Glass frosting powder for processing anti-dazzle glass and preparation method thereof

An anti-glare glass and frosting powder technology, applied in the field of frosting powder, can solve the problems of increasing production cost, poor fluidity of anti-glare liquid, and being unsuitable for large-scale production.

Inactive Publication Date: 2013-04-10
LONGYAN HEDA MACHINERY
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The paste made from the above formula is simple to make, has a wide range of passing through the net, does not produce burrs, and is not affected by temperature and humidity. It is more suitable for making glass handicrafts quickly. Due to the large amount added, the fluidity of the anti-glare liquid is poor, and the surface of the anti-glare glass produced by the above-mentioned patent is relatively rough, not suitable for cleaning or polishing, which increases the production cost and is not suitable for large-scale production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Frosting powder for processing anti-glare glass is made by mixing the following raw materials according to the following weight ratio: ammonium bifluoride 44%, ammonium fluoride 10%, ammonium fluorosilicate 10%, potassium fluoroborate 10%, fluoride Calcium 3%, precipitated barium sulfate 3%, barium carbonate 3.5%, polyethylene glycol 5%, gum arabic 1.5%, starch 3%, organic acid 7%.

[0011] The preparation method of frosting powder for processing anti-glare glass, firstly mix ammonium bifluoride 44%, ammonium fluoride 10%, ammonium fluorosilicate 10%, potassium fluoroborate 10%, calcium fluoride 3%, precipitated barium sulfate 3% %, barium carbonate 3.5%, polyethylene glycol 5%, gum arabic 1.5%, starch 3%, and organic acid 7% were ground into fine powder respectively, and then the above fine powder was poured into a mixer and stirred until uniform.

Embodiment 2

[0013] The frosting powder used for processing anti-glare glass is made by mixing the following raw materials according to the following weight ratio: ammonium bifluoride 46%, ammonium fluoride 12%, ammonium fluorosilicate 8%, potassium fluoroborate 8%, fluoride Calcium 5%, Precipitated Barium Sulfate 5%, Barium Carbonate 5%, Polyethylene Glycol 3%, Gum Arabic 1%, Starch 2%, Organic Acid 5%.

[0014] The preparation method of frosting powder for processing anti-glare glass, firstly mix 46% of ammonium bifluoride, 12% of ammonium fluoride, 8% of ammonium fluorosilicate, 8% of potassium fluoroborate, 5% of calcium fluoride, and 5% of precipitated barium sulfate %, 5% barium carbonate, 3% polyethylene glycol, 1% gum arabic, 2% starch, and 5% organic acid are ground into fine powders respectively, and then pour the above fine powders into a mixer and mix until uniform.

Embodiment 3

[0016] Frosting powder for processing anti-glare glass is made by mixing the following raw materials according to the following weight ratio: ammonium bifluoride 48%, ammonium fluoride 14%, ammonium fluorosilicate 6%, potassium fluoroborate 6%, fluoride Calcium 7%, precipitated barium sulfate 7%, barium carbonate 3%, polyethylene glycol 1%, gum arabic 1.5%, starch 2.5%, organic acid 4%.

[0017] The preparation method of frosting powder for processing anti-glare glass, firstly mix ammonium bifluoride 48%, ammonium fluoride 14%, ammonium fluorosilicate 6%, potassium fluoroborate 6%, calcium fluoride 7%, precipitated barium sulfate 7% %, barium carbonate 3%, polyethylene glycol 1%, gum arabic 1.5%, starch 2.5%, and organic acid 4% were ground into fine powders respectively, and then the above fine powders were poured into a mixer and stirred until uniform.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses glass frosting powder for processing anti-dazzle glass and a preparation method thereof. The glass frosting powder is prepared by mixing the following raw materials in percentage by weight: 44-48% of ammonium bifluoride, 10-14% of ammonium bifluoride, 6-10% of ammonium fluosilicate, 6-10% of potassium fluoborate, 3-7% of calcium fluoride, 3-7% of precipitated barium sulphate, 3-7% of barium carbonate, 1-5% of polyethylene glycol, 0.5-1.5% of Arabic gum, 1-3% of starch and 3-7% of organic acid. The preparation method comprises the steps of grinding the raw materials into powder respectively, then pouring the fine powder into a mixer, and uniformly mixing.

Description

technical field [0001] The invention relates to a frosting powder for processing anti-glare glass, and also relates to a preparation method of the frosting powder. Background technique [0002] Chinese patent CN101654330B discloses such a glass anti-glare liquid and a method for processing anti-glare glass using the anti-glare liquid. The anti-glare liquid is mixed with the following raw materials according to the following weight ratio: 10-22 parts of gum arabic powder , 40-45 parts of hydrochloric acid, 20-23 parts of hydrofluoric acid, 10-15 parts of ammonium bifluoride, 10-20 parts of polyethylene glycol; the method is carried out according to the following steps: ⑴ cleaning the glass; Treat the cleaned garbage glass for 30-120 seconds; ⑶ cooling down; ⑷ spray cleaning, constant temperature drying. The paste made from the above formula is simple to make, has a wide range of passing through the net, does not produce burrs, and is not affected by temperature and humidity...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C15/00
Inventor 张源兴张树和
Owner LONGYAN HEDA MACHINERY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com