Inflaming retarding system and preparation method of inflaming-retarding real silk

A system and real silk technology, applied in the direction of textiles, papermaking, fiber treatment, etc., can solve the problems of large smoke generation and large addition, and achieve the effects of no formaldehyde release, promotion of char formation, and reduction of visibility

Active Publication Date: 2012-12-19
苏州盛泽科技创业园发展有限公司
View PDF10 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Chinese invention patent application CN1958936A discloses a method of grafting real silk with vinyl phosphate for flame retardant finishing. This modification can obtain good flame retardant performance on the basis of ensuring the orig

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inflaming retarding system and preparation method of inflaming-retarding real silk
  • Inflaming retarding system and preparation method of inflaming-retarding real silk
  • Inflaming retarding system and preparation method of inflaming-retarding real silk

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Example 1: Flame-retardant finishing and performance testing of real silk fabrics

[0039] The formula of flame retardant working fluid is as follows:

[0040] components Dosage Methacryloxyethyl Dimethyl Phosphate 5 g A 151 (silicon component) 5 g ammonia Appropriate amount, adjust the pH value of the finishing solution to 4.5 potassium persulfate 0.2 g water 300 g

[0041] Wherein, the trade name of the silicon component is A151, and its main chemical component is vinyltriethoxysilane.

[0042] Silk fabric is 10g silk power spinning (36g / m 2 ).

[0043] First add the silicon component into water, ultrasonically disperse for 60 minutes, then add methacryloyloxyethyl dimethyl phosphate under stirring, adjust the pH of the finishing solution to 4.5 with ammonia water, add potassium persulfate, and make the silk fabric Immerse in the working fluid, seal it, place it in a vibrating water bath, raise the temperature, control...

Embodiment 2

[0053] Example 2: Flame-retardant finishing and performance testing of real silk fibers

[0054] The formula of flame retardant working fluid is as follows:

[0055] components Proportion Methacryloxyethyl Dimethyl Phosphate 2.5 g A 171 2.0 g ammonia Appropriate amount, adjust the pH value of the finishing solution to 4.5 Ammonium persulfate 0.11 g water 200g

[0056] Wherein, the trade name of the silicon component is A171, and its main chemical component is vinyltrimethoxysilane.

[0057] The silk fiber sample is 5g degummed silk fiber (21 / 22 denier, degumming rate 23%).

[0058] First add the silicon component into water, ultrasonically disperse for 30 minutes, then add methacryloyloxyethyl dimethyl phosphate under stirring, adjust the pH of the finishing solution with ammonia water to 4.3, add ammonium persulfate, and the silk fiber Immerse in the working solution, seal it, place it in a vibrating water bath, raise the temper...

Embodiment 3

[0062] Example 3: Preparation of flame-retardant silk fabric by steaming method

[0063] The formula of flame retardant working fluid is as follows:

[0064] components Proportion Methacryloxyethyl Dimethyl Phosphate 7.5 g A 171 7.5 g ammonia Appropriate amount, adjust the pH value of the finishing solution to 4.5 potassium persulfate 0.33 g water 150g

[0065] Wherein, the trade name of the silicon component is A171, and its main chemical component is vinyltrimethoxysilane.

[0066] Silk fabric is 8g silk power spinning (36g / m 2 ).

[0067] Immerse the above-mentioned silk fabric in the prepared flame-retardant working solution, dipping and rolling twice, the soaking time is 1min, the liquid rolling rate is 95%, and then dried at 40°C for 3min, placed in saturated steam for 10min, taken out, cold running water Wash, then wash with 50°C water, then wash with cold running water, and then dry at 70°C. The limiting oxygen index of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an inflaming retarding system and a preparation method of an inflaming-retarding real silk. The inflaming retarding system is a phosphorus-silicon collaborative system, wherein a phosphorus component is methacryloyloxyethyl dimethyl phosphate and a silicon component is a vinyl silane coupling agent. The preparation method comprises the following steps of: preparing an inflaming-retarding working solution and adjusting the pH (Potential of Hydrogen) value of the working solution to 4-4.5; immersing a real silk textile into the inflaming-retarding working solution, and heating the real silk textile at 80-85 DEG C for 10-60 minutes; and washing the real silk textile by water and drying the real silk textile to obtain the inflaming-retarding real silk. A fire retardant provided by the invention is durable, and no formaldehyde is released in an inflaming retarding and sorting process; and the smoke amount of the real silk textile in a combustion process is as low as required.

Description

technical field [0001] The invention belongs to the technical field of textile finishing, and in particular relates to a method for low-smoke and flame-retardant finishing of textiles, especially silk. Background technique [0002] Fires caused by textiles account for approximately 20 percent of residential fires, but account for 50 percent of all fire deaths. The cause of death is mostly due to the high concentration of smoke generated by the burning of materials in the fire, which affects visibility and causes suffocation. Therefore, legislation in various countries puts forward corresponding flame-retardant performance requirements for textiles used in different fields, and while using flame-retardant materials, reducing the amount of smoke generated when the materials are burned is particularly important to reduce the fire fatality rate. [0003] Silk fiber, known as the "Fiber Queen", is widely used in clothing and decorative materials due to its health care, comfort, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M14/06
Inventor 关晋平陈国强朱云朋
Owner 苏州盛泽科技创业园发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap