Production method of foamed concrete dry powder composite mortar

A technology of foamed concrete and composite mortar, which is applied in the field of building energy-saving and thermal insulation materials, and can solve problems such as poor thermal insulation effect, layered cracks, shelling, etc.

Inactive Publication Date: 2013-03-06
山东隆济时节能科技股份有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its main disadvantage is that in the process of pressurization and solidification, each air bubble in the brick will be strung together into a whole body cellular brick, which is easy to breathe and has poor thermal insulation effect.
In recent years, some people have used organic insulation boards such as EPS boards, XPS boards, and PU as interlayer insulation boards for the outer or inner layers of walls. Problems such as cracks, peeling and flammability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The present invention will be further described below.

[0009] The invention discloses a production method of foamed concrete dry powder composite mortar, which is suitable for the manufacture of foamed concrete dry powder composite mortar. The manufacturing method of foamed concrete dry powder composite mortar is described in detail as follows.

[0010] (1) Dry the fine tailings separately, and then sieve them into ore-forming powder between 100-400 mesh, and transport them to the three-dimensional tank for storage;

[0011] (2) Transport the fly ash to the three-dimensional tank for storage;

[0012] (3) Put the sulfoaluminate cement into a three-dimensional tank for storage;

[0013] (4) Transport quicklime powder over 200 mesh to a three-dimensional tank for storage;

[0014] (5) Transport the foaming agent to the three-dimensional tank for storage;

[0015] (6) Transport the light aggregate to the three-dimensional tank for storage;

[0016] (7) Send the abov...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of foamed concrete dry powder composite mortar. The foamed concrete dry powder composite mortar is prepared from fine tailing sand, sulfoaluminate cement, quicklime, fly ash, glass beads, a foaming agent and lightweight aggregate as raw materials. The production method is characterized in that quicklime and fly ash are used as binders and initiators; a surfactant is used as the foaming agent; and fine tailing sand, glass beads and sulfoaluminate cement are uniformly suspended in a material and the mixture is cured into the foamed concrete dry powder composite mortar in a short time. The foamed concrete dry powder composite mortar has low density, good thermal insulation performances and high affinity, is convenient for slurry coating and construction, is not delaminated, does not crack, has high strength, can be prepared by one step, and satisfies wall later decoration requirements.

Description

technical field [0001] The invention relates to a building energy-saving thermal insulation material, in particular to a production method of foamed concrete dry powder composite mortar. Background technique [0002] The source of building energy saving starts from the wall, therefore, there are air-entrained concrete foam blocks (air-entrained blocks) on the market. The main raw materials of this block are cement, sand, quicklime, gypsum, and aluminum powder. After mixing and grinding into a slurry, the mold is installed, and the foam is initially cured. First, it is cut into bricks of required specifications, and then pressurized by an autoclave. solidified. Its main technology is to use quicklime to exothermically foam, form gypsum, cut first, and heat-cure with gas. Its main disadvantage is that in the process of pressurization and curing, each air bubble in the brick will be strung together into a whole body cellular brick, which is easy to breathe and has poor therma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02C04B28/36
Inventor 孙娥
Owner 山东隆济时节能科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products