Composite electromagnetic shielding material and method for manufacturing same

A shielding material and composite electromagnetic technology, which is applied in the field of electromagnetic pollution prevention and microwave anechoic chambers, can solve the problems of difficult uniform dispersion, high cost and low output of carbon nanomaterials, and achieve the effects of easy dispersion, high production efficiency and large electrical loss.

Inactive Publication Date: 2013-02-06
SOUTHWEAT UNIV OF SCI & TECH
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are two serious problems in the practical application of carbon nanotubes or nanofibers. One is that carbon nanotubes or nanofibers are difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite electromagnetic shielding material and method for manufacturing same
  • Composite electromagnetic shielding material and method for manufacturing same
  • Composite electromagnetic shielding material and method for manufacturing same

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1:

[0038] A composite electromagnetic shielding material, composed of carbonized bacterial cellulose and paraffin wax as a base material;

[0039] The preparation method of the composite electromagnetic shielding material includes the following steps:

[0040] a. Bacterial cellulose is obtained by static shallow dish culture, same as the prior art;

[0041] b. Carbonized bacterial cellulose: the process parameters are: the carbonization temperature of bacterial cellulose is 800~1600 ℃, the background vacuum pressure is 10 -2 ~10 4 Pa, holding time is 0.5 h~4 h;

[0042] c. Take paraffin with the same volume as carbonized bacterial cellulose;

[0043] d. Mix the carbonized bacterial cellulose and paraffin at a volume ratio of 1:1, heat the mixture to 90 ℃ ~ 92 ℃, mechanically stir for 30 ~ 50 minutes, and then mix ultrasonically for 20 ~ 50 minutes in a water bath at 85 ℃ ~ 90 ℃ After cooling.

Example Embodiment

[0044] Example 2:

[0045] A composite electromagnetic shielding material, composed of carbonized bacterial cellulose and epoxy resin as a matrix material;

[0046] The preparation method of the composite electromagnetic shielding material includes the following steps:

[0047] a. Bacterial cellulose is obtained by static shallow dish culture, same as the prior art;

[0048] b. Carbonized bacterial cellulose: the process parameters are: the carbonization temperature of bacterial cellulose is 800~1600 ℃, the background vacuum pressure is 10 -2 ~10 4 Pa, holding time is 0.5 h~4 h;

[0049] c. Take epoxy resin equal in volume to carbonized bacterial cellulose;

[0050] d. Mix the carbonized bacterial cellulose and epoxy resin in a volume ratio of 1:1, mechanically stir the mixture for 30-50 minutes, and then leave it for 1 day to solidify naturally.

Example Embodiment

[0051] Example 3:

[0052] A carbonized bacterial cellulose electromagnetic shielding material, composed of a carbonized bacterial cellulose and a matrix material of silicon dioxide;

[0053] The preparation method of the carbonized bacterial cellulose electromagnetic shielding material includes the following steps:

[0054] a. Bacterial cellulose is obtained by static shallow dish culture, same as the prior art;

[0055] b. Carbonized bacterial cellulose: the process parameters are: the carbonization temperature of bacterial cellulose is 800~1600 ℃, the background vacuum pressure is 10 -2 ~10 4 Pa, holding time is 0.5 h~4 h;

[0056] c. Take the same volume of silicon dioxide as the carbonized bacterial cellulose;

[0057] d. Mix carbonized bacterial cellulose and silicon dioxide in a volume ratio of 1:1, mechanically stir the mixture for 60 minutes and then solidify.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite electromagnetic shielding material. The composite electromagnetic shielding material is characterized in that carbonized bacterial celluloses and a nanometer magnetic metal material are mixed to form the composite electromagnetic shielding material; or carbonized bacterial celluloses and a matrix material are mixed to form the composite electromagnetic shielding material; or carbonized bacterial celluloses and a nanometer magnetic metal material are mixed to form a mixture, and then the mixture and a matrix material are mixed to form the composite electromagnetic shielding material; the nanometer magnetic metal material is an optional one of Fe, Ni, Co, NiFe and CoFe; and the matrix material is an optional one of paraffin, epoxy resin and silicon dioxide. A method for manufacturing the composite electromagnetic shielding material includes steps of manufacturing bacterial celluloses; manufacturing the carbonized bacterial celluloses; and manufacturing the composite electromagnetic shielding material, and the like. The composite electromagnetic shielding material is thin, light, wide and strong, has the advantages of low cost, simplicity in manufacturing process, environmental protection and the like, and has wide application prospects in fields of electromagnetic pollution prevention, microwave dark chambers, high-frequency electronic products and the like.

Description

technical field [0001] The invention belongs to an electromagnetic shielding material and a preparation method thereof, and relates to a composite electromagnetic shielding material and a preparation method thereof. The composite electromagnetic shielding material of the invention is especially suitable for the fields of anti-electromagnetic pollution, microwave anechoic chamber and the like. Background technique [0002] With the development of science and technology, various high-frequency electromagnetic wave devices and instruments such as radars, satellites, microwave ovens, and mobile cordless phones are widely used, making the earth space full of electromagnetic waves of various frequency bands. These electromagnetic waves will affect other electromagnetic instruments. While causing interference, it also affects human health. According to reports, working in front of a computer for more than 6 hours a day will cause irreversible damage to human skin due to electromag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H05K9/00
Inventor 代波任勇王改花马拥军裴重华
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap