Film-coating product

A product and film layer technology, applied in the field of high-temperature heat-treated coated glass, can solve the problems of silver loss of low-radiation function, performance change, and performance degradation, and achieve high visible light transmittance, low surface resistance, and low emissivity.

Inactive Publication Date: 2012-07-11
FUYAO GLASS IND GROUP CO LTD +1
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Nowadays, in the production of off-line low-emissivity coated glass, most of them use pure silver as the functional film layer to reflect infrared rays. Because pure metal silver is easy to react with sulfide gas in the air, the performance of silver will be degraded, and silver will be easily oxidized and lost during high temperature heat treatment. Low-emissivity function, therefore, the current production of low-emissivity coated glass uses a multi-layer dielectric layer to protect the silver layer, and many low-emissivity coatings have great changes in performance after high-temperature heat treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] On the glass substrate 2.0C, sequentially plate ZnSnO with a thickness of 42nm 2 Film layer; Ag with a thickness of 12nm 1-a Nb a Film layer, wherein a=15wt%; a Ti film layer with a thickness of 3nm; a ZnSnO with a thickness of 22nm 2 Film layer; Si with a thickness of 18nm 3 N 4 The film layer is used as a protective layer to obtain heat-treatable low-emissivity coated glass.

[0051] Optical performance test

[0052] Before heat treatment, the emissivity of a single piece of low-emissivity coated glass is 0.055, and the visible light transmittance is 80.6%. The resistance is 11.2Ω / square; the low-emissivity coated laminated glass obtained after washing and assembling has been tested, and its visible light transmittance is 76.3%, and its direct solar transmittance is 48.7%.

[0053] physical properties

[0054] According to GB9656-2003, impact test, radiation resistance test, damp heat cycle test, etc. can meet the requirements. After testing, the knocking test...

Embodiment 2

[0056] On the glass substrate 2.0C, sequentially plate ZnSnO with a thickness of 37nm 1.8 Film layer; Ag with a thickness of 10nm 1-a Nb a Film layer, wherein a=2.5wt%; Ti film layer with a thickness of 2nm; ZnSnO with a thickness of 76nm 1.8 Film layer; Ag with a thickness of 12nm 1-a Nb a Film layer, wherein a=2.5wt%; a Ti film layer with a thickness of 3nm; a ZnSnO layer with a thickness of 28nm 1.8 Film layer; TiO with a thickness of 10 nm 2 The film layer is used as a protective layer to obtain heat-treatable low-emissivity coated glass.

[0057] Optical performance test

[0058] Before heat treatment, the emissivity of a single piece of low-emissivity coated glass is 0.041, and the visible light transmittance is 78.8%. The resistance is 4.1Ω / square; the low-emissivity coated laminated glass obtained after washing and assembling has been tested, and its visible light transmittance is 75.1%, and its direct solar transmittance is 41.6%.

[0059] physical properties ...

Embodiment 3

[0062] On the glass substrate 2.0C, sequentially plate ZnSnO with a thickness of 34nm 2.3 Film layer; Ag with a thickness of 12nm 1-a Nb a Film layer, wherein a=0.05wt%; Ti film layer with a thickness of 2nm; ZnSnO with a thickness of 72nm 2.3 Film layer; Ag with a thickness of 10nm 1-a Nb a Film layer, wherein a=0.05wt%; Ti film layer with a thickness of 3nm; ZnSnO with a thickness of 68nm 2.3 Film layer; Ag with a thickness of 9nm 1-a Nb a Film layer, wherein a=0.05wt%; Ti film layer with a thickness of 3nm; ZnSnO with a thickness of 22nm 2.3 Film layer; ZrO with a thickness of 12nm 2 The film layer is used as a protective layer to obtain heat-treatable low-emissivity coated glass.

[0063] Optical performance test

[0064] Before heat treatment, the emissivity of a single piece of low-emissivity coated glass is 0.022, and the visible light transmittance is 76.1%. The resistance is 2.1Ω / square; the low-emissivity coated laminated glass obtained after washing and as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a film-coating product, in particular relates to film-coating glass capable of being performed with high-temperature thermal treatment. Materials for reflecting infrared film layers of the film-coating product is changed from traditional pure silver materials into alloy materials of silver and niobium, an Agl-aNba film layer deposited by the alloy materials of silver and niobium replaces a pure silver film layer to serve as a functional layer of the film-coating product, stability of films in high-temperature thermal treatment is improved, and simultaneously chemical stability of a silver layer is improved and mechanical performance of the silver layer is improved. The film-coating product has high visible light transmission rate, good mechanical resistance and chemical stability. The film-coating product is mainly used in automobile windshields.

Description

【Technical field】 [0001] The invention relates to a coated product, in particular to a coated glass capable of high temperature heat treatment. 【Background technique】 [0002] Ordinary glass has no heat insulation function. With the enhancement of people's awareness of energy saving, many buildings or cars now use low-emissivity coated glass or heat-reflective coated glass. These coated glasses can play a very good heat insulation effect, making the building Increased comfort inside the vehicle or in the vehicle. [0003] Chinese patent CN201020503119.8 discloses a single-silver low-emissivity glass. The single-silver low-emission glass uses an AgCu layer instead of the traditional pure silver film layer as the functional layer, so that the product has the characteristics of low reflectivity and low emissivity. The patent discloses that the copper-containing silver alloy used as the infrared reflection layer has a good infrared reflection function, but the copper contained ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/06B32B9/04C03C17/36C03C27/12
Inventor 尚贵才李艺明
Owner FUYAO GLASS IND GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap