A kind of water-based ultra-high-speed spraying joint glue and preparation method thereof

A joint glue, ultra-high-speed technology, applied in the direction of polymer adhesive additives, non-polymer adhesive additives, monocarboxylate copolymer adhesives, etc., can solve the high viscosity and solid content of the joint glue , unable to meet production needs, accumulated damage and other problems, to achieve excellent rheological properties, avoid accumulated damage, and low solid content

Active Publication Date: 2020-12-01
北京长润化工有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mouthpiece glue produced by this method can meet the demand of 12,000-17,000 cigarettes per minute, and the residual amount of vinyl acetate monomer has also been correspondingly reduced. The content is still high, which cannot meet the production needs of up to 20,000 pieces / minute, and the emulsifier OP-10 used in the synthesis process is an alkylphenol polyoxyethylene ether nonionic emulsifier, which has accumulated damage to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] 1. Ratio preparation

[0064] Prepare materials according to the following proportions by weight: 60 parts of vinyl acetate, 14 parts of acrylic acid, 7 parts of methyl methacrylate, 12 parts of polyvinyl alcohol, 0.6 part of ammonium persulfate, 156 parts of deionized water, 5 parts of triethyl citrate 0.5-0.8 parts of polydimethylsiloxane, 1.5 parts of polyoxyethylene lauryl ether, 0.5-0.8 parts of Bropol, and 1.4 parts of sodium bicarbonate.

[0065] In an embodiment of the present invention, ammonium persulfate can also use other thermal decomposition initiators, such as potassium persulfate, tert-butyl hydroperoxide, and a redox system initiator, such as ammonium sulfate-bisulfite Sodium, etc.; Triethyl citrate can also be replaced by acetyl tributyl citrate, triacetin or 2,2,4-trimethyl-1,3-pentanediol diisobutyrate; Base siloxane can also be replaced by white mineral oil, but polydimethylsiloxane is preferred; Bropol used in the present invention can also be rep...

Embodiment 2

[0085] In addition to preparing materials according to the following proportions by weight: use 64 parts of vinyl acetate, 12 parts of acrylic acid, 7 parts of methyl methacrylate, 0.6 parts of ammonium persulfate, 1.6 parts of sodium bicarbonate, 14 parts of polyvinyl alcohol, isomeric alcohol poly 1.4 parts of oxyethylene ether, 5 parts of triethyl citrate, 0.6 parts of polydimethylsiloxane, 0.6 parts of Bropol, 193 parts of water; and the remaining 18 parts of polyvinyl alcohol aqueous solution in the reactor, other Steps and mode of operation are all the same as in Example 1.

Embodiment 3

[0087] In addition to preparing materials according to the following proportions by weight: use 62 parts of vinyl acetate, 16 parts of acrylic acid, 8 parts of methyl methacrylate, 0.8 parts of potassium persulfate, 1.5 parts of sodium bicarbonate, 10 parts of polyvinyl alcohol, lauryl polyoxygen 1.5 parts of vinyl ether, 4 parts of triethyl citrate, 0.6 part of white mineral oil, 0.6 part of isothiazolinone, 180 parts of total water; Example 1 is the same.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
solid contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-based ultra-high-speed spraying filter tipping adhesive and a preparation method thereof. The method uses polyvinyl alcohol as a protective colloid, and isomeric alcohol polyoxyethylene ether as an emulsifier to produce a ternary copolymer emulsion of vinyl acetate, methyl methacrylate, and acrylic acid, further improves fluidity and cohesiveness by adding a plasticizer and a polyvinyl alcohol aqueous solution, effectively lowers residual vinyl acetate monomers by vacuuming while stirring under relatively high temperature, and uses ionized water to adjust viscosity, thereby producing the ultra-high-speed spraying filter tipping adhesive suitable for a spraying gluing cigarette making machine. The method does not use any alkylphenol ethoxylates emulsifier which has accumulative harm to human body; and on the premises of low viscosity and low solid content, the produced filter tipping adhesive has high paper adhesion and high drying speed, and can achievestable adhesive supply on the spraying gluing cigarette making machine which is working at a speed of 20000 cigarettes per minute. The produced cigarette does not show air leak, filter tipping disconnection, wrinkles, or other undesirable phenomena, and has low a rejection rate.

Description

technical field [0001] The invention relates to a polymer adhesive, in particular to a water-based super-high-speed spray nozzle glue suitable for the cigarette industry. Background technique [0002] Mouth glue is an important cigarette material connecting cigarettes and filters, and its consumption is the largest among all water-based cigarette glues including lap glue for cigarettes, packaging glue and filter rod forming centerline glue. In the cigarette production process, it plays a decisive role in the crimping quality of cigarettes. At present, the gluing methods of the nozzle glue mainly include roller coating and spraying gluing. Different gluing methods have different performance requirements for the nozzle glue. One is that at the same coiling speed, compared with the roller coating method, spraying glue requires a more suitable drying speed of glue. Second, different gluing methods require different rheological properties of the nozzle glue. In order to prevent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J131/04C09J11/06C09J11/08C08F218/08C08F220/06C08F220/14C08F2/30
CPCC08F2/30C08F218/08C08K2201/014C09J11/06C09J11/08C09J131/04C08L29/04C08L83/04C08L71/02C08K5/11C08K5/103C08L91/06C08F220/06C08F220/14
Inventor 董彦林曹贵昌张弘胤
Owner 北京长润化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap