Polyacrylate binder for pigment printing and preparation method of polyacrylate binder

A technology of polyacrylate and pigment printing, which is applied in the field of textile coatings, can solve the problems of insufficient water resistance, and achieve the effects of good washing resistance, low film forming temperature, and good water resistance

Inactive Publication Date: 2013-05-15
上海奇想青晨新材料科技股份有限公司
View PDF10 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, this type of material still has some technical weaknesses in practical applications, such as insufficient water resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyacrylate binder for pigment printing and preparation method of polyacrylate binder
  • Polyacrylate binder for pigment printing and preparation method of polyacrylate binder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A. First, add 2 parts by weight of compound emulsifier and 20 parts by weight of deionized water into the polymerization reactor, stir and heat up;

[0036] B. 30 parts by weight of deionized water, 7 parts by weight of composite emulsifier, 25 parts by weight of hard monomer (8 parts by weight of styrene and 17 parts by weight of methyl methacrylate composite) are added in the pre-emulsification kettle, Under the condition of constant speed (820 rev / min), after stirring for 360 minutes, a pre-emulsion was obtained, and 4.96 parts by weight thereof were weighed as the bottom seed reaction solution for subsequent use;

[0037] C. Raise the temperature of the polymerization reactor in step A to 70°C, drop 4.96 parts by weight of the bottom seed reaction solution in step B, and then add 1 part by weight of the initiator as the bottom initiator to react for 90 minutes, and continue to the polymerization reactor Add 200 parts by weight of deionized water, slowly lower the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyacrylate binder for pigment printing. The binder is prepared by polymerizing the following raw materials: a hard monomer, a soft monomer, a functional monomer, a compound emulsifying agent, organic silicone, an initiator, a pH regulating agent and deionized water. The invention also provides a preparation method of the polyacrylate binder for the pigment printing. According to the binder and the preparation method disclosed by the invention, proper proportion of the soft monomer to the hard monomer is selected, the mixture of a negative ion emulsifying agent and a nonionic emulsifying agent is used, and the binder is obtained through core-shell polymerization reaction so as to ensure that the binder for the pigment printing disclosed by the invention has pretty low film forming temperature, pretty good water resistance, and good scrubbing resistance, and can be widely applied to a pigment printing process in a dyeing and printing industry.

Description

technical field [0001] The invention belongs to the field of textile paints, in particular to a polyacrylate paint printing adhesive and a preparation method thereof. Background technique [0002] The pigment printing process not only has the characteristics of bright color, complete color spectrum, high color yield and easy color matching, but also has the advantages of simple process flow, energy saving and low cost, so it has developed rapidly in recent years and has become more and more popular. The printing and dyeing industry attaches great importance to it. The pigment printing process mainly uses the adhesive film-forming substance to fix the pigment that is insoluble in water, has no affinity and reactivity to the fabric on the fabric, so as to achieve the purpose of coloring, so the performance of the adhesive will directly affect the printed product. the quality of. [0003] However, this type of material still has some technical weaknesses in practical applicat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52C08F220/18C08F212/08C08F220/14C08F220/06C08F220/28C08F2/30C08F2/26C08G77/06
Inventor 戚向东
Owner 上海奇想青晨新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com