, which comprises the following raw materials of coarse aggregate, fine aggregate, a gelatinizing agent, a water reducing agent and water, wherein the gelatinizing agent comprises cement and coal ash, and the coarse aggregate comprises 50-100 percent of recycled coarse aggregate prepared from thebuilding waste. A preparation method of the recycled aggregate medium-dry hard concrete comprises the following steps of: pretreating the building waste, removing impurities, remaining waste concrete, waste bricks and the like; crushing and screening to prepare the recycled coarse aggregate; mixing the recycled coarse aggregate, natural sand, cement and water according to the proportion, adding the coal ash and the water reducing agent, stirring uniformly to obtain a mixture; and squeezing and forming the mixture, curing for 2 days to obtain the recycled aggregate medium-dry hard concrete. The invention solves the problems of worsening ecological environment and the like caused by difficulty in treating the building waste; and the building wastes are used for manufacturing the recycled aggregate for replacing natural aggregate, the increasingly deficient natural aggregate and damage degree to the ecological environment are reduced, and the living environment of human beings is protected. The recycled aggregate medium-dry hard concrete prepared by using the method has high strength and high abrasive resistance, and can be used for building base installations such as city roads, housing constructions and the like.

Description

technical field [0001] The invention relates to a semi-dry hard concrete and a preparation method thereof, in particular to a recycled aggregate semi-dry hard concrete prepared from construction waste and a method thereof. Background technique [0002] According to the workability of the mixture, concrete can be divided into dry hard concrete, semi-dry hard concrete, plastic concrete, fluid concrete, high fluid concrete and fluid concrete. Generally, the concrete whose consistency value is greater than 30s is called super-dry hard concrete, the consistency value between 20s and 30s is called dry hard concrete, and the consistency value less than 20s is called semi-dry hard concrete. Ordinary concrete in construction engineering is called ordinary concrete mixture before it is set and hardened. It must have good consistency and workability, which is convenient for construction operations such as mixing, transportation, pouring, and tamping, and has the properties of uniform ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B28/04
Inventor 吴勇生李如燕孙可伟林志伟张剑波
Owner 云南华威废弃物资源化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products