Preparation method of Ru/C catalyst and glycerine hydrogenolysis method

A glycerol hydrogenolysis and catalyst technology, which is applied in the preparation of organic compounds, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of limited service life of catalysts, poor catalyst stability, complicated production operations, etc., and achieve outstanding activity. Stability, good stability, the effect of reducing production cost

Active Publication Date: 2013-04-17
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ru / C is more suitable for reacting in an aqueous solution, but because the aqueous solution of the reaction raw material contains a certain amount of alkali, the pH value is generally 9-11, and the Ru / C catalyst prepared by the existing method has poor stability in such a medium. The conversion rate will decrease with time, so the service life of the catalyst is limited. In order to maintain a certain catalytic activity, the catalyst needs to be replaced frequently, which makes the production operation complicated and the cost increases
Experiments have shown that the higher the alkali content in the reaction raw materials, the worse the stability of the catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] The preparation method of the glycerol hydrogenolysis catalyst of the present invention adopts ruthenium as an active component and activated carbon as a carrier, completes the loading of the active component by an exchange method, and then uses a chemical reagent (formaldehyde or hydrazine hydrate) for reduction, which is similar to other preparation methods. In comparison, this Ru / C catalyst can maintain better activity stability in basic raw materials. Compared with copper catalyst, it is more suitable for dilute glycerol with higher water content as raw material, and can obtain better hydrogenolysis effect in the gas-liquid-solid three-phase reaction under mild conditions. The active component ruthenium used is generally RuCl 3 ·xH 2 O, the carrier activated carbon is coconut shell activated carbon, etc. In order to better disperse the active components on the surface of the carrier, the carrier can be ground into 40-80 mesh fine powder.

[0016] The hydrogenolysi...

Embodiment 1

[0018] Weigh 0.99gRuCl 3. xH 2 O (containing Ru37.5-40%), add deionized water to dissolve, adjust pH=1 with hydrochloric acid, add 8g activated carbon, and let stand for 12 hours. Heat in a water bath around 45°C, adjust pH=9 with 4% NaOH aqueous solution, add 15ml formaldehyde solution, heat to 80°C, and stir and reflux for 4 hours. After cooling to room temperature, wash with deionized water until neutral and free of Cl - ions (with 0.1M AgNO 3Aqueous solution test), a Ru / C catalyst was obtained, and the Ru content was about 4.7%.

Embodiment 2

[0020] Weigh 0.49gRuCl 3. xH 2 O (containing Ru37.5-40%), add deionized water to dissolve, adjust pH=2 with hydrochloric acid, add 8g activated carbon, and let stand for 2 hours. Heat in a water bath at about 60°C, adjust pH=11 with 4% NaOH aqueous solution, add 10ml formaldehyde solution, heat to 90°C, and stir and reflux for 2 hours. After cooling to room temperature, it was washed with deionized water until neutral to obtain a Ru / C catalyst with a Ru content of about 2.3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a Ru / C catalyst and a glycerine hydrogenolysis method. The Ru / C catalyst uses active carbon as a carrier and Ru as an active component. The preparation method comprises the steps of: with a RuCl3 water solution as an exchange solution, loading RuCl3 on the carrier by using an exchange method; and with formaldehyde or hydrazine hydrate as a reducing agent, completing the reduction reaction under the alkaline condition to obtain the Ru / C catalyst. When the Ru / C catalyst is used in the glycerine hydrogenolysis reaction, the transformation rate of glycerine is high, the selectivity of dihydric alcohol is good, and the stability of the catalyst in a reaction medium is good; and the Ru / C catalyst is especially suitable for the hydrogenolysis reaction of dilute glycerine with high water content.

Description

technical field [0001] The invention relates to a preparation method of a Ru / C catalyst and a method for preparing a dihydric alcohol by hydrogenolysis of glycerol. Background technique [0002] The traditional production method of chemical alcohol is based on petroleum, and it is prepared through a series of chemical processes (the most important of which is oxidation reaction). For example, ethylene oxide is used as a raw material to produce ethylene glycol, and propylene oxide is used as a raw material to produce propylene glycol, which consumes a large amount of petroleum products every year. Due to the shortage of petroleum resources and the non-renewability of petroleum, the use of renewable resources to replace petroleum to produce polyhydric alcohols is the development direction in this field. For example, glycerol can be obtained by hydrogenolysis at high temperature and high pressure to obtain dihydric alcohols such as ethylene glycol and propylene glycol. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/46C07C31/20C07C29/60C07C29/00
Inventor 苏杰陈明李风华
Owner CHINA PETROLEUM & CHEM CORP