Thermal-sublimation water-based intaglio printing ink and preparation method thereof

A sublimation and water-based technology, applied in transfer printing, ink, printing, etc., can solve the problems of inability to prepare dye content, ink with high color concentration, etc., achieve excellent storage stability, clear printing patterns, and is conducive to safe production and The effect of environmental protection

Inactive Publication Date: 2012-07-18
SUN YAT SEN UNIV +1
View PDF8 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitation of chemical reaction, this method ca

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The N-vinylamide-acrylic acid ester copolymer emulsion formula prepared in embodiment 1 is as shown in table 1:

[0056] Table 1 Emulsion monomer mass and its percentage

[0057] monomer name Dosage / g Mass percentage / % MMA 153 68 NVP 45 20 BA 20.3 9 VAC 4.5 2 A-174 2.2 1 Total monomer 225 100

[0058] The synthesis process of the N-vinylamide-acrylate copolymer emulsion of the present embodiment is as follows:

[0059] Dissolve 0.45g AIBN in a mixture of 45g NVP, 153g MMA, 20.3g BA, 4.5g VAc and 2.2g A-174 cross-linking monomer, and add it to 81g solution containing 2.5g emulsifier CO- 436 and 1.25g of emulsifier NP-10 in deionized water, emulsified at high speed for 60min to prepare a pre-emulsion for use. Then add 27g of 10% PVA-1799 aqueous solution, 1.25g of CO-436 and 0.63g of NP-10, 130g of deionized water, 1.12g of sodium bicarbonate in the normal pressure reactor, and start stirring to raise the ...

Embodiment 2

[0067] The N-vinylamide-acrylate copolymer emulsion formula prepared in embodiment 2 is as shown in table 3:

[0068] Table 3 Emulsion monomer mass and its percentage

[0069] monomer name Dosage / g Mass percentage / % MMA 148.5 66 NVC 45 20 BA 15.7 7 VAC 4.5 2 AC-76 11.3 5 Total monomer 225 100

[0070] The synthesis process of the N-vinylamide-acrylate copolymer emulsion of the present embodiment is as follows:

[0071] Dissolve 0.75g AIBN in a mixture of 45g NVC, 148.5g MMA, 15.7g BA, 4.5g VAc and 11.3g AC-76 cross-linking monomer, and add it to 80.8g emulsifier 073 dissolved in 3g and 1.5g of emulsifier NP-40 in deionized water, and emulsified at high speed for 60min to prepare a pre-emulsion for use. Then add 13.5g concentration in the normal pressure reactor and be 10% PVA-1799 aqueous solution, 1.5g emulsifier 073 and 0.75g emulsifier NP-40, the deionized water of 139g, 0.9g sodium bicarbonate, start to stir a...

Embodiment 3

[0079] The N-vinylamide-acrylate copolymer emulsion formula prepared in embodiment 3 is as shown in table 5:

[0080] Table 5 Emulsion monomer mass and its percentage

[0081] monomer name Dosage / g Mass percentage / % MMA 134.4 56 NVC 38.4 16 BA 43.2 18 AM 4.8 2 AC-76 19.2 8 Total monomer 240 100

[0082] The synthesis process of the N-vinylamide-acrylate copolymer emulsion of the present embodiment is as follows:

[0083] Dissolve 0.64g AIBN in a mixture of 38.4g NVC, 134.4g MMA, 43.2g BA, 4.8g AM and 19.2g AC-76 cross-linking monomer, and add it to 73.8g emulsified solution containing 3.36g 073 and 1.12g of emulsifier NP-40 in deionized water, emulsified at high speed for 60min to prepare a pre-emulsion for use. Adding 24g concentration then is the PVA-2099 aqueous solution of 10% in normal pressure reactor, 1.68g emulsifier 073 and 0.56g emulsifier NP-40, the deionized water of 120.6g, 1.68g sodium acetate, start...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Thermal decomposition temperatureaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses thermal-sublimation water-based intaglio printing ink and a preparation method thereof. The thermal-sublimation water-based intaglio printing ink is composed of components in percentage by weight: 15-35% of disperse dye size, 24-50% of an N-vinylamide-acrylic ester copolymer emulsion, 0.3-2.5% of a thickening agent, 0.1-2% of an antifoaming agent, 0.1-3% of a neutralizer, 0.1-0.5% of a preservative and 10-42% of de-ionized water. The thermal-sublimation water-based intaglio printing ink has high heat resistance; and transferred printing paper is not adhered to a cloth material in a transfer printing process. The thermal-sublimation water-based intaglio printing ink also has excellent storage stability; patterns printed on various transferred printing paper are clear; the printing patterns transferred onto dacron, nylon cloth material and textile have clear profiles without any friction ghosting and transfer ghosting and are bright in color; and color fastness complies with wearing requirements. The thermal-sublimation water-based intaglio printing ink has no any toxic organic solvent residue, can be diluted with water and is good for safe production and environment protection.

Description

technical field [0001] The invention belongs to the field of inks, and in particular relates to a sublimation water-based gravure printing ink and a preparation method thereof. Background technique [0002] The sublimation transfer printing technology of disperse dyes has been applied to synthetic fiber fabrics since the 1970s, and it is still stable at more than 5% of the total global printing industry. The use of sublimation water-based gravure printing ink is to print the ink on the transfer paper first, and the printed paper and the fabric are overlapped in a heat press machine and heated (150-250°C) under pressure. The dye in the ink layer is heated and directly From solid dye to gaseous phase, it penetrates into the fiber and makes it colored. The printing process of this kind of textile cloth and fabric does not need to be washed, and the cloth feels soft after printing, which not only saves costs but also does not pollute the environment. In addition, the entire pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/10D06P5/28D06P1/16D06P1/52C08F220/14C08F226/10C08F226/06C08F2/30C08F2/26
Inventor 王小妹张超李欣李瑞良许嘉年
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products