Preparation method of hydroprocessing catalyst

A hydrogenation treatment and catalyst technology, applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve problems such as limited effect and complicated process, so as to improve utilization rate, improve dispersion, avoid The effect of reactive metal entry

Active Publication Date: 2012-05-23
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method process is too co...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] This example describes the preparation of alumina carrier with pseudo-boehmite dry rubber powder. The specific surface area of ​​the pseudo-boehmite dry rubber powder is 390m 2 / g, the pore volume is 0.90ml / g.

[0033] According to the weight ratio of pseudo-boehmite dry rubber powder and SB powder of 3:1, mix evenly, add an appropriate amount of acid solution, and HNO in the acid solution 3 The weight concentration is 1.84%, and the rest is distilled water. After rolling for 20 minutes, squeeze the strips with a clover orifice plate with a diameter of 1.9 mm. After drying at 120°C for 4 hours and calcining at 500°C for 3 hours, the resulting alumina carrier strip is marked as A.

Embodiment 2

[0035] The invention prepares a catalyst.

[0036] Use 5g of glycerol to make an aqueous solution, impregnate 100g of carrier A in an equal volume, place it for 2 hours, and treat it at 150°C for 1.5 hours in an air atmosphere to obtain a carrier that supports organics. Use an impregnating solution containing Mo, Ni, and P with equal volume The carrier was impregnated, dried in an air atmosphere at 150°C for 2 hours, and calcined in an air atmosphere at 450°C for 1.5 hours. The catalyst obtained was designated as CAT1.

Embodiment 3

[0038] The invention prepares a catalyst.

[0039] Use 15g of glycerol to make an aqueous solution, impregnate 100g of carrier A in an equal volume, leave it for 2 hours, and treat it at 180°C for 1.5 hours in an air atmosphere to obtain a carrier that supports organics. Use an impregnating solution containing Mo, Ni, and P with equal volume The carrier was impregnated, dried in an air atmosphere at 150°C for 2 hours, and calcined in an air atmosphere at 480°C for 2 hours, and the catalyst obtained was designated as CAT2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of hydroprocessing catalyst, comprising the following steps of: (1) preparing a porous catalyst carrier; (2) impregnating the catalyst carrier with organic compound solution; (3) carrying out heat treatment by utilizing the organic compound additive supported carrier obtained by the step (2); (4) supporting active metal component onto the organic matter supported carrier, so as to obtain a catalyst precursor; and (5) roasting the catalyst precursor obtained by the step (4), so as to obtain the hydroprocessing catalyst. In the preparation method disclosed by the invention, the organic matter is uniformly supported onto surface of the catalyst carrier, and then the active metal is supported, operational performance of the catalyst is improved, especially aggregation of the catalyst in a roasting process is reduced, and dispersion of the active metal of the catalyst is improved.

Description

Technical field [0001] The invention relates to a preparation method of a hydroprocessing catalyst, in particular to a preparation method of a high-activity hydroprocessing catalyst. Background technique [0002] Crude oil and distillate oil obtained from crude oil contain impurities such as sulfur, nitrogen, oxygen and metals. The presence of these impurities not only affects the stability of the oil, but also emits SO during use X , NO X And other harmful gases pollute the environment. In the secondary processing of oil products, the presence of impurities such as sulfur, nitrogen, oxygen and metals can poison the catalyst. Therefore, removing the above impurities is an important process in oil processing. Distillate hydrotreating refers to the process in which feed oil and hydrogen come into contact with the catalyst at a certain temperature and pressure to remove impurities and saturated with aromatics. [0003] Typical hydrotreating catalysts are oxides of metals of groups ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J37/02C10G45/04
Inventor 彭绍忠吕振辉
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap