Method for preparing foamed ceramic sound absorption material through protein foaming
A technology of foam ceramics and sound-absorbing materials, applied in ceramic products, applications, household appliances, etc., can solve problems such as difficulty in control, and achieve the effects of no pollution to the environment, low preparation costs, and wide sources of raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] A method for preparing a foam ceramic sound-absorbing material by foaming protein of the present invention, comprising the following steps:
[0033] (1) Preparation of foam slurry: mix and dissolve silicon nitride powder, sintering aid (choose yttrium oxide) and dispersant (DURAMAX-D3005 dispersant produced by Rohm and Haas) in water, among which silicon nitride powder The amount of water added to the solvent is 40vol.%, the amount of sintering aid added to the silicon nitride powder is 5wt.%, the amount of dispersant added to the solid phase component is 0.35wt.%, and then added to the mixture Whey protein powder (the addition of whey protein powder is 8wt.% of the mixture) is ball milled once for 20 hours, and egg white protein powder is added to the mixed components after the first ball mill (the addition of egg white protein powder is mixed 2wt.% of the component is subjected to secondary ball milling, and foam slurry is obtained after secondary ball milling for 10 ...
Embodiment 2
[0040] A method for preparing a foam ceramic sound-absorbing material by foaming protein of the present invention, comprising the following steps:
[0041] (1) Preparation of foam slurry: mix and dissolve silicon nitride powder, sintering aid (choose yttrium oxide) and dispersant (DURAMAX-D3005 dispersant produced by Rohm and Haas) in water, among which silicon nitride powder The amount of water added to the solvent is 50vol.%, the amount of sintering aid added to the silicon nitride powder is 5wt.%, the amount of dispersant added to the solid phase component is 0.35wt.%, and then added to the mixture Whey protein powder (the addition of whey protein powder is 4wt.% of the mixture) is ball milled once for 20 hours, and egg white protein powder is added to the mixed components after the first ball mill (the addition of egg white protein powder is mixed 4wt.% of the components) for secondary ball milling, and foam slurry was obtained after secondary ball milling for 10 hours;
...
Embodiment 3
[0048] A method for preparing a foam ceramic sound-absorbing material by foaming protein of the present invention, comprising the following steps:
[0049] (1) Preparation of foam slurry: mix and dissolve silicon nitride powder, sintering aid (choose yttrium oxide) and dispersant (DURAMAX-D3005 dispersant produced by Rohm and Haas) in water, among which silicon nitride powder The amount of water added to the solvent is 50vol.%, the amount of sintering aid added to the silicon nitride powder is 5wt.%, the amount of dispersant added to the solid phase component is 0.35wt.%, and then added to the mixture Whey protein powder (the addition of whey protein powder is 8wt.% of the mixture) is ball milled once for 20 hours, and egg white protein powder is added to the mixed components after the first ball mill (the addition of egg white protein powder is mixed 2wt.% of the component is subjected to secondary ball milling, and foam slurry is obtained after secondary ball milling for 10 ...
PUM
Property | Measurement | Unit |
---|---|---|
density | aaaaa | aaaaa |
density | aaaaa | aaaaa |
density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com