Water-based epoxy enamel paint

A water-based epoxy and enamel technology, applied in the field of coatings, can solve the problems of low corrosion resistance and salt resistance, complex procedures and high cost, and achieve the effect of improving anti-corrosion performance

Active Publication Date: 2012-12-19
重庆南方漆业有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, my country's current research on water-based epoxy paint is in the initial stage of exploration, and there are still low corrosion resistance and salt resistance, complicated procedures and high costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based epoxy enamel paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A. Preparation of water-based epoxy enamel (first):

[0031] (1), the material Huntsman (3985) 170Kg, deionized water 250Kg, medium chrome yellow 20Kg, titanium dioxide (298) 10Kg, precipitated barium sulfate 300Kg, Efka (EFKA4560) 1Kg, air chemical industry (420) 1Kg, air chemical (DF62) 1Kg, silica Grace (E30) 1Kg, tartrazine 250Kg are added to the mixing tank in turn and stirred evenly;

[0032] (2), the solution obtained in step (1) is ground by a sand mill until the fineness is within 40 microns, and then the solution is put back into the mixing tank;

[0033] (3), the solution obtained in step (2) is toned, filtered, and packed in equal amounts;

[0034] B, the preparation of water-based epoxy enamel (second):

[0035] (1), 400Kg of material E-51 epoxy resin, 10Kg of 601 epoxy resin, 20Kg of ethylene glycol butyl ether, 20Kg of Kanglilai chemical industry (PEF108), 10Kg of Kanglilai chemical industry (FORM-100) are added to the reactor, and the temperature is ra...

Embodiment 2

[0040] A. Preparation of water-based epoxy enamel (first):

[0041] (1), the material air chemical industry (RH900) 200Kg, deionized water 350Kg, medium chrome yellow 50Kg, titanium dioxide (298) 50Kg, precipitated barium sulfate 400Kg, Efka (EFKA4560) 5Kg, air chemical industry (420) 5Kg, Air chemical industry (DF62) 5Kg, silica Grace (E30) 5Kg, tartrazine 300Kg are added to the mixing tank in turn and stirred evenly;

[0042] (2), the solution obtained in step (1) is ground by a sand mill until the fineness is within 40 microns, and then the solution is put back into the mixing tank;

[0043] (3), the solution obtained in step (2) is toned, filtered, and packed in equal amounts;

[0044] B, the preparation of water-based epoxy enamel (second):

[0045] (1), material E-51 epoxy resin 500Kg, 601 epoxy resin 60Kg, ethylene glycol butyl ether 50Kg, Kanglilai chemical industry (PEF108) 50Kg, Kanglilai chemical industry (FORM-100) 50Kg are added to the reactor, and the temperatu...

Embodiment 3

[0050] A. Preparation of water-based epoxy enamel (first):

[0051] (1), the material Huntsman (3985) 185Kg, deionized water 300Kg, medium chrome yellow 35Kg, titanium dioxide (298) 30Kg, precipitated barium sulfate 350Kg, Efka (EFKA4560) 3Kg, air chemical industry (420) 3Kg , Air Chemical Industry (DF62) 3Kg, Silica Grace (E30) 3Kg, Lemon Yellow 3Kg are added to the mixing tank in turn and stirred evenly;

[0052] (2), the solution obtained in step (1) is ground by a sand mill until the fineness is within 40 microns, and then the solution is put back into the mixing tank;

[0053] (3), the solution obtained in step (2) is toned, filtered, and packed in equal amounts;

[0054] B, the preparation of water-based epoxy enamel (second):

[0055] (1), material E-51 epoxy resin 450Kg, 601 epoxy resin 35Kg, ethylene glycol butyl ether 35Kg, Kanglilai chemical industry (PEF108) 35Kg, Kanglilai chemical industry (FORM-100) 30Kg are added to the reactor, and the temperature is raised ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based epoxy enamel paint being a two-component coating which is prepared by epoxy resin emulsion, curing agents, tinting pigments, auxiliaries and so on. The water-based epoxy enamel paint has tough paint films and the advantages of excellent adhesion, flexibility, abrasive resistance and shock resistance and good chemical resistance, solvent resistance, water resistance, salt water resistance, durability and corrosion resistance. The water-based epoxy enamel paint is widely applied to the surface rust protection of ships, steel structures, wharf steel facilities and so on.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a water-based epoxy enamel. Background technique [0002] As an important coating, epoxy paint is widely used in the coating anti-corrosion process due to its good anti-corrosion performance. Can be used as primer and intermediate coat for metal products. [0003] With the increasing demand for water-based epoxy coatings, especially the gradual increase in the quality requirements for epoxy topcoats, most of the epoxy anti-rust paints in the market are solvent-based coatings. During the curing process of the coating film, there is a large amount of solvent Volatility does not conform to the sustainable development policy of "low-carbon environmental protection, energy saving and emission reduction" formulated by the state. The new water-based epoxy topcoat has attracted people's attention and attention. However, my country's current research on water-based epoxy paint is in the initial ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D5/08
Inventor 穆建渝
Owner 重庆南方漆业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com