Method for preparing zno film with hierarchical structure porous array by electrodeposition method

A technology of hierarchical structure and electrodeposition method, applied in the direction of electrolytic inorganic material coating, etc., can solve the problem of high requirements for operators' basic skills and achieve the effect of reducing the technical difficulty of operation

Inactive Publication Date: 2016-03-30
HENAN UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the preparation of ZnO array films, aluminum oxide (AAO) templates are usually used to prepare, but this method needs to prepare high-quality porous array alumina templates in advance, and also requires a good template transfer technology, and the preparation process has a great impact on the operator. Basic skills required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing zno film with hierarchical structure porous array by electrodeposition method
  • Method for preparing zno film with hierarchical structure porous array by electrodeposition method
  • Method for preparing zno film with hierarchical structure porous array by electrodeposition method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The method for preparing hierarchical structure porous array ZnO film by electrodeposition method comprises the following steps:

[0045]1) Assemble PS templates with different layers and particle sizes on the FTO conductive glass, the specific method is:

[0046] a. After cleaning the glass slide, vertically immerse it in a PS aqueous solution with a PS particle size of 2.5 μm (the PS mass concentration of the PS aqueous solution is 5%) and let it stand for 2 to 3 minutes, then pull it out vertically at a pulling speed of 4cm / min , dried at room temperature to obtain a single-layer array template, and then slowly insert the single-layer array template into water at an inclination angle of 45°, the PS beads are automatically peeled off and rearranged in a single layer on the water surface, and a single-layer array template floating on the water surface is obtained. layer PS template;

[0047] b. Use tweezers to take another FTO conductive glass (the size of FTO conduct...

Embodiment 2

[0055] The method for preparing hierarchical structure porous array ZnO film by electrodeposition method comprises the following steps:

[0056] 1) Assemble PS templates with different layers and particle sizes on the FTO conductive glass, the specific method is:

[0057] a. After cleaning the glass slide, vertically immerse it in a PS aqueous solution with a PS particle size of 2.5 μm and let it stand for 2 to 3 minutes, then pull it out vertically at a pulling speed of 4 cm / min, and dry it at room temperature to obtain a single-layer array template. Then the single-layer array template is slowly inserted into the water at an inclination angle of 45°, the PS balls are automatically peeled off and rearranged in a single layer on the water surface, and a single-layer PS template floating on the water surface is obtained;

[0058] b. Use tweezers to take another FTO conductive glass (the size of FTO conductive glass is 2x1cm 2 ) as a carrier, after cleaning, insert the carrier ...

Embodiment 3

[0066] The method for preparing hierarchical structure porous array ZnO film by electrodeposition method comprises the following steps:

[0067] 1) Assemble PS templates with different layers and particle sizes on the FTO conductive glass, the specific method is:

[0068] a. After cleaning the glass slide, vertically immerse it in a PS aqueous solution with a PS particle size of 2.5 μm and let it stand for 2 to 3 minutes, then pull it out vertically at a pulling speed of 4 cm / min, and dry it at room temperature to obtain a single-layer array template. Then the single-layer array template is slowly inserted into the water at an inclination angle of 45°, the PS balls are automatically peeled off and rearranged in a single layer on the water surface, and a single-layer PS template floating on the water surface is obtained;

[0069] b. Use tweezers to take another FTO conductive glass (the size of FTO conductive glass is 2x1cm 2 ) as a carrier, after cleaning, insert the carrier ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The present invention involves a method of preparation of a grading structure of the electrical sedimentary method of a multi -hole array ZNO film: 1), assemble the number of layers and particles with different particles and particle size on the FTO conductive glass, and put the income template after drying the temperature of the vacuum and dry it in the vacuum drying.Dry in the box; 2) The templates made by step 1 as the working electrode, the platinum sheet as the electrode, the saturated glyphosa mercury electrical reference electrode, the zinc salt water solution as the sediment, -1.3V deposition 10 ~ 10 ~30min; 3) The template after the step 2) The template after the electricity is accumulated was rinsed with a secondary ion water, and the vacuum drying box was dried in the vacuum drying box after the room temperature was dry.The present invention can prepare a hierarchical ZNO porous array film with a hierarchical structure that can be controlled by the number of layers and pores, reducing the difficulty of operating technology, and realizing the number of ZNO porous array films that can prepare the number of layers and pores with electrical deposition method, and have a classified structure.

Description

technical field [0001] The invention relates to the field of preparation of nanometer materials, in particular to a method for preparing ZnO thin films with hierarchical structure porous arrays by electrodeposition. Background technique [0002] Zinc oxide (ZnO) with a hexagonal wurtzite structure is a wide-bandgap semiconductor, which has broad application prospects in luminescence, sensors, superhydrophobic materials, dye-sensitized solar cells, and photocatalytic degradation of organic wastewater. As one of the commonly used functional materials, ZnO has the advantages of non-toxicity, high catalytic activity, and strong oxidation ability. The performance of ZnO thin film material is slightly inferior to that of powder material, but it is convenient for thin film material to have the advantages of easy separation and recyclability. [0003] At present, the methods for preparing ZnO thin films mainly include magnetron sputtering, chemical vapor deposition, hydrothermal sy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D9/04
Inventor 雷建飞李立本倪静杜凯魏荣慧毛爱霞
Owner HENAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap