Mg-Li porcelain and its production method
A lithium-magnesium porcelain and enamel technology, applied in the field of daily-use ceramics, can solve the problems of poor molding, easy to fry porcelain, poor firing performance, etc., and achieve the effects of loose production conditions, light and thin shape, and good thermal stability.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] The lithium-magnesium ceramic bowl is composed of a green body and an enamel layer. The raw material weight percentage of the green body ingredients is: 76% talc, 13.5% kaolin, 7% feldspar, 2% spodumene, 2% additives, The plastic adhesive is 0.5%; the raw material weight percent of the enamel layer ingredients is composed of 46% feldspar, 25% quartz, 14% talc, 10% kaolin, 2.5% zinc oxide and 2.5% additives. Make the green body and enamel separately, measure the moisture content of the raw materials when making the green body, and then weigh various raw materials according to the weight percentage of the raw materials used in the green body ingredients, put the raw materials in a ball mill, mix and ball mill for 25-30 hours to the desired Fineness, put it into the pulp tank and stir evenly, then sieve, remove iron, squeeze mud, rough smelt, stale, scouring, roll forming, drying, trimming, and make the green body; according to the ingredients used in the enamel layer Raw ...
Embodiment 2
[0015] The lithium-magnesium ceramic bowl is composed of a green body and a glaze layer. The raw material weight percentage of the green body ingredients is: 70% talc, 17% kaolin, 10% feldspar, 1.3% spodumene, 1% additive, The plastic adhesive is 0.7%; the raw material weight percentage of the enamel layer ingredients is composed of 48% feldspar, 20% quartz, 13% talc, 12% kaolin, 3% zinc oxide and 4% additive. Make the green body and enamel separately, measure the moisture content of the raw materials when making the green body, and then weigh various raw materials according to the weight percentage of the raw materials used in the green body ingredients, put the raw materials in a ball mill, mix and ball mill for 25-30 hours to the desired Fineness, put it into the slurry tank and stir evenly, then sieve, remove iron, squeeze mud, rough smelt, stale, scouring, roll forming, drying, trimming to form a green body; raw materials used in ingredients according to the enamel layer ...
PUM
Property | Measurement | Unit |
---|---|---|
whiteness | aaaaa | aaaaa |
water absorption | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap