Archaized bricks produced by using polished brick factory waste materials and preparation method thereof

A technology of polished brick waste and antique bricks, which is applied in the field of antique bricks, can solve the problems of low treatment and utilization of polished brick waste water and slag, water and air pollution, and waste slag occupying cultivated land, etc., to achieve green and environmentally friendly industrial production and sustainable development. The effect of high surface wear resistance and long service life

Inactive Publication Date: 2013-04-17
李建顺
View PDF1 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The degree of treatment and utilization of polished tile wastewater and waste residue is relatively low, and most of them are landfilled, resulting in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. Brick manufacturing

[0035] Weighing by weight: 9 parts of polished tile waste, 11 parts of blank raw materials, 10 parts of water; mix the obtained components evenly to obtain the required mixture; grind the obtained mixture into slurry, and the grinding time is 9 hours, the moisture content is controlled at 30-35%; add the coloring material according to the design requirements, mix the coloring material and the slurry evenly to obtain a colored slurry; transport the colored slurry to the spray tower, process and dry to powder shape; the dried powder is injection molded and punched into adobe, the pressure is controlled at 210-230Pa; the adobe is dried through a drying kiln to obtain a finished adobe;

[0036] 2. Glazing on the surface of brick adobe

[0037] Take in parts by weight: 0.5 parts of raw materials for glaze, 0.25 parts of water; mix the obtained ingredients evenly, grind them into glaze slurry, and the grinding time is 25 hours; apply the glaze slurry...

Embodiment 2

[0041] 1. Brick manufacturing

[0042] Weigh by weight: 10 parts of polished tile waste, 10 parts of blank raw materials, 10 parts of water; mix the obtained components evenly to obtain the required mixture; grind the obtained mixture into slurry, and the grinding time is 11 hours, the moisture content is controlled at 30-35%; add the coloring material according to the design requirements, mix the coloring material and the slurry evenly, and obtain a colored slurry; transport the colored slurry to the spray tower, and process and dry to Powder form; injection mold the dried powder and punch it into adobe, the pressure is controlled at 210-230Pa; dry the adobe through a drying kiln to obtain a finished adobe;

[0043] 2. Glazing on the surface of brick adobe

[0044] Take in parts by weight: 1 part of raw materials for glaze, 0.5 part of water; mix the obtained ingredients evenly, grind them into glaze slurry, and the grinding time is 30 hours; apply the glaze slurry on the su...

Embodiment 3

[0048] 1. Brick manufacturing

[0049] Weigh by weight: 8 parts of polished tile waste, 12 parts of blank raw materials, 10 parts of water; mix the obtained components evenly to obtain the required mixture; grind the obtained mixture into slurry, and the grinding time is 10 hours, the moisture content is controlled at 30-35%; add the coloring material according to the design requirements, mix the coloring material and the slurry evenly to obtain a colored slurry; transport the colored slurry to the spray tower, process and dry to powder shape; the dried powder is injection molded and punched into adobe, the pressure is controlled at 210-230Pa; the adobe is dried through a drying kiln to obtain a finished adobe;

[0050] 2. Glazing on the surface of brick adobe

[0051] Take in parts by weight: 1 part of raw materials for glaze, 0.5 part of water; mix the obtained ingredients evenly, grind them into glaze slurry, and the grinding time is 30 hours; apply the glaze slurry on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses archaized bricks produced by using polished brick factory waste materials. The bricks comprise the following components in part by weight: 8 to 10 parts of polished brick waste materials, 10 to 12 parts of raw materials for blanks, 0.04 to 1 part of raw materials for glazes and 10 to 15 parts of water, wherein the raw materials for the blanks are one of clay, quartz and chinastone or combinations thereof. The bricks have the benefits that the water absorptivity is about 1-3 percent, the breaking strength can achieve 2,050 N, the surface wear resistance is high, grinding marks are visible by level 4 and 2,100 r, and the service life is long; and at the same time, as the archaized bricks are produced by using the polished brick factory waste materials, the wastes are turned into the wealth, and the environment-friendly industrial production and the sustainable development can be achieved.

Description

technical field [0001] The invention relates to the technical field of decorative materials, in particular to an antique brick produced by using waste materials from a polished brick factory. Background technique [0002] With the continuous progress of society, people's requirements for environmental protection are getting higher and higher. At present, the wastewater and waste produced by the polishing of a large number of vitrified tiles in the ceramic industry have a great impact on the environment. The degree of treatment and utilization of polished tile wastewater and waste residue is relatively low, and most of them are landfilled, resulting in a large amount of waste residue occupying cultivated land, polluting water and air, and how to effectively treat waste has become a problem. Contents of the invention [0003] The purpose of the present invention is to produce a kind of antique brick with low water absorption rate, high strength and good anti-slip and anti-fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/22C04B33/132C04B35/14C04B41/86
CPCY02P40/60
Inventor 李建顺
Owner 李建顺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap