Method for producing overturning plate valve cover by resin sand

A technology of resin sand and flap valve, which is applied in the direction of coating, casting molding equipment, casting mold, etc.

Inactive Publication Date: 2012-11-14
SHANXI YUQING ENVIRONMENTAL PROTECTION
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]The flap valve cover is the flue outlet part of the coke oven smoke exhaust and dust removal equipment. The existing flap valve cover is generally made of ductile iron castings made of QT500-7. The wall thickness of the casting is 8 mm. In the actual production process, because the casting is a large plane and thin wall, it is not only difficult to cast, but also casting defects such as cold shut and warping deformation account for a large proportion during casting, and there is carburization in the casting. Body structure, affecting the quality of castings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] (1) The mold is made of aluminum alloy material. The mold is an integral structure. The sand box is integrally cast with ductile iron. There are sprue, runner and inner runner for pouring; there are positioning holes on the sand box, and positioning pins are used between the sand boxes; the sand box is matched with the mold.

[0024] (2) Preparation of resin sand: resin sand uses raw sand as aggregate, furan resin as binder, and curing agent as hardening catalyst.

[0025] The proportioning of resin sand according to mass unit parts is: 100 parts of raw sand, 4-5 parts of spodumene, 4-5 parts of ilmenite, 1.0-2.0 parts of furan resin, 0.4-1.0 parts of curing agent; resin sand The total ignition loss is below 4%, and the nitrogen content is less than 0.1%.

[0026] The original sand is made of high-quality natural quartz sand. The actual use proves that adding 4% spodumene and 4% ilmenite to the total mass of the original sand can achieve the chilling effect. Mix the o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for producing an overturning plate valve cover by resin sand, aiming at effectively reducing the cementite tissue in a casting piece, and improving the yield. The method comprises the following steps of: firstly manufacturing a mould and a sand box, wherein the mould is of an integrated structure, and the sand box is wholly cast by nodular iron; evenly mixing raw sand and curing agent, and adding furan resin in proportion, and evenly mixing; filling the resin sand into the sand box till the sand box is filled and struck off, and putting on a plain jolter to be mechanically rammed; preparing coating material, and coating the coating material on the surface of formed resin sand, wherein the coating method adopts a pouring and coating method; after the coating material is dried, baking the surface of the resin sand coated with the coating material by a blast burner; hoisting the sand box to a pouring platform for mould assembling; adding raw materials into an intermediate frequency furnace to be smelted according to the normal nodular iron proportion, and balling according to a normal method; transporting the balled molten iron to the pouring platform, pouring under the temperature condition of 1450 DEG C, releasing a box clamp after pouring for 1 hour, and keeping the temperature for 2 hours; falling the sand after cooling to be less than 200 DEG C; and cleaning the casting piece.

Description

technical field [0001] The invention relates to a method for producing a flap valve cover by using resin sand. Background technique [0002] The flap valve cover is the flue outlet part of the coke oven smoke exhaust and dust removal equipment. The existing flap valve cover is generally made of ductile iron castings made of QT500-7, and the thickness of the casting is 8mm. In the actual production process, the casting is Large plane and thin wall parts are not only difficult to cast, but also have a large proportion of casting defects such as cold shut and warping deformation during casting. There is cementite structure in the casting, which affects the quality of the casting. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the above-mentioned prior art, and provide a method for producing a flap valve cover by using resin sand that can effectively reduce the cementite structure in the casting and improve the yield...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/22B22C3/00B22C9/22
Inventor 薛忠
Owner SHANXI YUQING ENVIRONMENTAL PROTECTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products