Cuprous sulfide film with preferred orientation growth

A copper sulfide, preferred orientation technology, applied in photovoltaic power generation, sustainable manufacturing/processing, electrical components and other directions, can solve the problems of not preparing copper sulfide thin film, difficult to obtain, etc., achieving low production cost, high production efficiency, The effect of low equipment requirements

Inactive Publication Date: 2012-10-03
SHANDONG JIANZHU UNIV
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the obtained film material in this patent application will be different from the powder material in the formation and crystal growth process and mechanism, and it is difficult for the powder mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cuprous sulfide film with preferred orientation growth
  • Cuprous sulfide film with preferred orientation growth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] a. Cleaning of the glass substrate: The glass substrate (size 2mm×2mm) was cleaned as described above.

[0034] b. 5.316 parts of CuCl 2 2H 2 Put O into a glass bottle, add 75.614 parts of ethanolamine, 113.421 parts of deionized water, add ammonia water until the pH is 8.0, and use ultrasonic vibration for more than 30 minutes to mix the substances in the solution evenly.

[0035] c. Drop the above solution onto the glass substrate placed on the homogenizer, and then start the homogenizer. The homogenizer rotates at 200 rpm for 5 seconds and at 3000 rpm for 15 seconds, so that the dripped solution is coated After uniformity, the substrate was dried at 100°C, and then the above-mentioned solution was dripped and spin-coated again, and then dried again. This was repeated 10 times, and a precursor thin film sample with a certain thickness was obtained on the glass substrate.

[0036] d. Put the precursor film sample obtained by the above process into an airtight contain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a cuprous sulfide film with preferred orientation growth and belongs to the technical field of semiconductor films. The cuprous sulfide film is obtained through the following steps of firstly cleaning a glass substrate; then putting CuCl2.2H2O into a solvent, spincoating the mixture on the glass substrate to obtain a precursor film, drying the precursor film, putting the dried precursor film into a sealable container containing sulfur powder and hydrazine hydrate and ensuring that the precursor film sample is not contacted with the hydrazine hydrate and the sulfur powder; and finally drying the precursor film. The obtained cuprous sulfide film is subjected to crystal growth along a preferred orientation [111] and is better in continuity and uniformity.

Description

technical field [0001] The invention belongs to the technical field of semiconductor thin films, in particular to a copper disulfide thin film with preferred orientation growth. Background technique [0002] With the development of society and economy, my country's total energy consumption has increased sharply, and energy shortages and pollution caused by energy consumption have become prominent problems in domestic social development. Harmonious society is of great significance. In order to make full use of solar energy, which is a clean, safe and environmentally friendly renewable resource, the research and development of photovoltaic materials for solar cells has been paid more and more attention in recent years. [0003] Transition metal sulfides are widely used due to their good photoelectric properties, and copper sulfide is an important transition metal sulfide. The compounds composed of Cu and S have some special optoelectronic properties due to their variability i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01L31/0392H01L31/032H01L31/18
CPCY02E10/50Y02P70/50
Inventor 刘科高孙昌李静许斌石磊
Owner SHANDONG JIANZHU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap