Cleaning agent for stainless steel-aluminum alloy plate combined electric kettle and preparation method

A technology for aluminum alloy plates and electric kettles, which is applied in the field of bright cleaning agents and preparations for combined electric kettles made of stainless steel and aluminum alloy plates. It can solve the problems of poor oxidation resistance and discoloration by oxidation of electric kettles, and achieve polishing and oxidation resistance. Strong, strong emulsifying effect, high solvency effect

Inactive Publication Date: 2012-10-10
DALIAN SANDAAOKE CHEM
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] c. The overall surface of the electric kettle after cleaning has poor oxidation resistance, and it will be oxidized and discolored within one month

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Raw materials and mass percentages used are as follows:

[0026] Sodium hydroxide 0.1%

[0027] Sodium Carbonate 5%

[0028] Potassium metasilicate pentahydrate 1%

[0029] Potassium pyrophosphate 3%

[0030] Borax decahydrate 1%

[0031] Sodium tripolyphosphate 4%

[0032] Penetrant 0.1%

[0033] Special low foaming surfactant for spray degreasing 2%

[0034] Special surfactant for wax removal water 0.5%

[0035] Y-73 ultrasonic cleaning low foam surfactant 2%

[0036] Y-75 ultrasonic cleaning low foam surfactant 0.5%

[0037] Defoamer 3%

[0038] water balance.

[0039] The production method is carried out according to the following steps: first add the calculated and weighed water into the reaction kettle, start the agitator, and control the rotation speed to 60 rpm, and then se...

Embodiment 2

[0042] Raw materials and mass percentages used are as follows:

[0043] Sodium hydroxide 0.5%

[0044] Sodium carbonate 1%

[0045] Potassium metasilicate pentahydrate 4%

[0046] Potassium pyrophosphate 1%

[0047] Borax decahydrate 3%

[0048] Sodium tripolyphosphate 1%

[0049] Penetrant 1.8%

[0050] Special low foam surfactant for spray degreasing 0.5%

[0051] Special surfactant for wax removal water 3%

[0052] Y-73 ultrasonic cleaning low foam surfactant 0.5%

[0053] Y-75 ultrasonic cleaning low foam surfactant 3%

[0054] Defoamer 1%

[0055] water balance.

[0056] Raw material source and production method are with embodiment 1.

Embodiment 3

[0058] Raw materials and mass percentages used are as follows:

[0059] Sodium hydroxide 0.25%

[0060] Sodium Carbonate 2.5%

[0061] Potassium metasilicate pentahydrate 3%

[0062] Potassium pyrophosphate 2%

[0063] Borax decahydrate 2%

[0064] Sodium tripolyphosphate 3%

[0065] Penetrant 1%

[0066] Special low foaming surfactant for spray degreasing 1.2%

[0067] Special surfactant for wax removal water 2%

[0068] Y-73 ultrasonic cleaning low foam surfactant 1.2%

[0069] Y-75 ultrasonic cleaning low foam surfactant 2%

[0070] Defoamer 2%

[0071] water balance.

[0072] Raw material source and production method are with embodiment 1.

[0073] When cleaning, the embodiment 1, embodiment 2 or embodiment 3 of the present invention is applied to the existing automatic cleaning line...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bright cleaning agent for a stainless steel-aluminum alloy plate combined electric kettle, which is generally used for spraying and ultrasonic washing, and can simultaneously remove oil, wax and other pollutants on the surface of stainless steel and aluminum alloy of the electric kettle to achieve strong polishing and oxidation resistance and other effects, and a preparation method. The bright cleaning agent is prepared from the following raw materials in percentage by weight: 0.1-0.5% of sodium hydroxide, 1-5% of sodium carbonate, 1-4% of potassium metasilicate pentahydrate, 1-3% of potassium pyrophosphate, 1-3% of borax decahydrate, 1-4% of sodium tripolyphosphate, 0.1-1.8% of penetrant, 0.5-2% of special low-foaming surfactant for spray degreasing, 0.5-3% of special surfactant for removing molten wax, 0.5-2% of Y-73 low-foaming surfactant for ultrasonic washing, 0.5-3% of Y-75 low-foaming surfactant for ultrasonic washing, 1-3% of defoaming agent and the balance of water.

Description

technical field [0001] The invention relates to a bright cleaning agent for a stainless steel and aluminum alloy plate combination electric kettle and a preparation method thereof, especially a bright cleaning agent which can be used for spraying and ultrasonic cleaning, and simultaneously removes oil, wax and other dirt on the surface of the stainless steel and aluminum alloy of the electric kettle Disclosed is a bright cleaning agent for a combined electric kettle with stainless steel and aluminum alloy plates that achieves the effects of polishing and strong oxidation resistance, and a preparation method thereof. Background technique [0002] At present, most electric kettles are made of a combination of two metal materials, that is, first stamped with 1Cr18Ni9Ti stainless steel, and then riveted and combined with a hard aluminum alloy plate to the bottom of the stainless steel pot. After the electric kettle is mechanically polished, there is polishing paste left on the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/19C23G1/22C23F3/02C23F3/04
Inventor 潘德顺张礼让黄文飞邱延胜史然峰李振忠
Owner DALIAN SANDAAOKE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap