A 304 stainless steel, production method technology, applied in the direction of metal rolling, manufacturing tools, metal processing equipment, etc., can solve the problems of high production efficiency, low cost, easy to rust on the end face, etc., achieve simple manufacturing process, low production cost, Strong corrosion resistance effect

Active Publication Date: 2012-11-28
无锡银荣板业有限公司
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies in the traditional composite technology, thereby providing a production method of 304 stainless steel and pure copper cold composite coil, which has high production ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment one: a kind of production method of 304 stainless steel and pure copper cold composite coil of the present invention adopts the following process steps:

[0025] The raw material substrate is 304 cold-rolled stainless steel coil with a width of 620mm and a thickness of 2.0mm; T2 pure copper coil with a width of 620mm and a thickness of 0.2mm; 304 cold-rolled stainless steel The weight of the copper coil is 500Kg; the degreasing time is subject to the bright and oil-free surface of the strip;

[0026] 1. Take 304 cold-rolled stainless steel coils and T2 pure copper coils and put them on the cleaning and degreasing unit for chemical degreasing treatment. Put 1000 kg of water and 120 kg of degreasing agent into the solution tank. The degreasing solution is made of For NaOH solution with a mass concentration of 12%, the temperature is controlled at 70°C; the degreasing time is subject to the bright and oil-free surface of the strip; the degreasing time is: 80 m / m...

Embodiment 2

[0033] Embodiment two: a kind of production method of 304 stainless steel and pure copper cold composite coil of the present invention adopts the following process steps,

[0034] The substrate is made of 304 cold-rolled stainless steel coil with a width of 580mm and a thickness of 2.0mm; the composite layer is made of T2 pure copper coil with a width of 580mm and a thickness of 0.2mm; the weight of the stainless steel coil is 5000Kg, and the weight of a single-layer copper coil 500Kg;

[0035] 1. Take 304 cold-rolled stainless steel coils and T2 pure copper coils and put them on the cleaning and degreasing unit for chemical degreasing treatment. Put 1000 kg of water and 150 kg of degreasing agent into the solution tank. The degreasing solution is made of NaOH solution with a mass concentration of 15%, the temperature is controlled at 80°C; the degreasing time is subject to the bright surface of the strip and no oil stain; the degreasing time is: 80 m / min; the drying temperatu...

Embodiment 3

[0042] Embodiment three: a kind of production method of 304 stainless steel and copper cold composite coil of the present invention adopts following processing steps:

[0043] The substrate is made of 304 cold-rolled stainless steel coil with a width of 550mm and a thickness of 2.0mm; the composite layer is made of T2 pure copper coil with a width of 550mm and a thickness of 0.2mm; the weight of the stainless steel coil is 5000Kg, and the weight of a single-layer copper coil 500Kg;

[0044] 1. Take 304 cold-rolled stainless steel coils and T2 pure copper coils and place them on the cleaning and degreasing unit for chemical degreasing treatment. Put 1000 kg of water and 180 kg of degreasing agent into the solution tank. The NaOH solution with a mass concentration of 18% is used, and the temperature is controlled at 70°C; the degreasing time is subject to the bright surface of the strip and no oil stain; the degreasing time is 10 seconds; the drying temperature is 90°C;

[0045...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production method of a 304 stainless steel and a pure-copper cold compound coiled material. The production method comprises the following process steps of: (1) preparing raw materials: carrying out surface oil-removing and decontaminating treatment on 304 coldly-rolling stainless steel and a pure-copper coiled material; (2) carrying out compound rolling: conveying the 304 coldly-rolling stainless steel and a copper metal material into a compound rolling machine to carry out synchronous room-temperature continuous compound rolling; (3) dispreading and annealing: carrying out the dispreading and annealing on a rolled stainless steel copper compound coiled material on an alloy layer; (4) flattening the stainless steel copper compound coiled material which is dispread and annealed; (5) carrying out bending and strengthening treatment on the flattened stainless steel copper compound coiled material; and (6) carrying out cutlengthing and splitting on the stainless steel copper compound coiled material to form a 304 stainless steel and copper cold compound material. The production method disclosed by the invention has a simple manufacturing process and low production cost; and the corrosion resistance of the steel-copper compound coiled material is strong and no rusts are formed on the end surfaced of the steel-copper compound coiled material, so that the requirements of a plurality of indoor and outdoor decorative materials are met.

Description

technical field [0001] The invention relates to a production method of 304 stainless steel and pure copper cold composite coil, belonging to the technical field of stainless steel and copper composite materials. Background technique [0002] 304 stainless steel is a common general-purpose stainless steel, also known as 18 / 8 stainless steel in the industry, with excellent stainless corrosion resistance and better resistance to intergranular corrosion. Rust resistance is stronger than 200 series stainless steel materials. It is also better in high temperature resistance, and the general use temperature limit is less than 650°C. The corrosion resistance is better than 430 stainless steel, but the price is cheaper than 316 stainless steel. It is suitable for daily life and is a nationally recognized food-grade stainless steel. It is suitable for food processing, storage and transportation; it has good processing performance and weldability , Suitable for plate heat exchangers,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B1/38B21B15/00C21D8/02
Inventor 谢举霞刘岗周洪岳邓炳如
Owner 无锡银荣板业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap