Flexible face brick

A flexible facing and formula technology, applied in the field of flexible facing bricks, can solve the problems of poor weather resistance, uneconomical cost, and high cost

Inactive Publication Date: 2013-08-21
NANCHONG KYOHO ENERGY SAVING TECH
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as the international oil price continues to rise, the cost of such products is high and uneconomical, and pure resin products have poor weather resistance and are easy to age. Therefore, it is necessary for the construction industry to seek better and more economical facing brick products. in pursuit of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] First make a soft mold. In this embodiment, silicone rubber is used as the mold glue. Of course, rubber can also be used as the mold glue. First, the surface pattern of the facing brick is designed. The surface pattern is three-dimensional. To make a negative mold, the same negative mold should be made several times. Since the silicone rubber is in the form of paste, adding a crosslinking agent and curing agent will solidify into an elastic solid in a short time. The mold made of silicone rubber can clone the same shape. products, the precision of its cloning is very high.

[0013] Take 40 kg of white cement, 8 kg of fly ash, 25 kg of 60-mesh quartz sand, 10 kg of 100-mesh quartz sand, 1 kg of lignocellulose, 3 kg of silicon micropowder, also called perlite, 5 kg of talcum powder, and 2 kg of calcium oxide. kg, sodium silicate powder 1 kg, alkali inhibitor 0.5 kg, acrylic rubber powder 2.5 kg, add 2.5 kg iron oxide pigment and mix evenly, put 28.28 kg of water into a cl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a flexible face brick. The flexible face brick is prepared from the following materials in parts by weight: 35-45 parts of cement, 5-10 parts of fly ash, 20-30 parts of quartz sand with a fineness of about 60 meshes, 5-15 parts of quartz sand with a fineness of about 100 meshes, 1-3 parts of lignocelluloses, 1-5 parts of silica powder, 3-8 parts of talcum powder, 1-5 parts of calcium oxide, 1-3 parts of sodium silicate, 0.5-1 part of antalkaline, 2-3 parts of acrylic rubber powder and 2-5 parts of an iron oxide pigment. The flexible face brick is prepared in the following steps of: mixing the materials in a formula; adding 28 parts of water, usually deionized water to 100 parts of materials; adding powder into the water; pulping a mixture into slurry with a homogenizer; uniformly coating 2 / 3 slurry to a die according to a proportion of about 3kg of slurry per square meter; paving at least one layer of 4# alkali-proof fiberglass gridding cloth; then uniformly coating the remaining 1 / 3 slurry; and finally removing scratches with a blacking brush.

Description

technical field [0001] The invention generally relates to a composite building material, in particular to a flexible facing brick made of a composite material. Background technique [0002] In the known formula of flexible facing tiles, the binder is mainly polymer, and natural stone powder is added inside, which is processed by a special process. However, as the international oil price continues to rise, the cost of such products is high and uneconomical, and pure resin products have poor weather resistance and are easy to age. Therefore, it is necessary for the construction industry to seek better and more economical facing brick products. has been pursuing. Contents of the invention [0003] The object of the present invention is to provide a flexible decorative brick which can overcome the disadvantages of the known technology, has economical manufacturing cost and superior performance. [0004] In order to achieve the above object, the solution of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B28/04
Inventor 秦吉坤
Owner NANCHONG KYOHO ENERGY SAVING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com