Tool for compacting thick-walled hollow carbon/carbon (C/C) composite product

A composite material, hollow core technology, applied in metal material coating process, gaseous chemical plating, coating and other directions, can solve the problem of inability to achieve fast densification and uniform densification, large difference in density between inside and outside of products, and uniformity of distribution. problems, to achieve the effect of easy promotion and use, long service life and shortened residence time

Active Publication Date: 2014-02-12
XIAN AEROSPACE COMPOSITE MATERIALS INST
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the low decomposition temperature of conventional cracked gas (such as propylene) and its large molecular weight, it is easier to deposit on the outside of the C / C composite material preform in the soaking deposition process, thereby affecting the flow of cracked gas to the C / C composite material preform. Further diffusion inside, eventually leading to the inability to achieve rapid and uniform densification
[0004] In the traditional soaking CVI densification process, there are few special designs for the deposition space, which can easily cause the gas flow state to be disordered, and the reaction gas cannot flow out of this space immediately, thus forming a large hydrocarbon gas intermediate product. The product is more likely to produce by-products such as carbon black, and the density difference between the inside and outside of the product is large, which prolongs the densification cycle of pyrolytic carbon and affects the uniformity of its distribution state

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tool for compacting thick-walled hollow carbon/carbon (C/C) composite product
  • Tool for compacting thick-walled hollow carbon/carbon (C/C) composite product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] like figure 1 The dense tooling of a thick-walled hollow C / C composite product shown includes an outer cylinder 1, an air intake base 4 installed on the bottom of the outer cylinder 1, and an air intake base 4 installed on the top of the outer cylinder 1 for dispelling the gas in the outer cylinder 1. The derived air guiding device 9, the inside of the outer cylinder 1 and the upper part of the air intake base 4 are provided with an intake base 6, and a cavity 5 is formed between the intake base 4 and the intake base 6, specifically Yes, the air intake base 4 is provided with a support cylinder 3 that closely fits the inner wall of the outer cylinder 1, and the air intake base plate 6 is installed on the upper part of the support cylinder 3, so that the air intake base 4 and the intake air A cavity one 5 is formed between the gas substrates 6, the air intake base 4 is provided with an air inlet 4-1 for inputting gas into the cavity one 5, and the top surface of the gas ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tool for compacting a thick-walled hollow carbon / carbon (C / C) composite product, which comprises an outer barrel, a gas inlet substrate and a gas guide device, wherein the interior of the outer barrel is provided with a gas inlet basal plate; a cavity I is formed between the gas inlet substrate and the gas inlet basal plate; the gas inlet substrate is provided with a gas inlet; the top face of the gas inlet basal plate is provided with an inner barrel; a to-be-compacted thick-walled hollow C / C composite preform is sheathed onto the inner barrel; a gap I for the circulation of gas is formed between the outer surface of the C / C composite preform and the inner surface of the outer barrel; a gap II for the circulation of the gas is formed between the inner surface of the C / C composite preform and the outer surface of the inner barrel; and the gas inlet basal plate is provided with a plurality of diversion passages II and diversion passages III, wherein the diversion passages II are used for communicating the cavity I with the gap I, and the diversion passages III are used for communicating the cavity I and the gap II. According to the tool for compacting the thick-walled hollow C / C composite product, gas diversion can be performed, and thereby, the retention period of pyrolysis gas in a depositing space is shortened, and the C / C composite preform is rapidly and evenly compacted.

Description

technical field [0001] The invention relates to a dense tooling, in particular to a dense tooling for thick-walled hollow C / C composite material products. Background technique [0002] C / C composite material, that is, carbon fiber reinforced carbon-based composite material, is a high-performance material with the characteristics of light weight, high strength, high modulus, high dimensional stability, high chemical stability and high temperature resistance. It is widely used in high-tech fields such as aerospace, high-speed trains, and thermal field materials. Studies have shown that the mechanical / ablative properties of C / C composites vary with the amount of pyrolytic carbon they contain. With the increase of pyrolytic carbon content, the compression, shear and ablation resistance properties of the material are greatly improved. [0003] Chemical vapor infiltration (CVI) is a traditional method for preparing pyrolytic carbon. Due to the low decomposition temperature of c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C16/455C23C16/26
Inventor 李晋崔红李瑞珍庞菲孙建涛解惠贞张晓虎王坤杰
Owner XIAN AEROSPACE COMPOSITE MATERIALS INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products