Cement and preparation method thereof

A technology of cement and quartz sand powder, applied in the field of materials, can solve the problems of poor anti-seepage effect, etc., and achieve the effects of good waterproofness, excellent performance and good slurry stability

Inactive Publication Date: 2013-05-15
杨益
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the ones used in places with serious water seepage often have the disadvantage of poor anti-seepage effect, especially when waterproofing small gaps.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A cement comprising 50g of No. 80 cement, 20g of quartz sand powder, 5g of diatomaceous earth powder, 10g of barium sulfate powder, 3g of Op-10 emulsifier and 5g of sodium phosphate.

[0016] The particle size of quartz sand powder and diatomaceous earth powder are both 100 microns.

[0017] A preparation method of cement, comprising the following steps:

[0018] First, get the material of the stated weight for subsequent use.

[0019] Second, take 50g of No. 80 No. 80 cement, 20g of quartz sand powder, 5g of diatomaceous earth powder, 10g of barium sulfate powder, 3g of Op-10 emulsifier and 5g of sodium phosphate, mix them evenly, and grind them to the particle size in the jet mill is 50 microns.

[0020] Third, add 10g of barium sulfate powder, 8g of Op-10 emulsifier and 10g of sodium phosphate to the substance obtained in the previous step, and stir in a blender for 20 minutes to obtain the product.

Embodiment 2

[0022] A cement comprising 100g of No. 80 cement, 30g of quartz sand powder, 10g of diatomaceous earth powder, 15g of barium sulfate powder, 8g of Op-10 emulsifier and 10g of sodium phosphate.

[0023] Both the particle size of quartz sand powder and diatomaceous earth powder are 300 microns.

[0024] A preparation method of cement, comprising the following steps:

[0025] First, get the material of the stated weight for subsequent use.

[0026] Second, take 100g of No. 80 cement, 30g of quartz sand powder and 10g of diatomaceous earth powder, mix them evenly, and grind them in a jet mill until the particle size is 100 microns.

[0027] Third, add 15g of barium sulfate powder, 8g of Op-10 emulsifier and 10g of sodium phosphate to the substance obtained in the previous step, and stir in a blender for 20 minutes to obtain the product.

Embodiment 3

[0029] A cement comprising 70g of No. 80 cement, 25g of quartz sand powder, 8g of diatomaceous earth powder, 8g of barium sulfate powder, 5g of Op-10 emulsifier and 8g of sodium phosphate.

[0030] The particle size of quartz sand powder and diatomaceous earth powder are both 150 microns.

[0031] A preparation method of cement, comprising the following steps:

[0032] First, get the material of the stated weight for subsequent use.

[0033] Second, take 70g of No. 80 cement, 25g of quartz sand powder and 8 g of diatomaceous earth powder, mix them evenly, and grind them in a jet mill until the particle size is 70 microns.

[0034] Third, add 8 g of barium sulfate powder, 5 g of Op-10 emulsifier and 8 g of sodium phosphate to the substance obtained in the previous step, and stir in a blender for 15 minutes to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to cement, which comprises the following components by weight: 50-100g of 80# cement, 20-30g of silica sand powder, 5-10g of diatomite powder, 10-15g of barium sulfate powder, 3-8g of OP-10 emulsifier and 5-10g of sodium phosphate, wherein the granularities of 20-30g of silica sand powder and 5-10g of diatomite powder are respectively 100-300 micrometers. The preparation method of the cement comprises the following steps of: 1, taking the components by weight for later use; 2, uniformly mixing the 80# cement, the silica sand powder and the diatomite powder to obtain a mixture, and grinding the mixture to reach the granularity of 50-100 micrometers in an air-current mill; 3, adding the barium sulfate powder, the OP-10 emulsifier and the sodium phosphate into the ground material, and stirring for 10-20 minutes in a stirrer. The cement is excellent in waterproofness and can be used for improving the performance of cement paste with higher water content by using a material consisting of phosphate and mineral substances; the cement is especially suitable for being used during waterproof operation to small gaps; and the cement paste is good in paste stability and quick to harden.

Description

technical field [0001] The invention belongs to the field of materials, in particular to a cement and a preparation method thereof. Background technique [0002] Cement is a powdery hydraulic inorganic gelling material. It can be hardened in air or water after being stirred with water to form a slurry. It is used to cement sand, stone and other granular materials into mortar or concrete. [0003] At present, the ones used in places with serious water seepage often have the disadvantage of poor anti-seepage effect, especially when waterproofing small gaps. Contents of the invention [0004] One object of the present invention is to provide a kind of cement. Another object of the present invention is to provide a preparation method of cement. The cement has fine texture and good waterproof effect. The preparation method has simple steps and is safe and environment-friendly. [0005] The technical solutions adopted are: [0006] A cement comprising 50-100g of No. 80 cement,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B22/16
Inventor 杨益
Owner 杨益
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com