High water concrete for sidewalks and preparation method thereof

A concrete and sidewalk technology, applied in the field of special concrete, can solve the problems of rapid urbanization and environmental protection, increasing the drainage volume of urban drainage systems, increasing sewage treatment costs, etc., so as to reduce the heat island effect, broaden the use, improve Effect of water storage and circulation functions

Inactive Publication Date: 2012-09-19
重庆北足泡沫混凝土技术有限公司
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main disadvantage of this patent is: the prepared special concrete only has good water permeability, which only solves the problem of no water accumulation on the road surface in rainy days, but increases the drainage volu...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A kind of component and weight percent thereof of high water storage concrete for sidewalk are:

[0038] Cementitious material: 10% Porous aggregate: 83%

[0039] Water: 6.94% Water reducer: 0.03%

[0040] Redispersible latex powder: 0.03% Foaming agent: 0%

[0041] Among them: the porous aggregate is clay brick aggregate with a particle size of 0.9mm to 35mm; the water reducing agent is a naphthalene-based high-efficiency water reducing agent; the cementing material is cement, fly ash, slag powder, etc., and the cementing material is The weight percentage is:

[0042] Cement: 25% Fly Ash: 35%

[0043] Slag powder: 40%;

[0044] The foaming agent is an existing foaming agent.

[0045] A kind of preparation method of high water storage foam concrete for sidewalk, the concrete steps of described method are as follows:

[0046] (1) material preparation

[0047] Prepare materials according to the components and weight percentages of the high water storage concrete fo...

Embodiment 2

[0063] A kind of component and weight percent thereof of high water storage concrete for sidewalk are:

[0064] Cementitious material: 30% Porous aggregate: 55%

[0065] Water: 13.49% Water reducer: 0.5%

[0066] Redispersible latex powder: 1.0% Foaming agent: 0.01%

[0067] Among them: the porous aggregate is ceramic brick aggregate with a particle size of 0.9mm to 35mm; the water reducer is polycarboxylate high-efficiency water reducer; the cementing material is cement, fly ash, slag powder, etc., the cementing material The weight percentage is:

[0068] Cement: 20% Fly Ash: 60%

[0069] Slag powder: 20%;

[0070] The foaming agent is an existing foaming agent.

[0071] A kind of preparation method of high water storage foam concrete for sidewalk, the concrete steps of described method are as follows:

[0072] (1) material preparation

[0073] Prepare materials according to the components and weight percentages of the high water storage concrete for sidewalks in Examp...

Embodiment 3

[0086] A kind of component and weight percent thereof of high water storage concrete for sidewalk are:

[0087] Cementitious material: 20% Porous aggregate: 75.545%

[0088] Water: 4% Water reducer: 0.1%

[0089] Redispersible latex powder: 0.3% Foaming agent: 0.005%

[0090] Among them: the porous aggregate is ceramsite aggregate with a particle size of 0.9mm to 35mm; the water reducing agent is melamine high-efficiency water reducing agent; the cementing material is cement, fly ash, slag powder, etc., the cementing material is The weight percentage is:

[0091] Cement: 30% Fly Ash: 40%

[0092] Slag powder: 30%;

[0093] The foaming agent is an existing foaming agent.

[0094] A kind of preparation method of high water storage foam concrete for sidewalk, the concrete steps of described method are as follows:

[0095] (1) material preparation

[0096] Prepare materials according to the components and weight percentages of the high water storage concrete for sidewalks i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Water retentionaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to view more

Abstract

High water concrete for sidewalks and a preparation method thereof belong to the technical field of special concretes. The concrete is composed of a gelatinization material, porous aggregate, water, a water reducer, redispersable emulsion powder and a foaming agent. The method includes breaking and grading the porous aggregate, conducting pre-wetting treatment on the broken aggregate, adding the gelatinization material, the water reducer, the redispersable emulsion powder and the water into the aggregate, evenly mixing the mixture, then adding foam into the mixture, stirring evenly and pouring the mixture on the sidewalks on site to prepare the high water concrete for sidewalks. The invention is simple in device and convenient to construct on site. The concrete prepared in the method has the advantages of being low in cost, good in water storage performance, water permeability and air permeability, capable of reducing water discharge of an urban drainage system and the like and has the function of natural plants. Use of the concrete is one of the effective measures to alleviate the contradiction between quick development and environment protection in urbanization construction. The high water concrete can be widely used on the surface of sidewalks or roofs.

Description

technical field [0001] The invention belongs to the technical field of special concrete, in particular to special concrete for sidewalks and a preparation method thereof. Background technique [0002] With the rapid development of urbanization in our country, the problem that the urban surface of our country is covered by reinforced concrete houses and impermeable concrete pavement is increasing, and the damage to the environment is becoming more and more serious. How to properly handle the relationship between my country's urbanization and environmental damage is one of the most important issues that our government, cadres and the masses are extremely concerned about. In addition, because my country's urban construction does not separate the rainwater and sewage discharge systems, the rainwater and sewage are discharged together, resulting in a large increase in the amount of urban sewage during the rainy season, and a large increase in sewage treatment costs. Therefore, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B38/00
Inventor 俞心刚龚毅黄海珂林琳
Owner 重庆北足泡沫混凝土技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap