Black water-based ink for silk-screen printing

A water-based ink and screen printing technology, applied in the field of screen printing, can solve problems such as equipment failure, unfavorable printing, and excessive drying speed of black coloring materials, and achieve the effects of reduced foam, moderate drying speed, and improved color fastness

Inactive Publication Date: 2013-07-17
李莉
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The present invention aims to solve the problem that the water-based ink formulation in the prior art is not suitable for the preparation of black water-based ink, which will cause the black colorant to dry too fast and cannot be well fixed on the printed matter, which is not conducive to printing and even causes equipment failure. , to provide a black water-based ink for screen printing, its black is pure, and the drying speed is moderate during printing, and the color fastness is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A kind of black water-based ink for screen printing is made from the following raw materials in parts by weight:

[0041] Carbon black 22 parts

[0042] Anionic surfactant 2 parts

[0043] Latex 4 parts

[0044] 3 parts acrylic resin

[0045] 1 part ammonium hydroxide

[0046] 10 parts isopropyl alcohol

[0047] 3 parts cetylpyridinium bromide

[0048] Dispersant 2 parts

[0049] Defoamer 3 parts

[0050] 50 parts of deionized water.

Embodiment 2

[0052] A kind of black water-based ink for screen printing is made from the following raw materials in parts by weight:

[0053] Carbon black 40 parts

[0054] Anionic surfactant 10 parts

[0055] Latex 10 parts

[0056] 12 parts acrylic resin

[0057] Ammonium hydroxide 5 parts

[0058] 18 parts isopropanol

[0059] 9 parts cetylpyridinium bromide

[0060] Dispersant 9 parts

[0061] Defoamer 8 parts

[0062] 70 parts of deionized water.

Embodiment 3

[0064] A kind of black water-based ink for screen printing is made from the following raw materials in parts by weight:

[0065] Carbon black 31 parts

[0066] Anionic surfactant 6 parts

[0067] Latex 7 parts

[0068] 8 parts acrylic resin

[0069] 3 parts ammonium hydroxide

[0070] 14 parts isopropyl alcohol

[0071] 6 parts cetylpyridinium bromide

[0072] Dispersant 6 parts

[0073] Defoamer 6 parts

[0074] 60 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to black water-based ink for silk-screen printing, belonging to the technical field of silk-screen printing. The water-based ink is prepared from the following raw materials in parts by weight: 22-40 parts of carbon black, 2-10 parts of anionic surfactant, 4-10 parts of latex, 3-12 parts of acrylic resin, 1-5 parts of ammonium hydroxide, 10-18 parts of isopropanol, 3-9 parts of cetylpyridinium bromide, 2-9 parts of dispersant, 3-8 parts of defoaming agent and 50-70 parts of deionized water. The black water-based ink disclosed by the invention can solve the problems that a formula in the prior art is not suitable for preparing the black water-based ink, can enable the drying speed of a black pigment to be too fast and be incapable of well fixing the black pigment on a printed matter, is not conductive to printing and can even cause failure of equipment; and by using the combination of an alkali-soluble connecting material and a diffusible connecting material and selecting an appropriate color fixing agent for matching, the drying speed of the pigment is appropriate, the color fastness is improved, and the black water-based ink is further conductive to final printing effects.

Description

technical field [0001] The invention relates to an ink used in printing production, more specifically, the invention relates to a black water-based ink used for screen printing, which belongs to the technical field of screen printing. Background technique [0002] Screen printing belongs to stencil printing, and it is called the four major printing methods together with offset printing, embossing printing, and gravure printing. Stencil printing includes transcription, engraving, inkjet and screen printing. The principle of stencil printing is: when the printing plate (the hole that can pass the ink is made on the base of the paper film or other plate), the ink is transferred to the substrate (paper, ceramics, etc.) through the hole of the stencil through a certain pressure when printing ) to form an image or text. [0003] Screen printing originated in China and has a history of more than two thousand years. As early as the Qin and Han Dynasties in ancient China, the Jiej...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/03C09D11/107
Inventor 李莉
Owner 李莉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products