Preparation method of wood-organic-inorganic hybridized nano composite material based on doped nano POSS (Polyhedral Oligomeric Silsesquioxane)

A nano-composite material and wood technology, which is applied in the direction of impregnated wood, wood impregnation, wood processing equipment, etc., can solve the problems of low impact toughness, poor mechanical properties of wood-inorganic (nano) composite materials, poor thermal stability, etc.

Active Publication Date: 2012-11-14
SHANDONG AGRICULTURAL UNIVERSITY
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the technical problems of poor thermal stability, low impact toughness and poor mechanical properties of wood-inorganic (nano) composite materials in wood-organic polymer composites, the present invention provides a wood-organic-inorganic hybrid based on nano-POSS doping. chemical nanocomposites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of wood-organic-inorganic hybridized nano composite material based on doped nano POSS (Polyhedral Oligomeric Silsesquioxane)
  • Preparation method of wood-organic-inorganic hybridized nano composite material based on doped nano POSS (Polyhedral Oligomeric Silsesquioxane)
  • Preparation method of wood-organic-inorganic hybridized nano composite material based on doped nano POSS (Polyhedral Oligomeric Silsesquioxane)

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0033] Specific embodiment one: the preparation method of the wood-organic-inorganic hybrid nanocomposite material based on nano POSS doping in this embodiment is carried out according to the following steps:

[0034] 1. Weigh 1 mass part of the functional monomer and the toughening agent and mix them uniformly, the mass of the toughening agent is 1% to 150% of the mass of the functional monomer to obtain a monomer solution;

[0035]2. Weigh 0.1% to 10% POSS (with organic amine functional groups) of the monomer solution mass obtained in step 1, then dry the POSS for 24 hours at 105°C and 0.01MPa under vacuum drying conditions, and then dehydrate the POSS with tetrahydrofuran The dried POSS is dissolved to obtain a POSS tetrahydrofuran solution with a POSS mass concentration of 1% to 20%, and the POSS tetrahydrofuran solution is added to the monomer solution in step 1, and stirred evenly to obtain a transparent monomer solution in which nano-POSS is dissolved;

[0036] Three, t...

specific Embodiment approach 2

[0049] Embodiment 2: This embodiment differs from Embodiment 1 in that the mass of the toughening agent in step 1 is 50% of the mass of the functional monomer. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0050] Embodiment 3: The difference between this embodiment and Embodiment 1 is that in Step 2, 5% POSS by weight of the monomer solution obtained in Step 1 is weighed. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a wood-organic-inorganic hybridized nano composite material based on doped nano POSS (Polyhedral Oligomeric Silsesquioxane), which relates to a preparation method of a composite wood material. The preparation method disclosed by the invention solves the technical problems that the heat stability and the impact toughness of a wood-organic-polymer composite material is poor and low, and the mechanical property of a wood-inorganic (nano) composite material is poor. The preparation method disclosed by the invention comprises the following steps of: firstly, dissolving nano POOS (containing an organic amine function group) into a monomer solution and compounding an initiator and a cross-linking agent with the monomer solution to form an impregnation solution; after wood is placed into the impregnation solution and then is placed into a reaction tank, sealing and vacuumizing the reaction tank, removing vacuum of the reaction tank, and pressurizing the reaction tank by air; reducing the pressure of the reaction tank to normal pressure, taking out the wood, and covering the impregnated wood by aluminum-foil paper; and heating the wood, removing the aluminum-foil and continuously heating the wood, thus obtaining the wood-organic-inorganic hybridized nano composite material. The compatibility between a wood substrate interface and a polymer of the wood-organic-inorganic hybridized nano composite material is good, and the wood-organic-inorganic hybridized nano composite material has the advantages of good mechanical strength, heat stability, dimension stability, and corrosion resistance.

Description

technical field [0001] The invention relates to a method for preparing wood composite materials. Background technique [0002] Most of the wood-organic polymer composites prepared based on monomer impregnation and polymerization have good mechanical properties and durability (corrosion resistance and dimensional stability), and retain the ecological environment material characteristics of wood. There is a market demand in the field of materials and decorative materials for special places, and it is of great significance to the efficient utilization of wood, especially low-quality wood; but most of these materials have low thermal stability due to the poor heat resistance of polymers (such as The maximum pyrolysis temperature is a measure), even lower than the wood itself, and the impact toughness of this type of material is significantly reduced due to the brittle characteristics of the polymer, which limits the widening application of this type of material. [0003] The im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K3/08B27K3/50
Inventor 李永峰董晓英路则光
Owner SHANDONG AGRICULTURAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com