Ironmaking and aluminum extraction comprehensive utilization method of high-iron red mud

A high-iron red mud and red mud technology, applied in the field of metallurgy, can solve the problems of unfeasible economy, low recovery rate, and inability to realize large-scale industrial application, so as to reduce the emission of NOx and greenhouse gas CO2, and solve the problem of blast furnace slag Adhesive, beneficial effect of separation and trapping

Active Publication Date: 2012-12-12
NORTHEASTERN UNIV
View PDF10 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] To sum up, the currently implemented methods for recovering valuable elements such as aluminum, iron, and sodium from red mud all have problems such as high energy consumpti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0039] This example is basically the same as Example 1, except that the processing method of high-iron red mud minerals in Step 1 is as follows: the mixed red mud and other iron-containing materials are pelletized with an improved cylinder pelletizer or disc pelletizer. The ball machine produces small balls with a diameter of 3-8 mm, then rolls fuel and CaO powder on the surface of the small balls, distributes them on the sintering trolley, ignites and sinters, and sinters into molten and bonded grape-shaped qualified sintered ore; the charge in step 2 The temperature range is 1000°C, the total iron content of iron-containing materials is 45wt%, the lower tuyeres of the blast furnace are blasted with an oxygen enrichment rate of 60%, the hot air temperature is 1000°C, and the furnace body is injected with 900°C coke oven gas of 100Nm 3 / t; In step 3, in the aluminum recovery process, the amount of lime added must ensure that the alkalinity of the slag is CaO / SiO 2 =2.04, CaO / A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides an ironmaking and aluminum extraction comprehensive utilization method of high-iron red mud. The method is characterized in that a blast furnace is used as main equipment; red mud is utilized to prepare micropellet composite sinter or pellet; micropellet composite sinter or pellet and coke are then treated with hot charging into the furnace layer by layer at no less than 400 DEG C; rich oxygen to full oxygen blast is employed; and tuyeres on the furnace body are increased, and reducing gas rich in hydrogen is blown into the furnace, so as to realize red mud ironmaking. At the same, calcium oxide is added during a deslagging process; the slag is treated with temperature control cooling to obtain self-pulverization calcium aluminate slag, which is leached and extracted with alumina; and sodium element is synchronously recovered from high temperature exhaust of the furnace top, so as to complete efficient separation and recycling of aluminum, iron and sodium in the red mud.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, and relates to a comprehensive utilization method for ironmaking and aluminum extraction from high-iron red mud, in particular to a method for recovering iron, aluminum, sodium and other valuable metal elements from high-iron red mud. Background technique [0002] High-iron red mud is a kind of Fe produced in the process of extracting alumina from bauxite 2 o 3 Solid waste with a content exceeding 30% by weight. Enterprises in China's alumina industry will produce 1.0-1.8 tons of red mud for every 1 ton of alumina produced on average. Today, China's red mud stockpile has reached more than 200 million tons, and it is expected to reach 300 million tons by 2015. The storage of red mud not only needs to maintain its slope stability, but also occupies land, pollutes the environment, and poses serious safety hazards. [0003] Theoretically speaking, high-iron red mud is a very valuable resource f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B5/00C21B5/06C22B1/14C22B7/04C22B21/00
CPCY02P10/143Y02P10/20Y02P10/25
Inventor 李强张伟邹宗树
Owner NORTHEASTERN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap