Thermoplastic elastomer, preparation method thereof, application thereof and cable sheathing tube made therefrom

A thermoplastic elastomer, reactive technology, applied in the direction of insulating cables, cables, conductors, etc., can solve the problems of poor low temperature resistance, poor surface performance, poor processing performance, etc., to achieve light weight, environmental friendliness, excellent low temperature resistance performance Effect

Inactive Publication Date: 2012-05-30
SHANGHAI FRONTIER ELASTOMER
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] An object of the present invention is to provide a thermoplastic elastomer to overcome the defects of exis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic elastomer, preparation method thereof, application thereof and cable sheathing tube made therefrom
  • Thermoplastic elastomer, preparation method thereof, application thereof and cable sheathing tube made therefrom
  • Thermoplastic elastomer, preparation method thereof, application thereof and cable sheathing tube made therefrom

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Weighing raw materials: 100 parts of SEBS, 60 parts of paraffinic mineral oil, 20 parts of polypropylene, 5 parts of polyphenylene ether, 30 parts of flame retardant, 0.2 part of reactive high polysiloxane, 0.2 part of stabilizer, processing aid 0.4 parts.

[0047] The SEBS is styrene-ethylene-butylene-styrene block copolymer (KRATON G-1651), the chain hydrocarbon mineral oil is paraffin oil, the flame retardant is decabromodiphenylethane, the The stabilizer is antioxidant 1010, and the processing aid is α-methylstyrene.

[0048] Premix SEBS with chain hydrocarbon mineral oil and let it stand, then add the mixture and other raw material components into a two-way double-screw ribbon horizontal mixer (purchased from Taiwan Jinjiaxin Plastic Machinery Co., Ltd., model DJ2500) and mix evenly. A twin-screw mixing and granulating machine (purchased from Coperion Keya (Nanjing) Machinery Co., Ltd., model TE-75) melted and mixed, extruded and granulated, the mixing temperature...

Embodiment 2

[0050] Weighing raw materials: 100 parts of SEBS, 80 parts of paraffinic mineral oil, 40 parts of polypropylene, 5 parts of polyphenylene ether, 30 parts of flame retardant, 0.2 part of reactive high polysiloxane, 0.2 part of stabilizer, processing aid 0.4 parts.

[0051] The SEBS is styrene-ethylene-butylene-styrene block copolymer (KRATON G-1651), the chain hydrocarbon mineral oil is paraffin oil, the flame retardant is decabromodiphenylethane, the The stabilizer is antioxidant 1010, and the processing aid is α-methylstyrene.

[0052] Premix SEBS with chain hydrocarbon mineral oil and let it stand, then add the mixture and other raw material components into a two-way double-screw ribbon horizontal mixer (purchased from Taiwan Jinjiaxin Plastic Machinery Co., Ltd., model DJ2500) and mix evenly. A twin-screw mixing and granulating machine (purchased from Coperon Keya (Nanjing) Machinery Co., Ltd., model TE-75) melted and mixed, extruded and granulated, the mixing temperature wa...

Embodiment 3

[0054] Weigh raw materials: 100 parts of SEBS, 100 parts of paraffinic mineral oil, 50 parts of polypropylene, 5 parts of polyphenylene ether, 30 parts of flame retardant, 0.2 part of reactive polysiloxane, 0.2 part of stabilizer, processing aid 0.4 parts.

[0055] The SEBS is styrene-ethylene-butylene-styrene block copolymer (KRATON G-1651), the chain hydrocarbon mineral oil is paraffin oil, the flame retardant is decabromodiphenylethane, the The stabilizer is antioxidant 1010, and the processing aid is α-methylstyrene.

[0056] Premix SEBS with chain hydrocarbon mineral oil and let it stand, then add the mixture and other raw material components into a two-way double-screw ribbon horizontal mixer (purchased from Taiwan Jinjiaxin Plastic Machinery Co., Ltd., model DJ2500) and mix evenly. A twin-screw mixing and granulating machine (purchased from Coperion Keya (Nanjing) Machinery Co., Ltd., model TE-75) melted and mixed, extruded and granulated, the mixing temperature was 19...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Vicat softening point temperatureaaaaaaaaaa
Surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention provides a thermoplastic elastomer which comprises the following ingredients in parts by weight: 100 parts of SEBS (Styrene-Ethylene-Butadiene-Styrene), 60-120 parts of chain hydrocarbon mineral oil, 20-80 parts of polypropylene, 5-20 parts of polyphenylether, 30-70 parts of flame retardant, 0.2-0.3 part of reactive polysiloxane, 0.2-0.6 part of stabilizer and 0.4-1.0 part of processing additive. The invention further provides a preparation method of the thermoplastic elastomer, application of the thermoplastic elastomer and a cable sheathing tube made from the thermoplastic elastomer. Compared with the prior art, the thermoplastic elastomer has the beneficial effects that: the thermoplastic elastomer shows excellent heat resistance, the temperature of the Vicat softening point of the thermoplastic elastomer is 100DEG C, meanwhile, the thermoplastic elastomer has excellent low temperature resistance, the temperature for low-temperature embrittlement of the thermoplastic elastomer is -70DEG C, therefore, the defects that the existing material easily embrittles at low temperature and softens at high temperature are overcome; the obtained formed product has balance in elasticity and plasticity and the function of strong surface hydrophobicity; and the thermoplastic elastomer is lightweight, good in weather resisting property and environmentally-friendly.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a thermoplastic elastomer, a preparation method, its application and a cable sheath made of it. Background technique [0002] Existing bare steel-cored aluminum wires for high-voltage power transmission are directly exposed to the air, and encounter more and more complicated losses and safety issues caused by water accumulation, ice coating, corrosion, and contact caused by various climate changes. On the one hand, at the beginning of 2008, most parts of southern China were hit by a blizzard that had not happened in nearly 50 years, causing many transmission lines in many places in the south to be disconnected and down. The power department hopes to add a protective sheath to the cable in order to achieve the main function of anti-ice and snow condensation. The sheath is required to be assembled to adapt to the outdoor all-weather environment and the condition...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/02C08L23/12C08L71/12C08L83/06C08K5/03C08K3/22C08K3/38H01B7/17
Inventor 应启广马建伟朴成浩谷宗宝孙忠凤
Owner SHANGHAI FRONTIER ELASTOMER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap