Recycled PC (Polycarbonate) and recycled PET (polyethylene terephthalate)-containing halogen-free flame retardant resin composition and preparation method thereof

A technology of flame retardant resin and composition, applied in the field of composition and preparation thereof, can solve the problems of large influence on the performance of recycled PET, limited application of recycled PET, and no mention of the utilization of recycled materials, so as to improve molecular weight and solve poor stability. , the effect of reducing production costs

Active Publication Date: 2012-07-25
SHANGHAI KUMHO SUNNY PLASTICS
View PDF9 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN101338070A patent describes the preparation of a flame-retardant polycarbonate and polyester resin composition modified by a rubber-modified aromatic vinyl copolymer containing epoxy groups, but does not mention the utilization of recycled materials
[0008] Compared with recycled PC,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recycled PC (Polycarbonate) and recycled PET (polyethylene terephthalate)-containing halogen-free flame retardant resin composition and preparation method thereof
  • Recycled PC (Polycarbonate) and recycled PET (polyethylene terephthalate)-containing halogen-free flame retardant resin composition and preparation method thereof
  • Recycled PC (Polycarbonate) and recycled PET (polyethylene terephthalate)-containing halogen-free flame retardant resin composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～10

[0051] 1. Examples 1-10 and Comparative Examples 1-16

[0052] 1.1. Explanation of the meaning of the component code

[0053] Component A-1: ​​PC, polycarbonate with a weight average molecular weight of 25,000, produced by Hunan Petrochemical;

[0054] Component A-2: PC, polycarbonate with a weight average molecular weight of 21,000, produced by Hunan Petrochemical;

[0055] Component A-3: Regenerated PC, commercially available, the weight average molecular weight of polycarbonate is 24000;

[0056] Component: B-1: Regenerated PET, commercially available, its source is PET beverage bottle flakes, with a viscosity of 0.8dl / g;

[0057] Component B-2: virgin PET, viscosity 1.0, produced by Jinshan Petrochemical;

[0058] Component C-1: styrene-acrylonitrile copolymer-glycidyl methacrylate terpolymer (SAN-co-GMA), GMA content is 8%, acrylonitrile content is 28%;

[0059] Component C-2: styrene-acrylonitrile copolymer-glycidyl methacrylate terpolymer (SAN-co-GMA), GMA conten...

Embodiment 11～14

[0134] Examples 11 to 14 respectively provide halogen-free flame-retardant resin compositions containing recycled PC and recycled PET.

[0135] 2.1. Explanation of the meaning of the component code

[0136] Component A-1a, native PC, bisphenol A aromatic polycarbonate, with a weight average molecular weight of 10,000;

[0137] Component A-2a, virgin PC, bisphenol A type aromatic polycarbonate, with a weight average molecular weight of 40,000;

[0138] Component A-3a, regenerated PC, bisphenol A type aromatic polycarbonate, with a weight average molecular weight of 10000;

[0139] Component A-3b, regenerated PC, bisphenol A aromatic polycarbonate, with a weight average molecular weight of 40,000;

[0140] Component B-1a, recycled PET, commercially available, with a viscosity of 0.65dl / g;

[0141] Component B-1b, recycled PET, commercially available, with a viscosity of 0.9dl / g;

[0142] Component C-6: styrene-acrylonitrile copolymer-glycidyl methacrylate terpolymer (SAN-G...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a recycled PC (Polycarbonate) and recycled PET (polyethylene terephthalate)-containing halogen-free flame retardant resin composition and a preparation method thereof. The recycled PC and recycled PET-containing halogen-free flame retardant resin composition comprises the following components by weight percentage: 5 to 50% of native PC, 20 to 63% of recycled PC, 5 to 35% of recycled PET, 5 to 15% of toughener, 10 to 20% of flame retardant, 0.1 to 0.8% of flame-retardant anti-dripping agent, 0.1 to 1% of antioxidant, 0.1 to 2% of lubricant, and 0.2 to 2% of styrene-acrylonitrile-glycidyl methacrylate terpolymer containing 1 to 5% of glycidyl methacrylate and 20 to 33% of acrylonitrile. The preparation method comprises the following steps that: after the components are prepared, the recycled PET, the styrene-acrylonitrile-glycidyl methacrylate terpolymer are fully mixed, led out, subjected to extrusion granulation, and made into masterbatcehs; then the masterbatches and the remaining components are fully mixed, led out, and subjected to extrusion granulation to obtain the recycled PC and recycled PET-containing halogen-free flame retardant resin composition. The recycled PC and recycled PET-containing halogen-free flame retardant resin composition has a higher impact performance and good stability.

Description

technical field [0001] The invention relates to a composition and a preparation method thereof, in particular to a halogen-free flame-retardant resin composition containing recycled PC and recycled PET and a preparation method thereof. Background technique [0002] With the continuous and rapid development of the plastic industry, plastic products have been widely used in various industries, but accompanied by an increasing number of plastic waste, resulting in a huge waste of energy, more and more attention has been paid to the recycling of waste plastics . [0003] As we all know, plastic raw materials are chemical products extracted from natural petroleum. Petroleum is the lifeblood of modern industry and a non-renewable natural resource. According to statistics from relevant departments, the annual plastic waste generated by a medium-sized city can meet the raw material needs of 20 small and medium-sized plastic enterprises. Therefore, recycled plastic is petroleum rec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L67/02C08L25/14C08J3/22
Inventor 李文强高磊李强罗明华辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap