Hydrophobic masking tape and preparation method thereof

A technology of masking paper and tape, applied in the direction of adhesive, film/sheet adhesive, non-polymer organic compound adhesive, etc., can solve the problems of human injury, lack of use function, lack of UV resistance

Active Publication Date: 2013-06-26
SHANGHAI SMITH ADHESIVE NEW MATERIAL
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the adhesives of masking paper are generally made of volatile organic compounds such as benzene and toluene as solvents, which will produce toxic substances in the process of manufacture and use, pollute the environment, and cause harm to the human body
In addition, the existing masking tape lacks anti-ultraviolet (anti-UV) function, and does not have the function of outdoor use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The formula for preparing masking paper adhesive is as follows:

[0033] 300 parts of butyl acrylate,

[0034] 100 parts of isooctyl acrylate,

[0035] 2 parts acrylic,

[0036] 2 parts of hydroxyethyl acrylate,

[0037] 40 parts of styrene-acrylic emulsion,

[0038] 6 parts of sodium benzenesulfonate,

[0039] 450 parts of water,

[0040] 4 parts ammonium persulfate,

[0041] 0.2 parts of sodium bicarbonate.

[0042] The specific preparation method is as follows:

[0043] a. Add 85% sodium benzenesulfonate in the formula to the pre-emulsification kettle, mix with 45% water and stir evenly, and add all butyl acrylate, isooctyl acrylate, acrylic acid and hydroxyethyl acrylate in the formula Esters, stir evenly to make a pre-emulsion;

[0044] b. Add all the sodium bicarbonate, 55% water and all the remaining sodium benzenesulfonate in the formula to the reaction kettle; heat up to 85°C, add 70% ammonium persulfate, and all the styrene-acrylic emulsion;

[0045]...

Embodiment 2

[0048] The formula for preparing masking paper adhesive is as follows:

[0049] 280 parts of butyl acrylate,

[0050] 120 parts of isooctyl acrylate,

[0051] 4 parts acrylic,

[0052] 2 parts of hydroxyethyl acrylate,

[0053] 40 parts of styrene-acrylic emulsion,

[0054] 6 parts of sodium benzenesulfonate,

[0055] 400 parts of water,

[0056] 4 parts ammonium persulfate,

[0057] 0.2 parts of sodium bicarbonate.

[0058] The specific preparation method is as follows:

[0059] a. Add 88% sodium benzenesulfonate in the formula to the pre-emulsification kettle, mix with 40% water and stir evenly, and add all butyl acrylate, isooctyl acrylate, acrylic acid, and hydroxyethyl acrylate in the formula Esters, stir evenly to make a pre-emulsion;

[0060] b. Add all the sodium bicarbonate, 60% water and all the remaining sodium benzenesulfonate in the formula to the reaction kettle; heat up to 82°C, add 65% ammonium persulfate, and all the styrene-acrylic emulsion;

[0061...

Embodiment 3

[0064] The formula for preparing masking paper adhesive is as follows:

[0065] 260 parts of butyl acrylate,

[0066] 140 parts of isooctyl acrylate,

[0067] 3 parts acrylic,

[0068] 2 parts of hydroxyethyl acrylate,

[0069] 50 parts of styrene-acrylic emulsion,

[0070] 6 parts of sodium benzenesulfonate,

[0071] 450 parts of water,

[0072] 5 parts of ammonium persulfate,

[0073] 0.2 parts of sodium bicarbonate.

[0074] The specific preparation method is as follows:

[0075] a. Add 90% of the sodium benzenesulfonate in the formula to the pre-emulsification tank, mix with 50% of the water and stir evenly, and add all the butyl acrylate, isooctyl acrylate, acrylic acid and hydroxyethyl acrylate in the formula Esters, stir evenly to make a pre-emulsion;

[0076] b. Add all the sodium bicarbonate, 50% water and all the remaining sodium benzenesulfonate in the formula to the reaction kettle; heat up to 85°C, add 60% ammonium persulfate, and all the styrene-acrylic ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a hydrophobic masking tape and a preparation method thereof. The hydrophobic masking tape comprises a masking tape layer and an adhesive layer which is coated on the surface of the masking tape layer, wherein the adhesive formula of the adhesive layer comprises the following components in parts by weight: 200-300 parts of butyl acrylate, 100-200 parts of 2-ethylhexyl acrylate, 2-10 parts of acrylic acid, 2-10 parts of 2-hydroxyethyl acrylate, 30-60 parts of styrene-acrylic emulsion, 5-10 parts of sodium benzene sulfonate, 300-500 parts of water, 2-7 parts of ammonium persulfate and 0.1-0.5 part of sodium bicarbonate. A hydrophobic adhesive is adopted in a preparation process to remove the conventional organic solvent, and the masking tape is subjected to ultraviolet pretreatment, so that the produced masking tape is pollution-free and environment-friendly and has an outdoor use function.

Description

technical field [0001] The invention relates to a solvent-free water-based masking tape and a preparation method thereof. Background technique [0002] Masking tape is a high-tech decoration and spraying paper (also known as color separation tape because of its special properties), widely used in interior decoration, spraying of household appliances and spraying of high-end luxury cars. Masking tape is a roll-shaped adhesive tape made of masking paper and adhesive as the main raw materials. The adhesive is coated on the masking paper, and the other side is coated with anti-adhesive material. The color separation effect is clear and clear. It also has the effect of arc art, which has brought a new technological revolution to the decoration and spraying industry, and made the industry glow with new vitality. But at present, the adhesive of masking paper is generally made of volatile organic compounds such as benzene and toluene as solvents, which will produce toxic substances...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/04C09J4/02C09J4/06
Inventor 蔡振乐王如义
Owner SHANGHAI SMITH ADHESIVE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com