PU (Poly Urethane) sole antistatic agent

An antistatic agent and solvent technology, which is applied in the field of antistatic agents for PU soles, can solve problems such as dirt absorption, lower yield, and affect quality, and achieve the effects of simple preparation process, enhanced antistatic performance, and low production cost

Inactive Publication Date: 2013-08-28
SUZHOU JINGRO TECH
View PDF8 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Second, the harm caused by electrostatic gravity: (1) Electronic industry, absorbing dust, causing pollution of integrated circuits and semiconductor components, greatly reducing yield; (2) Film and plastic industry, making film or film winding uneven; film 1. CD plastic discs are contaminated with dust, which affects the quality; (3) causing printing industry, paper winding is not uniform, overprinting is not accurate, serious dirt absorption, and even paper bonding, affecting production; (4) textile industry, causing roots to flutter, Hazards such as entanglement, end breakage and yarn entanglement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An antistatic agent for PU shoe soles, which is composed of the following components mixed by weight percentage: 74% of 1-ethyl-3-methylimidazole ethyl sulfate, 15% of mannitol, and 11% of quaternary ammonium silver chloride.

[0018] The preparation method of the PU shoe sole antistatic agent of the present invention is to mix the above-mentioned components uniformly according to the proportion, stir at a high speed for 2-3 hours at room temperature, and then stand still for 1-2 hours to obtain the product.

Embodiment 2

[0020] An antistatic agent for PU shoe soles, which is composed of the following components mixed by weight percentage: 77% of 1-ethyl-3-methylimidazole ethyl sulfate salt, 12% of mannitol, and 11% of quaternary ammonium lithium chloride.

[0021] Its preparation method is identical with embodiment one.

Embodiment 3

[0023] An antistatic agent for PU shoe soles, which is composed of the following components mixed by weight percentage: 80% of 1-ethyl-3-methylimidazole ethyl sulfate, 12% of mannitol, and 8% of quaternary ammonium lithium chloride.

[0024] Its preparation method is identical with embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses PU (Poly Urethane) sole antistatic agent. The PU sole antistatic agent comprises the following components in percentage by weight: 68%-88% of 1-ethyl-3-methyl imidazole ethyl sulfate, 12%-18% of a polyalcohol solvent, and 8%-12% of quaternary ammonium salt compounds containing silver or lithium ions. The preparation method of the PU sole antistatic agent comprises the following steps of: uniformly mixing the components according to the proportion; stirring for 2 hours-3hours at a high speed under the normal temperature; and stewing for 1-2 hours to obtain the product. The PU sole antistatic agent disclosed by the invention is scientific in formula, low in production cost, simple in preparation process and capable of strengthening the antistatic performances of the sole.

Description

Technical field: [0001] The invention relates to an antistatic agent, in particular to an antistatic agent for PU shoe soles. Background technique: [0002] In the past, most of the materials used for shoe soles did not have natural materials, so the phenomenon of static electricity generated by friction was not taken seriously by people. However, with the development of petrochemical and electronic industries, polymer materials such as plastic rubber and chemical fibers have come out one after another, and the problem of static electricity has attracted more and more attention from all aspects. Because most of the polymer materials used in shoes belong to the category of electrolytes, their resistivity is very high, that is, the conductivity is very small, so it is easy to accumulate a large amount of charge, which will bring harm to life, production and even life. [0003] The hazard of static electricity refers to the damage caused by electrostatic discharge to electrost...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08K5/3445C08K5/19A43B13/04
Inventor 黄超
Owner SUZHOU JINGRO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products