Material used for manufacturing handle of refrigerator door and preparation method thereof

A technology for door handles and refrigerators, applied in the field of polymer materials and their forming and processing, can solve the problems of difficult cleaning of the film, and achieve the effects of excellent mechanical properties, good antibacterial properties and smooth surface

Active Publication Date: 2013-04-17
HEFEI GENIUS NEW MATERIALS
View PDF1 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in order to increase the antibacterial performance of the refrigerator door handle, some people will paste some antibacterial and wear-resistant films on the basis of the original materials, but this film is not easy to clean and needs to be replaced frequently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] First, SiC whiskers that are 3 parts by weight, compatibilizer 1 that are 3 parts by weight, antibacterial agent 1 that are 0.03 parts by weight, lubricant 1 that is 0.01 parts by weight and tetrakis[methyl-β] that are 0.01 parts by weight -(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester and tris(2,4-di-tert-butylphenyl)phosphite in a 1:1 mixture. Place in a temperature-controlled high-speed blender. Stir at high speed at 90°C for 2 minutes, then add 40 parts by weight of polybutylene terephthalate pellets and 5 parts by weight of acrylonitrile-styrene-acrylic acid terpolymer at room temperature and stir for 2 minutes, and finally mix The last component is put into the extruder. During the extrusion process, 35 parts by weight of glass fiber is added from the glass fiber port, mixed at 255-270°C to obtain a polymer, and the obtained polymer is extruded in a strip shape, and then It is cut into segments to form 2-5mm pellets. The obtained pellets we...

Embodiment 2

[0076] First, the SiC whiskers with 20 parts by weight, the compatibilizer 1 with 10 parts by weight, the antibacterial agent 2 with 2 parts by weight, the lubricant 2 with 2 parts by weight and the tetrakis[methyl-β with 2 parts by weight] -(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester and tris(2,4-di-tert-butylphenyl)phosphite in a 1:1 mixture. Place in a temperature-controlled high-speed blender. Stir at high speed at 90°C for 10 minutes, then add 83 parts by weight of polybutylene terephthalate pellets and 25 parts by weight of acrylonitrile-styrene-acrylic acid terpolymer at room temperature and stir for 6 minutes, and finally mix The last component is put into the extruder. During the extrusion process, 10 parts by weight of glass fiber is added from the glass fiber port, mixed at 255-270°C to obtain a polymer, and the obtained polymer is extruded in a strip shape, and then It is cut into segments to form 2-5mm pellets. The obtained pellets were i...

Embodiment 3

[0078] First, SiC whiskers with 5 parts by weight, compatibilizer 1 with 3 parts by weight, antibacterial agent 1 with 0.05 parts by weight, lubricant 1 with 0.05 parts by weight and tetrakis[methyl-β with 0.05 parts by weight] -(3,5-di-tert-butyl-4-hydroxyphenyl)propionate]pentaerythritol ester and tris(2,4-di-tert-butylphenyl)phosphite in a 1:1 mixture. Place in a temperature-controlled high-speed blender. Stir at high speed at 90°C for 5 minutes, then add 50 parts by weight of polybutylene terephthalate pellets and 8 parts by weight of acrylonitrile-styrene-acrylic acid terpolymer at room temperature and stir for 3 minutes, and finally mix The last component is put into the extruder. During the extrusion process, 30 parts by weight of glass fiber is added from the glass fiber port, mixed at 255-270°C to obtain a polymer, and the obtained polymer is extruded in strips, and then It is cut into segments to form 2-5mm pellets. The obtained pellets were injection molded into c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a material used for manufacturing a handle of a refrigerator door and a preparation method thereof. The material composition comprises the following components in parts by weight: 40-83 parts of polybutylene terephthalate, 5-25 parts of acrylonitrile- styrene-acrylonitrile composition, 10-35 parts of glass fiber, 3-20 parts of crystal whisker, 2-10 parts of a compatilizer, 0.03-2 parts of an antibacterial agent, 0.01-2 parts of a lubricating agent and 0.01-2 parts of other auxiliaries; and the components are mixed in the formula, and then extrusion pelleting is carried out by virtue of an extruding machine, so that the material composition product is obtained. Compared with the prior art, the material composition provided by the invention is subjected to moulding and processing, the prepared handle of the refrigerator door is smooth and produces no warpage on the surface, no glass fiber is exposed, dimensional stability is good, and the prepared handle of the refrigerator door is resistant to scraping and has excellent antibacterial property.

Description

technical field [0001] The invention relates to the field of polymer materials and their molding processing, in particular to a polybutylene terephthalate (PBT) composition used for preparing refrigerator door handles and a preparation method thereof. Background technique [0002] The door handle of the refrigerator is frequently used in daily life, and needs to be opened and closed frequently all year round, especially sometimes with hands stained with raw meat or other pollutants to open and close the refrigerator, leaving stains inadvertently, which makes the door handle of the refrigerator become bacteria or even Virus breeding grounds. Some people say that the door handle of the refrigerator is one of the ten dirtiest places in the house. The bacteria on it is 200 times that of the toilet seat. It is recommended to clean it with bleach and disinfectant once a week. In view of the special use environment and cleaning requirements, the requirements for the material of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L51/00C08L25/08C08L25/12C08K13/04C08K7/14C08K7/10C08K5/134C08K5/526
Inventor 吕励耘
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com