A kind of water-based glass paint and preparation method thereof

A technology of water-based glass paint and water-based polyurethane, which is applied in coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve problems such as weak permeability, poor chemical resistance, and poor adhesion, and achieve strong cohesion and Adhesion, small coefficient of thermal expansion, enhanced adhesion

Inactive Publication Date: 2016-01-20
合肥市科睦佰水性材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As a functional and environmentally friendly water-based paint, water-based glass paint has the advantages of obvious decorative effect, colorful paint film, and easy cleaning. Water-based glass paint has poor solvent permeability, poor wettability of water-based paint to glass, and high surface finish of the substrate, which makes it difficult for water-based paint to adhere well to glass equipment, which seriously hinders the development of glass paint. The types of water-based glass paint mainly include polyurethane water dispersion system, water-soluble polyacrylic resin type, and acrylate-modified polyurethane type. The main problems are poor adhesion, poor chemical resistance, poor solvent resistance, and poor water boiling resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A kind of water-based glass paint, it is made up of the raw material of following weight part:

[0019] Water-based polyurethane resin 65, modified epoxy resin 12, dipropylene glycol butyl ether 3, pure water 10, gull gum 0.6, defoamer dimethyl silicone oil 0.2, diisooctyl sodium sulfosuccinate 0.6, aluminum oxide 0.5 , accelerator TMTM0.4, leveling agent 0.5, polyethylene oxide 0.3, water-based silane coupling agent KH4601, dibutyl maleate 0.1;

[0020] The modified epoxy resin is composed of the following raw materials in parts by weight: E-20 epoxy resin 70, dicumyl peroxide 6, butenedioic anhydride 5, glycerin 4, nanometer calcium carbonate 8;

[0021] Mix the above weight parts of E-20 epoxy resin and dicumyl peroxide into a high-speed mixer, increase the stirring speed of the mixer from low speed to high speed, and when the temperature of the mixed material gradually rises to 85°C, add the above weight Parts of butenedioic anhydride, nano-calcium carbonate, stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne glass paint and a preparation method of the paint. The waterborne glass paint comprises the following raw materials in parts by weight: 55-65 parts of waterborne polyurethane resin, 8-12 parts of modified epoxy resin, 1-3 parts of dipropylene glycol mono butyl ether, 10-15 parts of pure water, 0.4-0.6 part of guar gum, 0.2-0.4 part of defoamer dimethyl silicone oil, 0.2-0.6 part of dioctyl sodium sulfosuccinate, 0.3-0.5 part of aluminium oxide, 0.2-0.4 part of accelerator TMTM, 0.3-0.5 part of flatting agent, 0.3-0.6 part of polyoxyethylene, 0.8-1.2 parts of waterborne silane coupling agent KH4600 and 0.1 part of dibutyl maleate. The waterborne glass paint produced by the method disclosed by the invention is free from bubbles, aggregation, foreign matters, and sediment stratification phenomenon, and can be infinitely diluted by using water, is reduced in cost and environment-friendly; a paint film is very strong in cohesive force and adhesive force and is strong in wear resistance at normal temperature; thermal expansion coefficient of the added modified epoxy resin is small so that adhesive attraction of the paint film is enhanced; and the adhesive force of the paint film is further enhanced by the added waterborne silane coupling agent.

Description

technical field [0001] The invention mainly relates to a paint and a preparation method thereof, in particular to a water-based glass paint and a preparation method thereof. Background technique [0002] As a functional and environmentally friendly water-based paint, water-based glass paint has the advantages of obvious decorative effect, colorful paint film, and easy cleaning. Water-based glass paint has poor solvent permeability, poor wettability of water-based paint to glass, and high surface finish of the substrate, which makes it difficult for water-based paint to adhere well to glass equipment, which seriously hinders the development of glass paint. The types of water-based glass paint mainly include polyurethane water dispersion system, water-soluble polyacrylic resin type, and acrylate-modified polyurethane type. The main problems are poor adhesion, poor chemical resistance, poor solvent resistance, and poor water boiling resistance. Contents of the invention [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D163/02C09D7/12
Inventor 吴协静曹晶晶
Owner 合肥市科睦佰水性材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products