Method for preparing steel ladle or tundish covering agent by using boron slurry

A covering agent and tundish technology, which is applied in the field of iron and steel metallurgy, can solve the problems of no boron mud being found, increase the cost of covering agent raw materials, processing and manufacturing costs, and high production costs, and achieve good spreadability, heat preservation and anti-oxidation effects, low cost effect

Inactive Publication Date: 2014-08-20
JIANGSU UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] China is rich in boron resources, with proven reserves exceeding 100 million tons (calculated as B2O3 ), however, most of the boron ores in China are of low grade, and most of them are mixed ores. The cost is too high and the treatment process is complicated. At present, China still lacks an industrialized method for realizing high value-added comprehensive utilization of waste boron mud. It has been treated as waste slag accumulation, which not only occupies a lot of land resources, but also has a large amount of open-air accumulation of boron mud. Soil and water Resources are seriously polluted; the accumulated boron mud in China is nearly 100 million tons, and the pollution and land occupation problems are becoming more and more serious. The comprehensive utilization of boron mud needs to be solved urgently
[0003]The main purpose of the ladle covering agent is to isolate the molten steel from the air, to avoid the inhalation and oxidation of the molten steel and to have a certain heat preservation effect. The basic components of the covering agent in the prior art are CaO, SiO2, Al2O3, MgO, Fe2O3, coke powder, etc., such as Chinese invention patents (application numbers 01105402.6, 200410084336.7, 200510023196.7), etc., all propose ladle covering agents composed of different proportions of the above materials; at present, these covering agents are basically composed of lime, silica, Wollastonite, corundum powder, magnesia and other single minerals are mixed and prepared, and the production cost is high, and these mineral resources are non-renewable resources, which are getting less and less, so the raw material cost and processing and manufacturing cost of the covering agent are increased.
[0004]The main composition of boron mud powder after dehydration is: MgO 24~40%, SiO2 20~35%, B2 O3 2~4%, Al2O3 2~4%, Fe2 O3 2~4%, CaO 2-10%, of which CaO, MgO, SiO2, Al2O3, B2O3, etc. are all important components in the covering agent, so it can be considered to treat boron mud as the main raw material of the covering agent; Iron oxide, phosphate and sulfide in boron mud are regarded as the main harmful substances used as ladle or tundish covering agent. With the development of society, the quality of steel is getting higher and higher, and boron mud must be specially treated and added with other components. The element can be used for ladle or tundish covering agent only after component adjustment, and search the prior art, do not find relevant reports on how to process boron mud and use it as ladle or tundish covering agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Step 1: boron mud treatment:

[0037] Using boron slime from a factory in Dandong as raw material, the boron slime is roasted and dehydrated in a reducing atmosphere formed by CO. The temperature of reduction roasting, dehydration and drying is controlled at 450°C. Then, the boron mud is removed by magnetic separation to remove Fe in the boron mud. 3 o 4 And Fe, Mn, the boron mud treated in this way can be used as one of the raw materials for the ladle or tundish covering agent, and the content (mass percentage) of MgO in the boron mud is 35%.

[0038] Step 2: CaO--Al 2 o 3 Preparation of premelted mixture:

[0039] Choose lime and corundum powder, according to CaO (48%, mass percentage) and Al 2 o 3 (52%, mass percentage) pre-melted at 1450 ° C, cooled and pulverized to obtain CaO--Al 2 o 3 The pre-melted mixture, the main mineral phase formed is 12CaO·7Al 2 o 3 .

[0040] Step three:

[0041] The carbonaceous material in this embodiment selects fine coke po...

Embodiment 2

[0044] Step 1: boron mud treatment:

[0045] Using boron mud from a factory in Dandong as raw material, the boron mud was passed through H 2 The formed reducing atmosphere is roasted, dehydrated and dried, and the temperature of the reduced roasted, dehydrated and dried is controlled at 400°C. Then, the boron mud is removed by magnetic separation to remove Fe in the boron mud. 3 o 4 And Fe, Mn, the boron mud treated in this way can be used as one of the raw materials for the ladle or tundish covering agent, and the content (mass percentage) of MgO in the boron mud is 30%.

[0046] Step 2: CaO--Al 2 o 3 Preparation of premelted mixture:

[0047] Lime and corundum powder are selected, according to CaO (46%, mass percentage) and Al 2 o 3 (54%, mass percentage) pre-melted at 1400 ° C, cooled and pulverized to obtain CaO--Al 2 o 3 The pre-melted mixture, the main mineral phase formed is 12CaO·7Al 2 o 3 .

[0048] Step three:

[0049] In this embodiment, carbon black is ...

Embodiment 3

[0052] Step 1: boron mud treatment:

[0053] Using boron mud from a factory in Dandong as raw material, the boron mud is passed through CO and H 2 Roasting, dehydration and drying under the formed reducing atmosphere, the temperature of reduction roasting, dehydration and drying is controlled at 500°C, and then the boron mud is removed by magnetic separation to remove the Fe in the boron mud 3 o 4 And Fe, Mn, the boron mud treated in this way can be used as one of the raw materials for the ladle or tundish covering agent, and the content (mass percentage) of MgO in the boron mud is 28%.

[0054] Step 2: CaO--Al 2 o 3 Preparation of premelted mixture:

[0055] Choose lime and corundum powder, according to CaO (52%, mass percentage) and Al 2 o 3 (48%, mass percentage) pre-melted at 1500 ° C, cooled and pulverized to obtain CaO--Al 2 o 3 The pre-melted mixture, the main mineral phase formed is 12CaO·7Al 2 o 3 .

[0056] Step three:

[0057] According to needs, add 2% ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of iron and steel metallurgy, in particular to a method for preparing a ladle or tundish covering agent by utilizing boron mud. In the present invention, firstly, the boron mud is dehydrated and dried in a gas furnace, the Fe2O3 in the boron mud is transformed into magnetic Fe3O4, and the MnO is reduced to Mn, which is then removed by magnetic separation, and the pre-melted mixture of CaO and Al2O3 is added to obtain the As a covering agent for molten steel in ladles or tundishes, a small amount of carbonaceous materials that control melting speed and melting performance can also be added as covering agents. The invention not only realizes the reuse of waste boron mud resources, but also has the advantages of simple preparation process, low processing cost, elimination of boron mud hazards, and reduction of metallurgical waste discharge. It has good performance, good spreadability, good effect of preventing molten steel from inhaling oxidation and heat preservation, has remarkable economic and social benefits, and is worth popularizing.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to a method for preparing a ladle or tundish covering agent by utilizing boron mud. Background technique [0002] my country is rich in boron resources, with proven reserves exceeding 100 million tons (in B 2 o 3 However, the grade of most boron ores in my country is low, and most of them are mixed ores. After extracting borax by carbon-alkali method, a large amount of waste boron mud will be produced. Since boron, iron, magnesium, etc. in boron mud are all lean ores, The extraction cost is too high and the treatment process is complicated. At present, my country still lacks an industrialized method for the comprehensive utilization of waste boron mud with high added value. Water resources are seriously polluted; boron mud has accumulated nearly 100 million tons in my country, and the pollution and land occupation problems are becoming more and more serious. The co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/111B22D1/00
Inventor 王宏明李桂荣赵玉涛杨丽莉曹磊赵加爱赵钊
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products