Water-based lotus leaf hydrophobic varnish for wallpaper and preparation method thereof
A technology of lotus leaf hydrophobicity and varnish, applied in papermaking, paper coating, textile and papermaking, etc., to prolong the shelf life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0046] A water-based lotus leaf hydrophobic varnish for wallpaper, comprising the following raw materials in proportion by weight: 15 parts of modified silicone polymer emulsion, 20 parts of non-film-forming acrylate emulsion, 10 parts of styrene-acrylic emulsion, and 3 parts of neutralizing amine , 2 parts of propylene glycol, 2 parts of water-based film-forming aids, 0.5 parts of water-based wetting and leveling agent, 0.2 parts of mineral defoamer, 8 parts of water-based nano-scale silicone waterproofing agent, 1 part of water-based polyurethane thickener, deionized 20 parts of water, 0.5 parts of silicone defoamer.
[0047] Prepare as follows:
[0048] (1) Add the modified silicone polymer emulsion, non-film-forming acrylate emulsion and neutralized amine into the container according to the stated ratio, and stir rapidly at a speed of 900r / min for 15min.
[0049] (2) Add mineral defoamer, propylene glycol, water-based film-forming aid, water-based wetting and leveling age...
Embodiment 2
[0054] A water-based lotus leaf hydrophobic varnish for wallpaper, comprising the following raw materials in proportion by weight: 35 parts of modified silicone polymer emulsion, 43 parts of non-film-forming acrylate emulsion, 15 parts of styrene-acrylic emulsion, and 1 part of neutralizing amine , 4 parts of propylene glycol, 7 parts of water-based film-forming agent, 1.4 parts of water-based wetting and leveling agent, 1 part of mineral defoamer, 10 parts of water-based nano-scale silicone water repellent, 4 parts of water-based polyurethane thickener, deionized 30 parts of water, 0.8 parts of silicone defoamer.
[0055] Prepare as follows:
[0056] (1) Add the modified silicone polymer emulsion, non-film-forming acrylate emulsion and neutralized amine into the container according to the stated ratio, and stir rapidly at a speed of 800r / min for 20min.
[0057] (2) Add mineral defoamer, propylene glycol, water-based film-forming aid, water-based wetting and leveling agent, a...
Embodiment 3
[0062] A water-based lotus leaf hydrophobic varnish for wallpaper, comprising the following raw materials in proportion by weight: 20 parts of modified silicone polymer emulsion, 50 parts of non-film-forming acrylate emulsion, 30 parts of styrene-acrylic emulsion, and 2 parts of neutralizing amine , 5 parts of propylene glycol, 6 parts of water-based film-forming aid, 2 parts of water-based wetting and leveling agent, 0.6 parts of mineral defoamer, 12 parts of water-based nano-scale silicone waterproofing agent, 5 parts of water-based polyurethane thickener, deionized 40 parts of water, 1 part of silicone defoamer.
[0063] Prepare as follows:
[0064] (1) Add the modified silicone polymer emulsion, non-film-forming acrylate emulsion and neutralized amine into the container according to the stated ratio, and stir rapidly at a speed of 650r / min for 20min.
[0065] (2) Add mineral defoamer, propylene glycol, water-based film-forming aid, water-based wetting and leveling agent, ...
PUM
Property | Measurement | Unit |
---|---|---|
glass transition temperature | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com